Fibrilia-reinforced polypropylene engineering composite as well as preparation method and application of fibrilia-reinforced polypropylene engineering composite

A composite material and hemp fiber technology, applied in the preparation of automobile parts, hemp fiber reinforced polypropylene engineering composite material and its preparation field, can solve the problem that the mechanical properties of the material need to be further improved, and achieve light weight and molding processing. The effect of excellent performance and excellent mechanical properties

Active Publication Date: 2015-11-25
ZHEJIANG XINLI NEW MATERIAL CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mechanical properties of t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fibrilia-reinforced polypropylene engineering composite as well as preparation method and application of fibrilia-reinforced polypropylene engineering composite
  • Fibrilia-reinforced polypropylene engineering composite as well as preparation method and application of fibrilia-reinforced polypropylene engineering composite
  • Fibrilia-reinforced polypropylene engineering composite as well as preparation method and application of fibrilia-reinforced polypropylene engineering composite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The formula is as follows:

[0039]

[0040] Weigh the following ingredients by weight:

[0041] Polypropylene copolymer (sales from Dongguan Xuanhao Plastic Co., Ltd., Yongjia, Taiwan, PP3015) 73Kg, kenaf fiber (5mm-10mm in diameter, Gaobeidian City Liangjiaying Shengli Hemp Rope Processing Factory) 20Kg, epoxy furan (HF9200, Wuxi Guangming Chemical Co., Ltd.) 2Kg, POE (Mitsui Chemicals DF740, Dongguan City Yu Yu Plastic Raw Materials Co., Ltd.) 5Kg, lauryl peroxide (Shanghai Puzhen Biotechnology Co., Ltd., CAS registration number 105-74-8) 0.5Kg.

[0042] The preparation process is as follows:

[0043] First, at an ambient temperature of 25°C, use a high-speed mixer to mix the above-mentioned weighed raw materials uniformly to obtain a uniformly mixed material; then, add the mixed material to a twin-screw extruder for melt blending (mixed The materials are sequentially passed through the melting and blending intervals with temperatures of 170°C, 172°C, 172°C, 1...

Embodiment 2

[0045] The formula is as follows:

[0046]

[0047] Weigh the following ingredients by weight:

[0048] Polypropylene copolymer (sales from Dongguan Xuanhao Plastic Co., Ltd., Yongjia, Taiwan, PP3015) 66.2Kg, kenaf fiber (5mm-10mm in diameter, Gaobeidian Liangjiaying Shengli Hemp Rope Processing Factory) 25Kg, epoxy furan (HF9200, Wuxi Guangming Chemical Co., Ltd.) 3Kg, POE (Mitsui Chemicals DF740, Dongguan City Yu Yu Plastic Raw Materials Co., Ltd.) 5Kg, lauryl peroxide (Shanghai Puzhen Biotechnology Co., Ltd.) 0.8Kg.

[0049] The preparation process is as described in Example 1.

Embodiment 3

[0051] The formula is as follows:

[0052]

[0053] Weigh the following ingredients by weight:

[0054] Polypropylene copolymer (sales from Dongguan Xuanhao Plastic Co., Ltd., Yongjia, Taiwan, PP3015) 60Kg, kenaf fiber (5mm-10mm in diameter, Gaobeidian City Liangjiaying Shengli Hemp Rope Processing Factory) 30Kg, epoxy furan (HF9200, Wuxi Guangming Chemical Co., Ltd.) 5Kg, POE (Mitsui Chemicals DF740, Dongguan City Yu Yu Plastic Raw Material Co., Ltd.) 5Kg, lauryl peroxide (Shanghai Puzhen Biotechnology Co., Ltd.) 1Kg.

[0055] The preparation process is as described in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a fibrilia-reinforced polypropylene engineering composite, a preparation method thereof and application of the fibrilia-reinforced polypropylene engineering composite to preparation of automobile parts. The composite is prepared from the following raw materials in percentage by weight: 59-80% of polypropylene, 19-30% of fibrilia, 1-5% of epoxy furan, 1-10% of a toughening agent and 0.1-3% of lauroyl peroxide, wherein both the fibrilia and epoxy furan are from renewable biomasses and meet the requirements of low carbon, environment friendliness and sustainable economic development. According to the fibrilia-reinforced polypropylene engineering composite, epoxy furan can reactively improve the interfacial compatibility of polypropylene and fibrilia under the initiating action of lauroyl peroxide, so that the composite is kept to have excellent mechanical property and processability and can be used for preparing the automobile parts. The preparation method of the composite, disclosed by the invention, can be used for preparing the composite through one-step extrusion and is simple, easy to operate and suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of polypropylene composite materials, in particular to a hemp fiber-reinforced polypropylene engineering composite material, a preparation method thereof, and an application in preparing automobile parts. Background technique [0002] With the "energy shortage" and "air pollution" becoming more and more serious, especially in recent years, the automobile market has developed rapidly, and the energy saving and emission reduction of automobiles has become urgent. In order to promote the progress of automobile products, protect the environment, promote energy conservation and sustainable development, the miniaturization and light weight of automobiles has attracted people's attention. [0003] Developed countries in the automobile industry have taken the amount of plastics and their composite materials as an important indicator to measure the level of modern automobile design and manufacturing technology. As o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/14C08L97/02C08L23/08C08K5/1535C08K5/14B29C47/92B29C48/92
CPCB29C48/92B29C2948/92209C08L23/14C08L2205/02C08L2205/03C08L2205/08C08L2205/16C08L97/02C08L23/0815C08K5/1535C08K5/14
Inventor 叶耀挺陈良光
Owner ZHEJIANG XINLI NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap