A pretreatment, spinnability technology, applied in fiber processing, fiber type, textile and papermaking, etc., can solve problems such as difficult to pass, easy to block, difficult to roll in the blowing process, etc.
Active Publication Date: 2015-08-19
ANHUI HUAMAO TEXTILE
View PDF5 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] However, the appearance of SORONA fiber is a spiral spring type, which is relatively fluffy, and the fibers are easy to condense into agglomerates, forming neps, and the spinnability is poor
During the production of the blowing and rolling machine, the concave and convex rollers are easy to block and difficult to pass through, so the blowing process is difficult to roll
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] (a) Take 5kg of liquid wax, mix it with 45kg of water and mix well to prepare 50kg of mixed solution for later use;
[0016] (b) Take SORONA fiber, weigh it as 1000kg, loosely pack it, and spread it evenly;
[0017] (c) Spray 1 kg of the mixed solution obtained in step (a) evenly on the SORONA fiber. In this step, the mass ratio of the mixed solution to the SORONA fiber is 1:1000;
[0018] (d) Cover the SORONA fiber with a plastic film and keep it warm for 24 hours at 25~30°C;
[0019] In steps (b) and (c), the relative humidity of the working environment is kept at 55%, and the temperature is kept at 25~30°C;
[0020] The specific resistance value of the material obtained in step (d) reaches the spinnable range after measurement.
Embodiment 2
[0022] (a) Take 5kg of liquid wax, mix it with 45kg of water and mix well to prepare 50kg of mixed solution for later use;
[0023] (b) Take SORONA fiber, weigh it as 1000kg, loosely pack it, and spread it evenly;
[0024] (c) Spray 1.5kg of the mixed solution obtained in step (a) evenly on the SORONA fiber. In this step, the mass ratio of the mixed solution to the SORONA fiber is 1.5:1000;
[0025] (d) Cover the SORONA fiber with a plastic film and keep it warm for 24 hours at 25~30°C;
[0026] In steps (b) and (c), the relative humidity of the working environment is kept at 55%, and the temperature is kept in the range of 25-30°C;
[0027] The specific resistance value of the material obtained in step (d) reaches the spinnable range after measurement.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a SORONA fiber spinnability preprocessing method, which can improve the spinnability of the SORONA fiber, so that the spinning becomes possible. The technical flow process is simple, and the processing cost is low. The method comprises the following steps that (a) liquid wax and water are mixed and uniformly stirred according to a mass ratio being 1:9; (b) the SORONA fiber is subjected to bale breaking and uniform spreading; (c) the mixing liquid obtained in the step (a) is uniformly sprayed onto the SORONA fiber, and in the step, the mass ratio of the mixing liquid to the SORONA fiber is (0.5 to 1.5):1000; (d) a plastic film is used for covering the SORONA fiber, and the heat insulation is carried out for at least 24 hours under the condition of 25 to 30 DEG C. In the steps (b) and (c), the relative humidity of the work environment is maintained at 55 to 60 percent, and the temperature is maintained at 25 to 30 DEG C.
Description
technical field [0001] The invention relates to textile technology, in particular to a spinnability pretreatment process of SORONA fiber before spinning. Background technique [0002] SORONA polymers are made from two main raw materials, 1,3-propanediol (PDO) and PTA (or DMT). Among them, PDO is its key raw material, accounting for 37% of the total raw materials. PDO can be produced through petrochemical processes, and DuPont of the United States has successfully used the method of SORONA sugar fermentation to efficiently produce the PDO required for the production of SORONA, thus revolutionizing the chemical fiber field and injecting a new concept of environmental protection. [0003] DuPont SORONA can give fibers and fabrics a soft feel, comfortable stretch and recovery, easy dyeing at room temperature and pressure, bright and lasting colors, and chlorine / ultraviolet resistance and stain resistance. It can be widely used in the development of various clothing fabrics: fr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more