Preparation method for PH-nano steel and iron corrosion inhibitor

A technology of nano-steel and anti-corrosion agent, which is applied in the field of steel anti-corrosion and PH-nano-steel anti-corrosion agent preparation. It can solve the problems of short anti-corrosion time, coking, and high temperature resistance, etc., and achieve long anti-corrosion time and good physical and chemical properties. , the effect of stable performance

Active Publication Date: 2015-09-09
长沙艾格防护新材料技术研发有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nowadays, guns and guns are mainly used for anti-corrosion of various oils such as gun oil, butter, etc., as well as various greases. Wash before use and difficult to clean
Smoke is produced when guns and cannons are fired, and there is coking after shooting, which makes it difficult to meet the needs of guns and cannons for storage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] The invention provides a kind of preparation method of PH-nanometer iron and steel corrosion inhibitor, comprises the following steps:

[0028] (1) prepare palm wax and sodium hydroxide respectively; prepare the mixture of absolute ethanol and deionized water; then prepare the first deionized water;

[0029] (2) Heat and melt the prepared palm wax until clear, and pour it into the first three-neck bottle;

[0030] (3) Pour the prepared sodium hydroxide into the first portion of deionized water until it is completely dissolved, then pour it into the first three-necked bottle filled with liquid palm wax, and finally mix the prepared anhydrous ethanol and deionized water All the mixed solution is poured into the first three-necked bottle;

[0031] (4) the first three-necked bottle in the step (3) is placed in an oil bath, and then three ports of the first three-necked bottle are respectively equipped with a thermometer, an agitator and a reflux condenser, and reacted for ...

Embodiment 1

[0051]Prepare 2000 grams of palm wax and 120 grams of sodium hydroxide, prepare 500 ml of a mixture of absolute ethanol and deionized water with a volume ratio of 1:1, and prepare the first 300 ml of deionized water. Heat and melt the prepared 2000 grams of palm wax at 100°C until clear, then pour it into the first three-necked bottle. Pour 120 grams of sodium hydroxide into the first part of deionized water of 300ml until it is completely dissolved, then slowly pour it into the first three-necked bottle filled with liquid palm wax, and then add the prepared absolute ethanol and deionized water All the mixed solution was poured into the first three-necked bottle. Finally, place the first three-necked flask in an oil bath whose temperature is controlled at 105°C, install a thermometer, a stirrer, and a reflux condenser on the three ports of the first three-necked flask, and react for about 6 hours to obtain a dark red liquid . Prepare 120ml of concentrated sulfuric acid and 5...

Embodiment 2

[0054] Prepare 1600 grams of palm wax and 96 grams of sodium hydroxide, prepare 500 ml of a mixture of absolute ethanol and deionized water with a volume ratio of 1:1, and prepare the first 300 ml of deionized water. Heat and melt the prepared 1600 grams of palm wax at a temperature of 100°C until it becomes clear, and then pour it into the first three-necked bottle. Pour 96 grams of sodium hydroxide into the first part of deionized water of 300ml until it is completely dissolved, then slowly pour it into the first three-necked bottle filled with liquid palm wax, then add the prepared absolute ethanol and deionized water All the mixed solution was poured into the first three-necked bottle. Finally, place the first three-necked flask in an oil bath whose temperature is controlled at 106°C, install a thermometer, a stirrer, and a reflux condenser on the three ports of the first three-necked flask, and react for about 6 hours to obtain a dark red liquid . Prepare 96ml of concen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method for a PH-nano steel and iron corrosion inhibitor, which includes the following steps: (1) palm wax and sodium hydroxide are respectively prepared; the mixture of absolute ethyl alcohol and deionized water is prepared; first deionized water is then prepared; (2) the prepared palm wax is heated to melt until the palm wax is clear, and the liquid palm wax is poured into a first three-neck bottle; (3) the prepared sodium hydroxide is poured into the first deionized water until the sodium hydroxide is completely dissolved, and is then poured into the first three-neck bottle loaded with the liquid palm wax, and finally, the prepared mixture of absolute ethyl alcohol and deionized water is completely poured into the first three-neck bottle. The product prepared by the method has stable properties, good physicochemical properties and long anticorrosion time, and can resist high temperature, coating is thin, guns and cannons do not need to be cleaned before being used, and the product does not have adverse effects on the performance of the guns and the cannons after shooting.

Description

technical field [0001] The invention relates to iron and steel anticorrosion technology, in particular to a preparation method of a PH-nanometer iron and steel anticorrosion agent, which belongs to the field of organic macromolecule synthesis. Background technique [0002] Anti-corrosion and anti-corrosion of steel equipment and products are very important to maintain stable performance, safety, and prolong life of equipment; in steel equipment and products, anti-corrosion and anti-corrosion of guns and cannons are particularly important. Nowadays, guns and guns are mainly used for anti-corrosion of various oils such as gun oil, butter, etc., as well as various greases. It needs to be washed before use and it is difficult to clean. Smoke is produced when guns and cannons are fired, and coking occurs after shooting, so it is difficult to meet the needs of guns and cannons for sealing. Contents of the invention [0003] The purpose of the embodiments of the present inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F11/08C23F15/00
Inventor 彭孝权
Owner 长沙艾格防护新材料技术研发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com