Polyparaphenylene benzo dioxazole fiber containing fluorine on surface and preparation method thereof

A technology of benzobisoxazole and poly-p-phenylene, which is applied in the field of poly-p-phenylene benzobisoxazole fiber and its preparation, can solve the problem of the decrease of the surface mechanical properties of the fiber itself, affecting the surface mechanical properties of the fiber itself, polymer Macromolecular chain breakage and other problems, to achieve the effect of improving interlayer shear strength, enhancing mechanical properties, and reducing the decline in mechanical strength

Active Publication Date: 2015-09-16
SICHUAN UNIV
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the macromolecular chain of PBO fiber contains a large number of C=N bonds, and fluorine gas is a strong oxidizing agent, both pure fluorination and oxygen fluorination can easily cause the polymer macromolecular chain to break and affect the fiber itself. The mechanical properties of the surface, and the decrease of the mechanical properties of the surface of the fiber itself will cause the interface between it and the composite material prepared by the resin to appear as a weak interface, which is not conducive to the improvement of the performance of the composite material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyparaphenylene benzo dioxazole fiber containing fluorine on surface and preparation method thereof
  • Polyparaphenylene benzo dioxazole fiber containing fluorine on surface and preparation method thereof
  • Polyparaphenylene benzo dioxazole fiber containing fluorine on surface and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] First place the poly-p-phenylene benzobisoxazole fiber body in a closed vacuum reactor, then evacuate, and replace the air in the reactor with nitrogen three times, then fill the vacuum reactor with hydrogen fluoride gas, and treat for 3 Minutes, then fill the vacuum reactor with fluorine / oxygen / nitrogen mixed gas, control the partial pressure of hydrogen fluoride in the reactor to 1KPa, the partial pressure of fluorine to 10KPa, the partial pressure of oxygen to 1KPa, and the partial pressure of nitrogen to 50KPa, and heat up The fluorination treatment was carried out at 25°C for 20 minutes, and finally the poly(p-phenylenebenzobisoxazole) fiber was stored in air atmosphere for at least 1 hour.

[0034] Add the obtained fluorine-containing PBO fiber into the epoxy resin matrix to prepare the corresponding composite material. The relevant properties of the obtained composite material are shown in the attached table.

Embodiment 2

[0036] First place the poly-p-phenylene benzobisoxazole fiber body in a closed vacuum reactor, then evacuate, and replace the air in the reactor with nitrogen three times, then fill the vacuum reactor with hydrogen fluoride gas, and treat for 5 Minutes, then fill the vacuum reactor with fluorine / oxygen / argon mixed gas, control the partial pressure of hydrogen fluoride in the reactor to 4KPa, the partial pressure of fluorine to 60KPa, the partial pressure of oxygen to 6KPa, and the partial pressure of argon to 240KPa, The temperature was raised to 50° C. for fluorination treatment for 5 minutes, and finally the poly(p-phenylenebenzobisoxazole) fiber was stored in air atmosphere for at least 1 hour.

[0037] Add the obtained fluorine-containing PBO fiber into the epoxy resin matrix to prepare the corresponding composite material. The relevant properties of the obtained composite material are shown in the attached table.

Embodiment 3

[0039] First place the poly-p-phenylene benzobisoxazole fiber body in a closed vacuum reactor, then evacuate, and replace the air in the reactor with nitrogen three times, then fill the vacuum reactor with hydrogen fluoride gas for 10 Minutes, then fill the vacuum reactor with fluorine / oxygen / helium mixed gas, control the partial pressure of hydrogen fluoride in the reactor to 0.01KPa, the partial pressure of fluorine to 0.5KPa, the partial pressure of oxygen to 0.05KPa, and the partial pressure of helium to The pressure is 5KPa, and the temperature is raised to 100°C for fluorination treatment for 2 hours, and finally the poly(p-phenylenebenzobisoxazole) fiber is stored in the air atmosphere for at least 1 hour.

[0040] Add the obtained fluorine-containing PBO fiber into the epoxy resin matrix to prepare the corresponding composite material. The relevant properties of the obtained composite material are shown in the attached table.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyparaphenylene benzo dioxazole fiber containing fluorine on surface, which is prepared through the following steps: the body of the polyparaphenylene benzo dioxazole fiber is treated by using a hydrogen fluoride gas, then is mixed by using fluorine / oxygen / inert gas, is subjected to fluoridation for 10 seconds to 2 hours at 5-150 DEG C, and finally is stored in air atmosphere for at least one hour. A contact angle between the surface of the obtained fiber and water is 60-90 degrees, the interlaminar shear strength of a composite material prepared from the fiber and epoxy resin is 30-45MPa, the tensile strength of an impregnated filament is 5.0-5.3GPa, and the tensile modulus is 264-280GPa. The polyparaphenylene benzo dioxazole fiber containing fluorine on surface is high in surface activity, interfacial interaction between the fiber and matrix resin is strong, the interlaminar shear strength of the composite material prepared by using the fiber can be improved by 50-125%, the tensile strength of the impregnated filament is improved by 4-10%, and the modulus is improved by 10-16%. According to the invention, the fluorination rate is high, the treatment time is short, the process is simple and controllable, the cost is relatively low, and the fiber has relatively strong application prospect.

Description

technical field [0001] The invention belongs to the technical field of poly-p-phenylene benzobisoxazole (PBO) fiber and its preparation, and in particular relates to a surface fluorine-containing poly-p-phenylene benzobisoxazole (PBO) fiber and a preparation method thereof. Background technique [0002] Compared with aircraft parts manufactured by traditional metal materials and methods, the integrated design and manufacture of fiber-reinforced resin-based composite materials can not only reduce the weight of aircraft parts by 20-30%, but also reduce the use and maintenance costs by 15-25% compared with metal materials. , so it has been widely used in aerospace field. It is understood that the amount of resin-based composite materials used in aircraft has reached more than 50% of its structural weight. [0003] Although fiber-reinforced resin-based composites have been widely used in the aerospace field due to their light weight, their mechanical properties cannot fully mee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/11D06M11/09C08L63/00D06M101/30
Inventor 刘向阳罗龙波吴鹏黄杰阳李保印刘洋
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka