Aviation magnalium cutting fluid and preparation method thereof

A magnesium-aluminum alloy and a preparation method technology, applied in the direction of lubricating compositions, etc., can solve the problems of restricting the development of national industries, easy odor of cutting fluid, easy corrosion of workpieces, etc., and achieve enhanced polar lubrication effect and strong corrosion inhibition effect. , the effect of low cost

Active Publication Date: 2015-11-11
苏州山河星程材料科技有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cutting fluid on the 7075 aviation magnesium aluminum alloy currently on the market has several problems: easy to break force, scratches on the workpiece, easy odor of the cutting fluid, and easy corrosion of the workpiece, etc.
This type of products mainly foreign cutting fluid manufacturers control the domestic market, such as Castrol, Blaser and other foreign brands, their product prices are high, the cost of use is high, which seriously restricts the development of national industries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] This example provides an aviation magnesium-aluminum alloy cutting fluid. Its raw materials include the following components by weight percentage: 35% mineral oil, 15% self-emulsifying ester (Priolube3955), 8% phosphate ester (Rhodia LB-400) , 5% monoethanolamine, 2% corrosion inhibitor (Lubrizol CP-NF-2), 8% sorbitan monooleate, 2% glycerol, 8% borate (Guangzhou Dexu Chemical DX6215 ), 3% isothiazolinone, 0.5% defoamer (Nanjing Sixin Technology X-35C) and the balance is water;

[0021] Its formulation includes the following steps: (a) adding the prescribed amount of water into the reactor, and starting the agitator; (b) sequentially adding the formulated amount of mineral oil, self-emulsifying ester, phosphoric acid ester, monoethanolamine, Corrosion inhibitor and sorbitan monooleate, stir for 1 hour; then add the formula amount of glycerin, borate, isothiazolinone and defoamer in sequence, continue to stir for 1 hour, add a raw material Stir to dissolve and then add ...

Embodiment 2

[0023] This example provides an aviation magnesium-aluminum alloy cutting fluid, the basic composition of which is basically the same as that in Example 1, the difference is that its content is inconsistent, specifically: 60% mineral oil, 10% self-emulsifying ester, 5% phosphate , 2% monoethanolamine, 1% corrosion inhibitor, 5% sorbitan monooleate, 0.5% glycerol, 5% borate (Guangzhou Dexu Chemical DX6215), 1% isothiazolinone, 0.1 % defoamer and balance water.

Embodiment 3

[0025] This example provides an aviation magnesium-aluminum alloy cutting fluid, the basic composition of which is basically the same as that in Example 1, the difference is that its content is inconsistent, specifically: 30% mineral oil, 20% self-emulsifying ester, 10% phosphoric acid ester , 5% monoethanolamine, 2% corrosion inhibitor, 10% sorbitan monooleate, 2% glycerol, 10% borate (Guangzhou Dexu Chemical DX6215), 5% isothiazolinone, 0.5 % defoamer and balance water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to aviation magnalium cutting fluid and a preparation method thereof. The aviation magnalium cutting fluid comprises, by weight, 30-60% of mineral oil, 10-20% of self-emulsifying ester, 5-10% of phosphate, 2-5% of monoethanolamine, 1-2% of a corrosion inhibitor, 5-10% of sorbitan monooleate, 0.5-2% of glycerol, 5-10% of borate, 1-5% of isothiazolinone, 0.1-0.5% of a defoamer and the balance water. By precisely controlling the components and ingredients of the preparation, on the one hand, the service life of the cutting fluid and the service life of a cutter can be prolonged, the polarity lubricating effect of the cutting fluid is enhanced, machined magnalium is better in degree of finish, the product reject ratio is reduced to be 0.03% that in the prior art, the cost is reduced, and the production efficiency is improved; on the other hand, the self-emulsifying ester and the phosphate have the synergistic interaction effect in the extreme pressure lubricating aspect after being compounded, the extreme pressure lubricating performance of the product is remarkably improved, particularly, the phosphate can produce wonderful effects after being compounded with the corrosion inhibitor, the corrosion inhibitor additive amount is reduced, the cost of the cutting fluid is lower, and the product corrosion inhibition effect is better.

Description

technical field [0001] The invention relates to a cutting fluid, in particular to an aviation magnesium-aluminum alloy cutting fluid and a preparation method thereof. Background technique [0002] The main metal materials used in aircraft are aluminum alloy, alloy steel, titanium alloy, copper alloy and high-temperature alloy. Among them, aluminum alloy accounts for the largest proportion, accounting for about 75%. The main grades of aluminum alloy used are: 2024, 2124 , 6061, 7050, 7075, 7475, etc. Among them, the 7-series aluminum is aviation magnesium-aluminum alloy. Due to its excellent comprehensive properties such as good toughness, high fatigue strength, and good stress corrosion resistance, the proportion of use in aircraft manufacturing is increasing; among the 7-series magnesium-aluminum alloys, it is the most widely used. The most popular is 7075, which is an aluminum-zinc-magnesium-copper series heat-treatable and strengthened deformable aluminum alloy, mainly i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/00C10M177/00
Inventor 王鹏举李富民刘大志
Owner 苏州山河星程材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com