Noiseless comfortable rubber heel lift and preparation method thereof

A kind of rubber and comfortable technology, applied in the field of organic polymer compounds, can solve the problems of general wear resistance, muscle strain on the back, easy to produce burrs, etc., to achieve the effect of improving wear resistance, reducing risks and protecting the environment

Active Publication Date: 2015-08-05
MAOTAI FUJIAN SOLES CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For a long time, Tianpi has always been fond of polyurethane materials with high hardness. The Shore hardness of the product is above 95A, even as high as 70D. However, the product is inelastic, which will cause the wearer to strain the back muscles and hurt the feet; the sound is very loud when walking , which brings embarrassment in quiet office places; polyurethane is physically cross-linked, and its wear resistance is average. After wear, it is easy to produce burrs, which affects the appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] In this embodiment, the quiet and comfortable rubber sky is composed of the following components by weight:

[0046] Natural rubber 3L 20 parts

[0047] SBR 1502 16 parts

[0048] Nitrile rubber 4975 18 parts

[0049] High styrene rubber HS860 8 parts

[0050] Glue powder 15 parts

[0051] Silica 27 parts

[0052] Mineral oil 4006 6 parts

[0053] Zinc oxide 3 parts

[0054] Antiager 1010 1.2 parts

[0055] Polyethylene glycol PEG4000 2.4 parts

[0056] Silane coupling agent Si69 2.5 parts

[0057] sulfur 6.5 parts

[0058] Vulcanization accelerator D 1.5 parts

[0059]Vulcanization accelerator DM 1.5 parts

[0060] Vulcanization accelerator NOBS 2 parts

[0061] The preparation method of the aforementioned quiet and comfortable rubber top cover weighs natural rubber, styrene-butadiene rubber, nitrile rubber, high-styrene rubber, rubber powder, white carbon black, mineral oil, zinc oxide, anti-aging agent, polyethylene Glycol, silane coupling agent, sulfur,...

Embodiment 2

[0064] In this example, the preparation method of a quiet and comfortable rubber sky is the same as that in Example 1, except that in the formula raw materials:

[0065] 15 parts of styrene-butadiene rubber 1502, 20 parts of nitrile rubber 4975, 30 parts of white carbon black, 10 parts of mineral oil 4006, 3 parts of silane coupling agent Si69.

[0066] The quiet and comfortable rubber sky skin prepared above has a density of 1.15g / cm 3 , hardness 82, DIN wear resistance 147 mm 3 , Xenon lamp aging test no spit frost phenomenon, ozone aging test no cracking phenomenon, dynamic anti-slip coefficient smooth dry 0.81 wet 0.48.

Embodiment 3

[0068] In this example, the preparation method of a quiet and comfortable rubber sky is the same as that in Example 1, except that in the formula raw materials:

[0069] 20 parts of styrene-butadiene rubber 1502, 15 parts of nitrile rubber DN003, and 6 parts of high-styrene rubber HS860.

[0070] The quiet and comfortable rubber sky skin prepared above has a density of 1.12g / cm 3 , hardness 79, DIN wear resistance 90 mm 3 , The xenon lamp aging test has no frost phenomenon, the ozone aging test has no cracking phenomenon, and the dynamic anti-slip coefficient is 0.76 for the dry type and 0.37 for the wet type.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of organic macromolecular compounds and provides a noiseless comfortable rubber heel lift and a preparation method thereof. The noiseless comfortable rubber heel lift comprises natural rubber, butadiene styrene rubber, butadiene-acrylonitrile rubber, high-styrene rubber, rubber powder, white carbon black, mineral oil, anti-aging agent, polyethylene glycol, silane coupling agent, zinc oxide, sulphur and vulcanization accelerating agent. The noiseless comfortable rubber heel lift has the advantages that the heel lift is elastic and noiseless, pressure and discomfort borne by the foot can be reduced, wearing comfort is improved, the trouble of noise is got rid of, and high wear-resisting and anti-slip performance and long service life are achieved.

Description

technical field [0001] The invention belongs to the technical field of organic polymer compounds, in particular to a quiet and comfortable rubber top and a preparation method thereof. Background technique [0002] The aesthetic concept of modern people is that a slender body is beautiful. After wearing high-heeled shoes, the body forms a posture of raising the head, chest and abdomen, looking tall, straight and graceful, which enhances the feeling of beauty. High-heeled shoes are very popular, enhancing beauty and improving self-confidence, but pains such as back muscle strain, knee arthritis, and ankle sprains also follow one after another. Women who love high-heeled shoes need to endure these ailments for a long time, and they have not been effectively solved. The design of the waterproof platform, heel height, heel slope, outsole, and top skin of high-heeled shoes are all very important. Among them, the material design of the top skin is particularly important. Usually,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/02C08L9/06C08L25/04C08K13/02C08K3/04C08K3/06C08K3/22C08K5/5415C08L71/08C08L21/00
CPCC08L7/00C08L2205/025C08L2205/035C08L9/06C08L9/02C08L91/00C08L21/00C08L71/00C08K13/02C08K3/36C08K2003/2296C08K3/06
Inventor 卢鑫丁思博罗显发廖毅彬郭彩莲周小兰林荷香林江金校红郑荣大
Owner MAOTAI FUJIAN SOLES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap