Preparation method of spherical nano silica-coated hexagonal boron nitride composite powder

A technology of spherical silica and hexagonal boron nitride, which is applied in lubricating compositions, petroleum industry, additives, etc., can solve problems such as inapplicability, and achieve the effects of convenient operation, tight combination, and simple process

Active Publication Date: 2015-10-14
东营宝丰汽车配件有限公司
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the carbon-coated hexagonal boron nitride obtained in patent CN102502535A is not suitable for ceramic-based and metal-based self-lubricating materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of spherical nano silica-coated hexagonal boron nitride composite powder
  • Preparation method of spherical nano silica-coated hexagonal boron nitride composite powder
  • Preparation method of spherical nano silica-coated hexagonal boron nitride composite powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Weigh 1 g of h-BN micron powder with a particle size of 10 μm and disperse it in 100 mL of absolute ethanol, ultrasonically disperse it for 10 min, add 4.5 mL of distilled water and 4 mL of ammonia water (pH value is about 8.5), and mix the obtained The solution was transferred into a three-necked flask, stirred magnetically and heated in a water bath until the temperature was 45°C;

[0029](2) Keeping the temperature at 45°C, add ethyl orthosilicate dropwise to the above mixed solution. The dropping method is as follows: divide 12mL of ethyl orthosilicate into 3 parts, and slowly add 4mL in 3 times within 1.5h tetraethyl orthosilicate; continue to react for 0.5h after the first dropwise addition, and then start to drop 4mL of tetraethylorthosilicate in the same way for the second time; after finishing the second dropwise addition, continue to react for 0.5h, Then start the third dropwise addition of 4mL tetraethyl orthosilicate in the same way; continue the reactio...

Embodiment 2

[0033] (1) Weigh 4 g of h-BN micron powder with a particle size of 10 μm and disperse it in 400 mL of absolute ethanol, ultrasonically disperse it for 20 minutes, add 18 mL of distilled water and 16 mL of ammonia water (pH value is about 8.5), and the obtained mixture Transfer to a three-necked flask, stir magnetically and heat in a water bath until the temperature is 30°C.

[0034] (2) Keeping the temperature at 30°C, add ethyl orthosilicate dropwise to the above mixed solution. The dropping method is: divide 36mL of ethyl orthosilicate into 3 parts, and add 12mL of orthosilicate dropwise within 1.5h ethyl ester; 0.5h later, add 12ml of tetraethyl orthosilicate dropwise for the second time in the same titration method; after completing the second drop of 0.5h, start the third dropwise addition; and so on, 36mL of tetraethyl orthosilicate total Slowly add dropwise to the mixture in 3 times, the total reaction time is 6h.

[0035] (3) After the reaction, the obtained suspensio...

Embodiment 3

[0037] (1) Weigh 2 g of h-BN micron powder with a particle size of 10 μm and disperse it in 200 mL of absolute ethanol, disperse it ultrasonically for 10 min, add 9 mL of distilled water and 12 mL of ammonia water (pH value is about 9), and dissolve the obtained mixture Transfer to a three-necked flask, magnetically stir and heat in a water bath at a heating temperature of 30°C.

[0038] (2) Keeping the temperature at 30°C, add tetraethyl orthosilicate dropwise to the above mixed solution. The dropping method is as follows: divide 24mL of tetraethyl orthosilicate into 6 parts, and add to the mixture obtained in step (1) every 4 hours. Slowly add 4mL tetraethyl orthosilicate dropwise into the solution, and the total reaction time is 24h. The specific operation is as follows:

[0039] Divide 24mL tetraethyl orthosilicate into 6 parts, each part of 4mL tetraethyl orthosilicate is added dropwise within 3h; continue to react for 1h after the first dropwise addition, and then add d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention relates to a preparation method of a spherical nano silica-coated hexagonal boron nitride composite powder. The method comprises: dispersing micrometer h-BN powder in an absolute ethyl alcohol and adding distilled water and ammonia water, and then adjusting the pH value to 9-12, maintaining the temperature at 30-70 DEG C, dropwise adding tetraethoxysilane, and reacting to obtain a turbid liquid; centrifuging the turbid liquid, washing by absolute ethyl alcohol, drying in vacuum at 30-120 DEG C to obtain an h-BN@SiO2 composite powder material with micron h-BN as nuclear and nano SiO2 as the shell. The silica-coated hexagonal boron nitride composite powder prepared by the method has the advantage that the coating layer is intact and dense and tightly combined with coated particles and has high bonding strength; and the powder can be add to ceramic or metal matrix to improve the mechanical performance of material, without reducing the friction properties of the material.

Description

technical field [0001] The invention relates to a preparation method of a spherical nano-silica-coated sheet-shaped micron hexagonal boron nitride composite powder, which belongs to the technical field of solid lubricant composite materials. Background technique [0002] Hexagonal boron nitride (h-BN) has a layered structure similar to graphite, has good lubricating properties, and is resistant to high temperature and chemical corrosion, and is widely used as a solid lubricant in high temperature environments. Introducing a solid lubricant into a ceramic or metal matrix to obtain a solid self-lubricating material can make the material itself have wear-reducing, wear-resistant and lubricating functions, eliminating the use of lubricating grease. However, it has been found that simply adding h-BN to the ceramic or metal matrix improves the friction properties of the material, but greatly reduces the mechanical properties of the material, which limits its application in some oc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M125/26C10M169/04C10M177/00C04B35/10
Inventor 许崇海陈辉肖光春陈照强衣明东马骏
Owner 东营宝丰汽车配件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More