High-strength waterproof magnesium oxysulfate fireproof board and manufacturing method thereof

A technology of magnesium oxysulfide and fireproof board, which is applied in chemical instruments and methods, hydraulic material layered products, lamination, etc. Weight, effect of enhancing compressive strength

Inactive Publication Date: 2015-11-11
郑春科
View PDF4 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a high-strength water-resistant magnesium oxysulfide fireproof board and its preparation method in order to solve the defects of poor water resistance and warping deformation of the fireproof board in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A high-strength water-resistant magnesium oxysulfide fireproof board, including a fiber layer and a slurry, the slurry includes a base material, a middle material, and a fabric. The formulations of the base material, the middle material, and the fabric in this embodiment are consistent, including the following components by weight: Divide: 240 parts of magnesium sulfate solution with a wave magnesium degree of 25 degrees, 300 parts of 85% light-burned magnesium oxide, 90 parts of fly ash, 60 parts of sawdust, 30 parts of light perlite, 1 part of tartrate, polycarboxylate 1 part of water agent, 9 parts of styrene-butadiene emulsion.

[0022] A method for manufacturing a high-strength water-resistant magnesium oxysulfide fireproof board, comprising the following steps:

[0023] A. Prepare the mold;

[0024] B. Take 240 parts of magnesium sulfate solution with a wave magnesium degree of 25 degrees after adding water to adjust, add 1 part of tartaric acid and 1 part of pol...

Embodiment 2

[0030] A high-strength water-resistant magnesium oxysulfide fireproof board, including a fiber layer and a slurry, the slurry includes a base material, a middle material, and a fabric, wherein the base material includes the following components in parts by weight: magnesium sulfate solution with a wave magnesium degree of 25 degrees 80 100 parts of 85% light-burned magnesia, 90 parts of fly ash, 10 parts of kaolin, 30 parts of light perlite, 0.2 parts of tartrate, 0.3 parts of polycarboxylate superplasticizer, and 5 parts of styrene-butadiene emulsion. The middle material includes the following components by weight: 240 parts of magnesium sulfate solution with a magnesia degree of 25 degrees, 300 parts of 85% light-burned magnesium oxide, 100 parts of fly ash, 60 parts of sawdust, 30 parts of light perlite, tartrate 0.6 parts, 1 part of polycarboxylate superplasticizer, 9 parts of styrene-butadiene emulsion. The fabric includes the following components by weight: 120 parts of ...

Embodiment 3

[0040] A high-strength water-resistant magnesium oxysulfide fireproof board, including a fiber layer and a slurry, the slurry includes a base material, a middle material, and a fabric, wherein the base material includes the following components in parts by weight: magnesium sulfate solution with a wave magnesium degree of 25 degrees 80 100 parts of 85% lightly burned magnesia, 90 parts of Shuangfei powder, 10 parts of kaolin, 30 parts of light perlite, 0.2 part of tartrate, 0.3 part of polycarboxylate superplasticizer, and 5 parts of styrene-butadiene emulsion. The middle material includes the following components by weight: 240 parts of magnesium sulfate solution with a magnesia degree of 25 degrees, 300 parts of 85% light-burned magnesium oxide, 100 parts of double fly powder, 60 parts of sawdust, 30 parts of light perlite, 0.6 parts of tartrate 1 part, 1 part of polycarboxylate superplasticizer, 9 parts of styrene-butadiene emulsion. The fabric includes the following compon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
heat releaseaaaaaaaaaa
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength waterproof magnesium oxysulfate fireproof board. The high-strength waterproof magnesium oxysulfate fireproof board comprises a fiber layer and slurry, wherein the slurry comprises a bottom material, an intermediate material and a surface material; the bottom material, the intermediate material and the surface material respectively comprise the following components in parts by weight: 80-240 parts of magnesium sulfate solution having the baume degree being 23-28 degrees, 100-300 parts of 85% light calcined magnesia, 0.1-5 parts of tartrate, 2-10 parts of butylbenzene emulsion, 0-100 parts of heavy-weight filler, 0-100 parts of lightweight filler and 0.1-5 parts of water reducing agent. The high-strength waterproof magnesium oxysulfate fireproof board has the advantages of low thermal expansion and shrinkage rate, low heat conduction coefficient, high strength, excellent waterproof property, no warping and deformation, over 0.95 softening coefficient, no halogenation, no scumming, excellent freezing resistance and noninflammability and the like.

Description

technical field [0001] The invention relates to a fireproof board, in particular to a high-strength water-resistant magnesium oxysulfide fireproof board and a preparation method thereof. Background technique [0002] Magnesium cement is a special kind of cement, which was invented by the Frenchman Sorrell in 1867, so it is also called Sorrell cement. And because most of it is formed by the condensation of magnesium chloride and magnesium oxide, it is also called magnesium oxychloride cement. At the same time, it uses magnesium oxide as the main component, and people are used to calling them magnesium cement. For more than 100 years, although scientists have conducted continuous research and development on magnesium cement and made great progress, its fatal shortcomings have seriously hindered people's development and use of it. The inherent disadvantages of magnesium oxychloride cement are: (1) poor water resistance: no matter it is the dissolution theory or the hydrolysis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/30C04B24/26C04B14/18C04B18/26C04B18/08C04B14/10C04B14/28B32B13/14B32B37/15C04B111/28
CPCY02W30/91
Inventor 郑春科
Owner 郑春科
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap