Colored hand cart tire rubber material filled with semi-wet modified attapulgite and preparation method of colored hand cart tire rubber material

A technology for modifying attapulgite and attapulgite, applied in special tires, vehicle parts, tire parts and other directions, can solve the problems of easy aggregation, large specific surface area and high surface activity, and achieve high mechanical strength and high vulcanization efficiency. , The effect of good processing fluidity

Active Publication Date: 2015-12-02
江苏欧廷高分子材料有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because AT has a large specific surface area and a large amount of silanol on the surface, it has high surface activity and is easy to aggregate; when it is used as a reinforcing agent for rubber materials, it is difficult to exist in the rubber matrix in the form of nano single crystals

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colored hand cart tire rubber material filled with semi-wet modified attapulgite and preparation method of colored hand cart tire rubber material
  • Colored hand cart tire rubber material filled with semi-wet modified attapulgite and preparation method of colored hand cart tire rubber material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] First adjust the roller distance of the double-roller mill to 0.1mm, add 70g of natural rubber thin pass plasticizing 8 times; adjust the roller distance to 0.5mm, add 30g of styrene-butadiene rubber thin pass until the mixing is uniform; adjust the roller distance to 2.0mm, When the rubber material is covered with rolls and there is a small amount of accumulated glue, add 6.0g plasticizer solid coumarone, 0.4g phthalocyanine green, 2.0g antioxidant SP-C, 1.5g antioxidant MB, 8.0g zinc oxide, 4.0g Stearic acid until mixed evenly; then add 60g of semi-wet modified attapulgite, 1.2g of accelerator NOBS, and 0.5g of accelerator DM in sequence; when the material is completely eaten, adjust the roller distance to 0.5mm, and pack it 4 times; Then adjust the roller distance to 2.5mm, add 0.2g accelerator TMTD and 1.4g insoluble sulfur in turn, adjust the roller distance to 0.2mm when the material is completely eaten, and pack it 6 times; control the mixing temperature at about ...

Embodiment 2

[0034] First adjust the roller distance of the double-roller mill to 0.1mm, add 70g of natural rubber thin pass plasticizing 9 times; adjust the roller distance to 0.5mm, add 30g of styrene-butadiene rubber thin pass until the mixing is uniform; adjust the roller distance to 2.0mm, When the rubber material is covered with rolls and there is a small amount of accumulated glue, add 5.0g plasticizer solid coumarone, 0.4g benzidine yellow, 2.0g antioxidant SP-C, 1.5g antioxidant MB, 7.0g zinc oxide, 3.5 Add 20g of precipitated white carbon black, 0.6g of solid polyethylene glycol, 40g of semi-wet modified attapulgite, 1.2g of accelerator NOBS, and 0.5g of accelerator DM in turn; When the material is complete, adjust the roller distance to 0.5mm, and pack the thin pass three times; then adjust the roller distance to 2.5mm, add 0.2g accelerator TMTD, 1.4g insoluble sulfur in turn, and adjust the roller distance to 0.2mm when the material is complete, thin Pack the mixture 7 times; c...

Embodiment 3

[0036] First adjust the roller distance of the double-roller mill to 0.1mm, add 70g of natural rubber thin pass plasticizing 10 times; adjust the roller distance to 0.5mm, add 30g of styrene-butadiene rubber thin pass until the mixing is uniform; adjust the roller distance to 2.0mm, When the rubber material is covered with rolls and there is a small amount of accumulated glue, add 4.0g plasticizer solid coumarone, 0.5g phthalocyanine blue, 2.0g antioxidant SP-C, 1.5g antioxidant MB, 5.0g zinc oxide, 2.0 G stearic acid until mixed evenly; then add 20g precipitated white carbon black, 0.6g solid polyethylene glycol, 20g semi-wet modified attapulgite, 1.2g accelerator NOBS; adjust the roller distance when the material is completely eaten to 0.5mm, pack 2 times with Botong; then adjust the roller distance to 2.2mm, add 0.2g accelerator TMTD and 1.4g insoluble sulfur in turn, adjust the roller distance to 0.2mm when the material is completely eaten, and pack 8 times with Botong; Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
Login to view more

Abstract

The invention provides a colored hand cart tire rubber material filled with semi-wet modified attapulgite. The colored hand cart tire rubber material comprises the following components in parts by mass: 70 parts of natural rubber, 30 parts of butadiene styrene rubber, 20-60 parts of semi-wet modified attapulgite, 0-25 parts of precipitated silica, 1.4-1.6 parts of a vulcanizing agent, 1.4-1.9 parts of an accelerant system, 5-8 parts of zinc oxide, 2-4 parts of stearic acid, 0-0.75 part of a white carbon black modifier, 3.5 parts of an anti-aging agent system, 4-6 parts of solid coumarone and 0.4-0.6 part of a colorant. The traditional rubber processing material and process are adopted, and the industrial-grade semi-wet modified attapulgite is applied to a colored hand cart tire, which is a development of a novel application field of attapulgite and is beneficial to the popularization and application of the semi-wet modified attapulgite to hand cart tire enterprises.

Description

Technical field [0001] The present invention is a rubber product technology field, which involves color force car tires and preparation methods that fill the semi -wet -wetting method. Background technique [0002] my country has more than 300 companies and more than 100,000 employees. With the continuous improvement of its technology, production equipment and product quality, it not only plays an important position in my country's rubber industry, but also ranks among the top in the world.The tires mainly include the internal and external tires of motorcycles, internal and external tires of bicycles, internal and external tires, and multi -purpose tires.According to statistics from the Chinese rubber industry's economic operation in 2014, the annual output of motorcycle tires in my country in 2014 was 170 million, the annual output of bicycle tires was 350 million, and the annual output of electric bicycle tires was 245 million. The amount continues to grow.It can be seen that t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/06C08L45/02C08K13/06C08K9/06C08K9/04C08K3/34C08K3/36C08K5/09C08K3/22C08K3/06B60C1/00B29C35/02B29B7/00
Inventor 张小萍刘琼琼侯亚合娄朗朗候玉奎
Owner 江苏欧廷高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap