A growth device and a growth method technology, applied in the field of crystal growth devices, can solve the problems of unable to grow surface tension crystals, difficult to grow crystals, etc., and achieve the effect of small difference in single crystal quality, good crystallization performance, and high single crystal repetition rate

Active Publication Date: 2017-07-28
威科赛乐微电子股份有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Crystal growth by optical floating zone method is carried out in optical floating zone furnace. For example, the Chinese patent with publication number CN 104389013 A discloses a device for growing crystal by optical floating zone method. However, this device cannot grow crystals with low surface tension, and it is difficult to grow crystals that are easily oxidized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of crystal growth device and growth method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] use as figure 1 In the growth device shown, there are two shadowless halogen lamps, symmetrically distributed, the power of the halogen lamp is 500W, and the voltage is 240V; the infrared light emitted by the shadowless halogen lamp is gathered in the center of the crystal growth chamber through the gold-plated stainless steel focusing screen; the crucible It is a transparent quartz crucible with an inner diameter of 6mm, a length of 80mm, and a wall thickness of 2mm. Lift and rotate on the support rod 5. There is a seed crystal groove at the lower end of the crucible, the diameter of the seed crystal groove is 4mm, and the length is 10mm. The inclination angle of the inner wall of the crucible is 1°.

[0060] The seed crystal in the direction of cleaning (111) is placed in the seed crystal tank, the length of the seed crystal is 10mm, and the diameter is 4mm. After melting the 5N 8g germanium polycrystalline raw material in other quartz crucibles, pour it into the q...

Embodiment 2

[0064] use figure 1 In the growth device shown, there are two shadowless halogen lamps, symmetrically distributed, the power of the halogen lamp is 1000W, and the voltage is 240V; the infrared light emitted by the shadowless halogen lamp is gathered in the center of the crystal growth chamber through the gold-plated stainless steel focusing screen; the crucible It is a transparent quartz crucible with an inner diameter of 5mm, a length of 80mm, and a wall thickness of 2mm. On a support pole that can be lifted and rotated. There is a seed crystal groove at the lower end of the crucible, the diameter of the seed crystal groove is 4mm, and the length is 5mm. The inclination angle of the inner wall of the crucible is 3°.

[0065] Under 4N argon atmosphere, 4g of 5N CaF 2 The powdered raw material was melted in a transparent quartz crucible and cooled in an argon atmosphere. Then take out the polycrystalline material, fill the seed crystal tank with seed crystal, the diameter o...

Embodiment 3

[0068] use as figure 1 In the growth device shown, there are two shadowless halogen lamps, symmetrically distributed, the power of the halogen lamp is 650W, and the voltage is 240V; the infrared light emitted by the shadowless halogen lamp is gathered in the center of the crystal growth chamber through the gold-plated stainless steel focusing screen; the crucible It is a transparent quartz crucible with an inner diameter of 8mm, a length of 80mm, and a wall thickness of 2mm. The surface of the crucible is smooth; the crucible is placed on the crucible holder located on the vertical line in the center of the crystal growth chamber, and the stainless steel crucible holder is firmly fixed to the crucible; the crucible holder is placed On a support pole that can be lifted and rotated. There is a seed crystal groove at the lower end of the crucible, the diameter of the seed crystal groove is 4mm, and the length is 10mm. The inclination angle of the inner wall of the crucible is 2°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
surface tensionaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The present application provides a crystal growth device, comprising: a focusing screen; an infrared light source and a transparent crucible arranged in the focusing screen, the infrared light source being arranged around the crucible; A support rod; the support rod and the crucible are connected through the crucible holder. The growth device provided by the present invention adopts a transparent crucible as a place for crystal growth, and the crystal growth device provided by the present invention can not only grow crystals that can be grown by conventional optical floating zone methods, but also can grow crystals with lower surface tension, Easily oxidized crystals and crystals with volatile components, the experimental results show that the crystals obtained by the growth device provided by the present invention have good crystallization properties, no defects such as bubbles, high single crystal repetition rate, and single crystal quality differences between different batches Small. The crystallization rate is between 90% and 100%. The invention also provides a crystal growth method.

Description

technical field [0001] The invention belongs to the technical field of crystal growth, and in particular relates to a crystal growth device and a growth method. Background technique [0002] The traditional melt method crystal growth techniques include pulling method, descent method, floating zone method, Kyropoulos method, temperature gradient method, heat exchange method, cold crucible method, guided mode method, flame method, etc. [0003] These crystal growth techniques that have been developed so far still have certain limitations. The pulling method and the guided mode method can be used for real-time observation when growing crystals, but it is difficult to grow crystals with inconsistent melting or low thermal conductivity; the descent method, temperature gradient method and heat exchange method can grow crystals with low thermal conductivity, However, it is impossible to observe the crystal growth in real time, and it is also impossible to grow crystals with incons...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B13/22
Inventor 狄聚青朱刘胡丹
Owner 威科赛乐微电子股份有限公司