Oil-resistant sealing glue and preparation method thereof

A sealant and oil-resistant technology, applied in the field of oil-resistant sealants, can solve the problems of vicious accidents, poor quality of seals, loss and trouble, and achieve the effect of good sealing

Inactive Publication Date: 2015-07-29
LIUZHOU LINGTONG TECH CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the quality of the seal is poor, it will cause loss and trouble if it is light, and it will cause serious accidents if it is serious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0012] The preparation method of oil-resistant sealant of the present invention is:

[0013] The hydrogenated nitrile butadiene rubber and fluororubber in the formulation amount are thinly passed separately, mixed and added to the open mill, and then the remaining components are added to the open mill for mixing until uniform, and then the sheet is produced to obtain the mixed rubber. Carry out one-stage vulcanization, control the vulcanization temperature to 165°C, the vulcanization time to 35 minutes, and the vulcanization pressure to 11MPa; after taking out the rubber, perform two-stage vulcanization in an oven at 165°C for 1 hour to obtain an oil-resistant sealant.

[0014] Example 2

[0015] The formula of oil-resistant sealant of the present invention is as follows:

[0016] Hydrogenated nitrile rubber 50kg, fluorine rubber 22kg, allyl alcohol 3kg, calcium carbonate 2kg, methyl hydrogen silicone oil 1kg, stearic acid 1.8kg, magnesium dimethacrylate 2kg, light calcium ...

Embodiment

[0020] The formula of oil-resistant sealant of the present invention is as follows:

[0021] Hydrogenated nitrile rubber 60kg, fluorine rubber 18kg, allyl alcohol 5kg, calcium carbonate 4kg, methyl hydrogen silicone oil 2kg, stearic acid 1.5kg, magnesium dimethacrylate 3kg, light calcium carbonate 0.5kg, allyl alcohol 0.2 kg, oleic acid diethanolamine borate 3kg, paraffin 1.8kg, diacetyl peroxide 0.8kg, zinc oxide 0.4kg, aluminum oxide 5kg, high wear-resistant carbon black 6kg, antioxidant 0.8kg, sulfur 3kg.

[0022] The preparation method of oil-resistant sealant of the present invention is:

[0023] The hydrogenated nitrile butadiene rubber and fluorine rubber in the formula are thinly passed and mixed into the open mill, and then the remaining components are added into the open mill for mixing until uniform, and then the sheet is obtained to obtain the mixed rubber. Carry out one-stage vulcanization, control the vulcanization temperature to 170°C, the vulcanization time to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an oil-resistant sealing glue. The oil-resistant sealing glue consists of the following components in parts by mass: 50-60 parts of hydrogenated butadiene-acrylonitrile rubber, 18-22 parts of fluororubber, 3-5 parts of allylalcohol, 2-4 parts of calcium carbonate, 1-2 parts of methyl hydrogen silicone oil, 1.5-1.8 parts of stearic acid, 2-3 parts of magnesium methacrylate, 0.2-0.5 part of light calcium carbonate, 0.2-0.5 part of allyl alcohol, 2-3 parts of oleic acid diethanolamine borate ester, 1.5-1.8 parts of paraffin, 0.8-1.2 parts of diacetyl peroxide, 0.2-0.4 part of zinc oxide, 9-12 parts of aluminum oxide, 6-8 parts of high-abrasion-resistance carbon block, 0.8-1.5 parts of an anti-aging agent and 1-3 parts of sulfur. The invention further provides a preparation method of the oil-resistant sealing glue. The oil-resistant sealing glue is high in sealing property, high-temperature resistance, abrasion resistance and oil resistance.

Description

technical field [0001] The invention relates to an oil-resistant sealant. Background technique [0002] Sealing products are important basic components of all kinds of machinery, and almost all industrial sectors cannot do without it. The quality of the sealing element is directly related to the service life and operational reliability of the machine. If the quality of the seals is poor, it will cause loss and trouble if it is light, and it will cause serious accidents if it is serious. Contents of the invention [0003] The invention provides an oil-resistant sealant with good oil resistance; the invention also provides a preparation method thereof. [0004] The invention provides an oil-resistant sealant. The oil-resistant sealant is composed of the following components in parts by mass: 50-60 parts of hydrogenated nitrile rubber, 18-22 parts of fluororubber, 3-5 parts of allyl alcohol, carbonic acid 2-4 parts of calcium, 1-2 parts of methyl hydrogen silicone oil, 1.5...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L15/00C08L27/12C08L83/05C08K13/02C08K3/26C08K5/09C08K5/098C08K3/22C08K3/04
Inventor 张文玲
Owner LIUZHOU LINGTONG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com