Production method for colored PET industrial filaments

A production method, colored polyester technology, applied in the direction of melt spinning, rayon manufacturing, filament/thread forming, etc., can solve the problems of poor color uniformity of colored yarn and difficulty in meeting the demand, and achieve general color uniformity, Improved performance, vibrant colors

Active Publication Date: 2015-10-07
WUXI SUOLIDE TECH DEV CO LTD
View PDF9 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the common color masterbatch method is used to produce colored polyester yarn, the color uniformity of the colored yarn is not good, and it is difficult to meet the demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The production of 1111dtex / 192f colored high-strength polyester industrial yarn is the target product; the spinning speed is set at 3000 m / min

[0031] The production steps are: ordinary bright PET slice → pulse conveying → SSP solid phase polycondensation → slice conveying after thickening → screw extruder extruding → melt filter filtration → adding spinning oil, color oil, antioxidant and antioxidant Ultraviolet agent→spinning box for spinning→metering pump metering→spinning of spinning components→delayed cooling→side blowing cooling forming→oiling tanker or oil nozzle→pre-drawing roller→multi-stage drafting relaxation heat setting (using multiple For drafting roller)→network device→winding forming. in,

[0032] During spinning:

[0033] The screw temperature setting of the screw extruder (5-zone heating); 294°C, 295°C, 296°C, 297°C, 298°C; the metering pump is 1 in and 4 out; 4x20.0cm 3 / rev, the pump supply rate is 79KG / h; the single-hole extrusion rate of the me...

Embodiment 2

[0057] Example 2 produces 1111dtex / 192f anti-oxidation ultra-high-strength polyester industrial yarn as the target product; the spinning speed is set at 3200 meters per minute)

[0058] The production steps are: ordinary bright PET slice → pulse conveying → SSP solid phase polycondensation → slice conveying after thickening → screw extruder extruding → melt filter filtration → adding spinning oil, color oil, antioxidant and antioxidant Ultraviolet agent→spinning box for spinning→metering pump metering→spinning of spinning components→delay cooling→side blowing cooling forming→oiling tanker or oil nozzle→pre-drawing roller→multi-stage drafting relaxation heat setting (using multiple For drafting roller)→network device→winding forming. in,

[0059] During spinning:

[0060] Screw temperature setting of the screw extruder (5-zone heating); 294°C, 295°C, 296°C, 297°C, 298°C

[0061] Metering pump: the metering pump is 1 in and 4 out; 4x20.0cm 3 / rev The output of the pump is 85...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
elongation at breakaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method for colored PET industrial filaments. A chip spinning one-step method production line is employed; when PET melt flux passes through a melt flux pipeline, color oil and auxiliary agent are added to the PET melt flux via an injection port on the melt flux pipeline; then the color oil and the PET melt flux are evenly mixed via a plurality of novel static mixers in the melt flux pipeline; and the mixed PET melt flux is redistributed into a spinning case or each spinning position. Colored high-strength PET industrial filament possesses even and bright colors, requires short production period and low energy consumption by the use of the production method.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a production method of colored polyester industrial yarn. Background technique [0002] Polyester industrial yarn refers to high-strength, coarse-denier polyester industrial filament, and its fineness is not less than 550dtex. According to its performance, it can be divided into high strength and low elongation type (ordinary standard type), high modulus and low shrinkage type, high strength and low shrinkage type, and active type. Among them, high-modulus low-shrinkage polyester industrial yarn has a tendency to gradually replace ordinary standard polyester industrial yarn in tires and mechanical rubber products due to its excellent properties such as high breaking strength, high elastic modulus, low elongation, and good impact resistance. ; High-strength and low-elongation polyester industrial yarn has the characteristics of high strength, low elongation, high mod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/08D01D5/096D01F1/10
Inventor 周卫中史小良
Owner WUXI SUOLIDE TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com