Production method of flame-retardant fiber board

A technology of refractory fiberboard and production method, which is applied in the field of refractory material manufacturing, can solve the problems of refractory fiberboard, such as large volume, inconsistent surface and internal hardness, and unsuitability for mechanical processing, and achieve excellent thermal and chemical stability, consistent hardness, and bulk density. small effect

Inactive Publication Date: 2015-09-30
LIUZHOU YITING TRADE
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a method for making refractory fiberboard, so as to solve the problem that the refractory fiberboard produced by the existing method has a large volume, inconsistent hardness between the surface and the inside, and is not suitable for machining

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A method for making a refractory fiberboard, comprising the following raw materials in weight: 100kg of aluminum silicate fiber, 9kg of silica-alumina sol, 12kg of tetraethyl orthosilicate, and 8kg of alumina fine powder;

[0016] The operation steps are as follows:

[0017] a. Take aluminum silicate fiber, silica-alumina sol, tetraethyl orthosilicate, alumina fine powder by the weight of above-mentioned each raw material, standby;

[0018] b. Put each raw material into a pulper, add water and stir to make cotton pulp;

[0019] c. adopt vacuum forming machine to make slab with the cotton pulp gained in step b;

[0020] d. Put the slab into the drying room and dry it at 100°C until the moisture content is lower than 8%, then the refractory fiberboard is obtained.

Embodiment 2

[0022] A method for making a refractory fiberboard, comprising the following raw materials in weight: 120kg of aluminum silicate fiber, 12kg of silica-alumina sol, 15kg of tetraethyl orthosilicate, and 10kg of alumina fine powder;

[0023] The operation steps are as follows:

[0024] a. Take aluminum silicate fiber, silica-alumina sol, tetraethyl orthosilicate, alumina fine powder by the weight of above-mentioned each raw material, standby;

[0025] b. Put each raw material into a pulper, add water and stir to make cotton pulp;

[0026] c. adopt vacuum forming machine to make slab with the cotton pulp gained in step b;

[0027] d. Put the slab into the drying room and dry it at a temperature of 140°C until the moisture content is lower than 8% to obtain the refractory fiberboard.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of a flame-retardant fiber board and relates to the technical field of preparation of refractory materials. The flame-retardant fiber board is prepared from the following raw materials in parts by weight: 100-120 parts of aluminium silicate fiber, 9-12 parts of silicon-aluminium sol, 12-15 parts of ethyl orthosilicate and 8-10 parts of additive. The production method of the flame-retardant fiber board comprises the following operation steps: weighing the raw materials according to the parts by weight, putting the raw materials into a thick liquid making machine, adding water and stirring for obtaining cotton pulp, preparing the cotton pulp into a board blank by adopting a vacuum moulding machine, putting the board blank into a drying chamber, and drying at the temperature of 100-140 DEG C until moisture content is lower than 8%, so that the flame-retardant fiber board is obtained. Compared with the prior art, the flame-retardant fiber board obtained by adopting the production method disclosed by the invention has low volume-weight, the hardness of the surface is consistent with that of the interior, the flame-retardant fiber board is applicable to processing of various finished products by virtue of mechanical equipment, and the finished products processed by adopting the flame-retardant fiber board is high in dimension accuracy.

Description

technical field [0001] The invention relates to the technical field of refractory material manufacturing, in particular to a method for manufacturing a refractory fiberboard. Background technique [0002] Refractory fiberboard has certain strength and hardness, strong wind erosion resistance, stable performance at high temperature, high compressive strength at high temperature, and is often used as heat insulation material for high temperature equipment. The refractory fiberboard produced by the existing refractory fiberboard manufacturing method has a large volume, and the hardness of the surface and the inside is not consistent, so it is not suitable for machining, and the products processed by the refractory fiberboard have low dimensional accuracy. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a method for making refractory fiberboard, so as to solve the problem that the refractory fiberboard produced by th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 王嘉龙冯娟张开亿
Owner LIUZHOU YITING TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com