High-solid low-VOC (volatile organic compound) benzene-free solvent-type acrylic resin

An acrylic resin and solvent-based technology, applied in the field of 3C coatings, can solve the problems of unsatisfactory viscosity, solid content and acid value, etc., and achieve the effect of improving market competitiveness, enhancing advantages and broadening market prospects

Inactive Publication Date: 2015-11-11
NANXIONG RISING CHEM IND
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing PUA topcoats generally use toxic and harmful reagents such as xylene and toluene as solvents, and the viscosity, solid content and acid value are not satisfactory, and there are certain limitations.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A high-solid, low-VOC benzene-free solvent-based acrylic resin, consisting of three parts A, B, and C; the part A is composed of butyl acetate and propylene glycol methyl ether acetate; the part B is composed of methyl methacrylate , styrene, hydroxypropyl acrylate, butyl methacrylate, butyl acrylate, acrylic acid and tert-butyl peroxybenzoate; the C part consists of tert-butyl peroxybenzoate and butyl acetate.

[0030] The amount of each component added is: 324 parts of butyl acetate, 64.8 parts of propylene glycol methyl ether acetate, 180 parts of methyl methacrylate, 180 parts of styrene, 100.8 parts of hydroxypropyl acrylate, 129.6 parts of butyl methacrylate, 50.4 parts of butyl acrylate, 7.2 parts of acrylic acid, 12 parts of tert-butyl peroxybenzoate, 2 parts of tert-butyl peroxybenzoate, 45 parts of butyl acetate.

[0031] A method for preparing the above-mentioned high-solid, low-VOC benzene-free solvent-based acrylic resin, consisting of the following steps: ...

Embodiment 2

[0038] A high-solid, low-VOC benzene-free solvent-based acrylic resin, consisting of three parts A, B, and C; the part A is composed of butyl acetate and propylene glycol methyl ether acetate; the part B is composed of methyl methacrylate , styrene, hydroxypropyl acrylate, butyl methacrylate, butyl acrylate, acrylic acid and tert-butyl peroxybenzoate; the C part consists of tert-butyl peroxybenzoate and butyl acetate.

[0039] The amount of each component added is: 324 parts of butyl acetate, 64.8 parts of propylene glycol methyl ether acetate, 160 parts of methyl methacrylate, 200 parts of styrene, 100.8 parts of hydroxypropyl acrylate, 100 parts of butyl methacrylate, 80 parts of butyl acrylate, 7.2 parts of acrylic acid, 12 parts of tert-butyl peroxybenzoate, 2 parts of tert-butyl peroxybenzoate, 45 parts of butyl acetate.

[0040] A method for preparing the above-mentioned high-solid, low-VOC benzene-free solvent-based acrylic resin, consisting of the following steps:

[00...

Embodiment 3

[0047] A high-solid, low-VOC benzene-free solvent-based acrylic resin, consisting of three parts A, B, and C; the part A is composed of butyl acetate and propylene glycol methyl ether acetate; the part B is composed of methyl methacrylate , styrene, hydroxypropyl acrylate, butyl methacrylate, butyl acrylate, acrylic acid and tert-butyl peroxybenzoate; the C part consists of tert-butyl peroxybenzoate and butyl acetate.

[0048] The amount of each component added is: 324 parts of butyl acetate, 64.8 parts of propylene glycol methyl ether acetate, 220 parts of methyl methacrylate, 140 parts of styrene, 100.8 parts of hydroxypropyl acrylate, 120 parts of butyl methacrylate, 60 parts of butyl acrylate, 7.2 parts of acrylic acid, 12 parts of tert-butyl peroxybenzoate, 2 parts of tert-butyl peroxybenzoate, 45 parts of butyl acetate.

[0049] A method for preparing the above-mentioned high-solid, low-VOC benzene-free solvent-based acrylic resin, consisting of the following steps:

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Acid valueaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a 3C paint, particularly a high-solid low-VOC (volatile organic compound) benzene-free solvent-type acrylic resin. The high-solid low-VOC (volatile organic compound) benzene-free solvent-type acrylic resin is a benzene-free system and is composed of a component A, a component B and a component C. The component A is composed of butyl acetate and propylene glycol methyl ether acetate. The component B is composed of methyl methacrylate, styrene, 2-hydroxypropyl acrylate, butyl methacrylate, butyl acrylate, acrylic acid and tert-butyl peroxybenzoate. The component C is composed of tert-butyl peroxybenzoate and butyl acetate. When being used as a finish paint matched with the primer for 3C electronic products, the resin has the advantages of favorable matching property, higher hardness, higher wear resistance, excellent alcohol resistance, excellent chemical resistance, excellent artificial sweat resistance, excellent cold / heat shock resistance, excellent high-temperature / high-dampness resistance, excellent artificial aging resistance and the like. The resin has high solid content, low viscosity and lower VOC, is more environment-friendly when being used as a benzene-free system, and has higher market competitiveness.

Description

technical field [0001] The invention relates to a 3C paint, in particular to a high-solid, low-VOC benzene-free solvent-based acrylic resin. Background technique [0002] 3C coating is the general term for coatings used in 3C products, and the so-called "3C products" are the combination of computers (Computer), communications (Communication) and consumer electronics (Consumer Electronics), also known as "information appliances". In 2014, the fourth year of the "Twelfth Five-Year Plan", China's transformation from "world factory" to "world market" has begun to emerge, and China's 3C industry will also face a new opportunity for comprehensive development. During the "Twelfth Five-Year Plan" period, the scale of my country's communication investment will reach 2 trillion yuan, and the 3C industry is facing a rare opportunity for development. At present, the large market of the 3C industry has indeed become one of the driving forces for the development of the national economy, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D125/14C09D7/00C08F220/14C08F212/08C08F220/28C08F220/18C08F220/06
Inventor 陈永怀
Owner NANXIONG RISING CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap