Method for casting and producing glass mould roughcast by V-process molding process

A molding process and casting production technology, which is applied in the field of glass mold castings and can solve problems such as poor processing accuracy, environmental protection, and complicated processes

Inactive Publication Date: 2015-10-21
HEBEI ANDY MOULD CO LTD
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a method for casting and producing glass mold blanks by V-method molding technology, so as to solve the problems of poor processing accuracy, complicated process and non-environmental protection existing in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] A kind of method of V-method molding process casting production glass mold blank, concrete process steps are as follows:

[0022] 1) Blank material: adopt the heat-resistant alloy cast iron material independently developed by our company as AD-VTFe-20-F to cast glass mold blanks. The chemical composition of the heat-resistant alloy cast iron is: C 3.3% ~ 3.8%, Si 1.9%~2.5%, Mn 0.5%~0.6%, P 0.06%~0.07%, S 0.02%~0.03%, Mo 0.5%~0.9%, V 0.1%~0.2%, Ti 0.2%~0.4%, Cr 0.1 %~0.2%, Mg 0.002%~0.004%, Cu 0.1%~0.2%, Zn 0.003%~0.004%, Al 0.03%~0.04%, Ni 0.4%~0.6%, and the rest is Fe;

[0023] 2) Form plate and mold core: adopt the overall aluminum alloy form plate designed and processed by our company; each V-method vacuum pumping box upper box is equipped with 4 freely replaceable form cores, and each form core has 2 half-piece assembled mold cores. The shape of the mold core can be combined with multiple aluminum alloy modules of different parts and sizes according to the shape an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for casting and producing glass mould roughcast by a V-process molding process. The method comprises the following processes: casting glass mould roughcast by adopting a heat-resistant alloy cast iron material; assembling aluminum alloy mould cores on replaceable mould board cores and finishing the cores; respectively placing replaceable mould board cores in an upper sand box and a lower sand box of a vacuum sand box; carrying out film laminating; carrying out film roasting; carrying out vacuum pouring; carrying out thermal treatment, and the like. According to the method, the mould roughcast, with a D-type graphite form in a roughcast inner cavity part and A-type graphite forms in other roughcast outer parts, is obtained by methods of carrying out process control and boiler-front inoculation treatment, adding alloy elements such as Mo, V, Ti, Cr, Cu and Al, adopting chilled iron cores and the like. The A-type graphite form structure has good static and dynamic strength, higher thermal conductivity and stable processing performances; the D-type graphite form structure has better compactness and higher tensile strength, and is remarkably improved in wear resistance, heat resistance, oxidization resistance and thermal fatigue resistance; and the mould roughcast with different graphite-form structures on key parts is glass mould roughcast which is most suitable for a glass bottle tank forming process.

Description

technical field [0001] The invention relates to the technical field of glass mold casting castings, in particular to a method for producing glass mold blanks by casting with a V-method molding process. Background technique [0002] Glass molds are an important part of the production process of daily-use glass products and one of the key elements in the molding of glass products. Daily-use glass products have good chemical stability and do not chemically react with their contents. At the same time, because they are made of glass raw materials that melt at a high temperature above 1500°C and can be melted and reused repeatedly, they are internationally regarded as the safest and most environmentally friendly. Food and pharmaceutical packaging materials. In recent years, with the continuous improvement of the living standards of Chinese residents, the demand for daily-use glass products is also increasing. While the output of glass products is increasing year by year, due to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22C9/03C22C38/56
Inventor 张胜德张海岭白志杰张君帧张胜杰
Owner HEBEI ANDY MOULD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com