Matrix resin with self-polishing performance and prepared self-polishing antifouling coating

A matrix resin and anti-fouling coating technology, applied in anti-fouling/underwater coatings, coatings, paints containing biocide, etc., can solve problems such as marine environmental hazards, and achieve marine environment-friendliness, easy hydrolysis, and easy maintenance Effect

Active Publication Date: 2017-12-22
MARINE CHEM RES INST CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its purpose is to reduce the ship's navigation resistance and save fuel consumption. However, in order to achieve a good antifouling effect, traditional antifouling coatings have added a large amount of organic tin, DDT and other substances harmful to the marine environment, causing serious damage to the marine environment. the harm of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Matrix resin with self-polishing performance and prepared self-polishing antifouling coating
  • Matrix resin with self-polishing performance and prepared self-polishing antifouling coating
  • Matrix resin with self-polishing performance and prepared self-polishing antifouling coating

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] a. Preparation of small molecule zinc acrylate monomer (a1)

[0037] Add the stoichiometric solvent and zinc oxide into a four-neck flask equipped with a stirring device, a condenser tube, a dropping funnel, and a thermometer, raise the temperature to 75-85°C, and mix one saturated organic acid and another unsaturated organic carboxyl Mix the acid and a certain amount of deionized water evenly according to the metering ratio, add dropwise into the four-necked bottle, add dropwise for 2 to 3 hours, keep warm until the mixed solution is clear and transparent, cool down and discharge, add solvent, and control small molecule The solid content of the zinc acrylate monomer a1 is 30-55%, and the small molecule zinc acrylate monomer (a1) of the present invention is obtained.

[0038] In the process of preparing the small-molecule zinc acrylate monomer (a1), the molar ratio of zinc oxide to one saturated organic acid and another unsaturated organic carboxylic acid is 1:1:1.

[00...

Embodiment 1

[0051] a. Small molecule zinc acrylate monomer a1-1

[0052] In a four-necked flask equipped with a stirring device, a condenser, a dropping funnel, and a thermometer, add 240 parts of xylene and 81.4 parts of zinc oxide under stirring, and heat to 80°C. A mixture of 86.1 parts of methacrylic acid, 122 parts of benzoic acid and 15 parts of water was added dropwise from the dropping funnel for 3 hours. Keep warm until the mixture is clear and transparent. The temperature was lowered, and 20 parts of solvent xylene was added to adjust the solid content to obtain the small molecule zinc acrylate monomer a1-1. The solid content of a1-1 was measured to be 48.1%.

[0053] b. Self-polishing matrix resin A-1

[0054] In a four-neck flask equipped with a stirring device, a condenser, a dropping funnel, and a thermometer, add 100 parts of xylene and 10 parts of ethyl acrylate under stirring, and heat to 105°C. From the dropping funnel, add 25 parts of methyl methacrylate, 20 parts o...

Embodiment 2

[0056] a. Small molecule zinc acrylate monomer a1-2

[0057] In a four-neck flask equipped with a stirring device, a condenser, a dropping funnel, and a thermometer, add 200 parts of xylene and 81.4 parts of zinc oxide under stirring, and heat to 80°C. A mixture of 72.1 parts of acrylic acid, 122 parts of benzoic acid and 20 parts of water was added dropwise from the dropping funnel for 3 hours. Keep warm until the mixture is clear and transparent. The temperature was lowered, and 40 parts of xylene was added to adjust the solid content to obtain the small molecule zinc acrylate monomer a1-2. The solid content of a1-2 was measured to be 48.1%.

[0058] b. Self-polishing matrix resin A-2

[0059] In a four-neck flask equipped with a stirring device, a condenser, a dropping funnel, and a thermometer, add 100 parts of xylene and 10 parts of ethyl acrylate under stirring, and heat to 105°C. From the dropping funnel, drop 25 parts of methyl methacrylate, 20 parts of ethyl acryl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a matrix resin with self-polishing performance and an environment-friendly self-polishing antifouling coating prepared by using the resin. The matrix resin contains functional groups, so it has good self-polishing performance. The antifouling coating prepared by using the matrix resin Coatings, the matrix resin containing functional groups on the surface of the antifouling coating undergoes a hydrolysis reaction with weakly alkaline seawater to generate a hydrophilic resin, which gradually dissolves into seawater, and at the same time the coated antifouling agent Released to realize the "denudation" of the surface layer, the newly exposed coating continues to undergo hydrolysis reaction with seawater, and finally realizes the self-polishing effect of "layer peeling" of the coating. The antifouling paint prepared with the matrix resin has the characteristics of controllable self-polishing performance, long antifouling period, excellent antifouling performance and the like.

Description

technical field [0001] The invention relates to a matrix resin with self-polishing performance and an environment-friendly self-polishing antifouling coating prepared by using the resin. The matrix resin contains functional groups, so it has good self-polishing performance. The antifouling coating prepared by using the matrix resin Coatings, the matrix resin containing functional groups on the surface of the antifouling coating undergoes a hydrolysis reaction with weakly alkaline seawater to generate a hydrophilic resin, which gradually dissolves into seawater, and at the same time the coated antifouling agent Released to realize the "denudation" of the surface layer, the newly exposed coating continues to undergo hydrolysis reaction with seawater, and finally realizes the self-polishing effect of "layer peeling" of the coating. The antifouling paint prepared with the matrix resin has the characteristics of controllable self-polishing performance, long antifouling period, exce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/06C08F220/14C09D133/12C09D133/10C09D5/16C09D7/12
Inventor 于雪艳陈正涛王科张华庆丛巍巍肖玲桂泰江
Owner MARINE CHEM RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com