Brittle solid spice bead for cigarette filter stick and preparation method thereof

A technology of solid spices and cigarette filter rods, applied in the fields of e-liquid filter elements, applications, tobacco, etc., can solve the problem of extremely high surface tension and achieve a wide range of applications

Active Publication Date: 2015-12-02
HUBEI CHINA TOBACCO IND +1
View PDF11 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when preparing liquid fragrance beads, the surface tension of the liquid fragrance is extremely high, and must match the surface tension of the glue, otherwise it cannot be dripped into pills, which has great limitations. Therefore, it is necessary to seek a new fragrance Bead preparation method, expanding the range of applicable flavors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Heat and melt 75% PEG polymer (molecular weight: 2000) in a water bath at 70°C according to mass percentage, then add 10% mint essence and 15% glycerin, mix well and let stand for 2 hours.

[0029] (2) The above-mentioned mixed solution was dripped into liquid paraffin by an automatic dropping pill machine, condensed and solidified to obtain the spherical soft core, the diameter of the soft core was 2 mm, and the crushing strength was 500 Pa.

[0030] (3) Mix 5% sodium alginate, 5% propylene glycol and 90% water according to the mass percentage, stir evenly, let stand for 2 hours, and set aside.

[0031] (4) first adopt the coating pan to wrap the ethyl cellulose alcohol solution on the surface of the soft core to isolate moisture, and then wrap the solution in the step (3) on the surface of the spherical soft core to form a brittle shell to prepare solid spice beads. The thickness of the brittle shell of the solid spice beads is 1 mm, and the crushing strength is 1...

Embodiment 2

[0033] (1) 55% PEG polymer (molecular weight 2000) and 30% PEG polymer (molecular weight 6000) are heated and melted in a water bath at 70°C, and then 5% green tea essence and 10% glycerin are added thereto, mixed Let stand for 2h after uniformity.

[0034] (2) The above-mentioned mixed solution was dripped into liquid paraffin by an automatic dropping pill machine, condensed and solidified to obtain the spherical soft core. The diameter of the soft core was 2.5mm, and the crushing strength was 650pa.

[0035] (3) Mix 3% gelatin, 9% glycerin and 88% water in a certain proportion, stir evenly, let stand for 2 hours, and set aside.

[0036] (4) first adopt the coating pan to wrap the ethyl cellulose alcohol solution on the surface of the soft core to isolate moisture, and then wrap the solution in the step (3) on the surface of the spherical soft core to form a brittle shell to prepare solid spice beads. Finally, a layer of ethyl cellulose film is wrapped on the outer surface o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a brittle solid spice bead for a cigarette filter stick. The brittle solid spice bead comprises a spherical soft kernel and a brittle shell, wherein the brittle shell covers the surface of the spherical soft kernel in a lagging cover manner, and raw materials of the spherical soft kernel is prepared from the following ingredients in percentage by mass: 65 to 90 percent of PEG (polyethylene glycol) polymer or a PEG polymer mixture with a molecular weight of 2000 to 6000, 5 to 25 percent of glycerinum and 0.5 to 15 percent of essence, and raw materials of the brittle shell is prepared from the following ingredients in percentage in mass: 3 to 50 percent of natural high polymer material, 1 to 10 percent of plasticizer, and 60 to 90 percent of water. The invention also provides a preparation method of the brittle solid spice bead for the cigarette filter stick. The brittle solid spice bead is not subjected to the limitation of the essence type and characteristics and high in applicability.

Description

technical field [0001] The invention relates to the technical field of cigarettes, in particular to crisp solid flavor beads used for cigarette filter rods and a preparation method thereof. Background technique [0002] At present, most cigarette manufacturers achieve the purpose of increasing the flavor of cigarettes by adding liquid flavor beads to cigarette filter rods. Chinese patent (authorized announcement number: CN102108136B, authorized announcement date: October 24, 2012) uses sodium alginate solution as the glue of the spice bead shell, wraps the liquid essence in the glue to form a capsule by dripping method, and squeezes it hard When the spice beads are pressed, not only can the aroma components be released, but also accompanied by a crisp sound. However, when preparing liquid fragrance beads, the surface tension of the liquid fragrance is extremely high, and must match the surface tension of the glue, otherwise it cannot be dripped into pills, which has great l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A24D3/02A24D3/04
Inventor 刘冰陈义坤郭国宁岳海波刘祥浩
Owner HUBEI CHINA TOBACCO IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap