Anti-wrinkle anti-fouling microfiber leather and its manufacturing method

A microfiber leather and a manufacturing method technology, applied in the field of clothing materials, can solve the problems of easy sweating, easy to wrinkle, affecting the quality of clothing materials, etc., and achieve excellent elongation recovery, high elastic recovery rate, and excellent thermal performance. Effect

Active Publication Date: 2017-05-31
TIANSHOU FUJIAN SUPERFIBER TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing clothing materials have poor air permeability and uncomfortable wearing. When people are exercising, they tend to sweat a lot. If the sweat cannot be discharged in time, it will make people feel stuffy and uncomfortable, which will affect the comfort of wearing.
When dyeing thicker clothing materials, they are all dyed as a whole. Dyeing is an industry with high pollution and high energy consumption, which consumes water, wastes resources, and increases production costs; clothing materials are easy to fade after dyeing; clothing materials do not have waterproof, oil-proof, and wrinkle-resistant properties. It is easy to wrinkle and reduce the service life of the fabric, especially for the fabric used in curtains and sofa releases
In addition, some clothing materials will be coated with a layer of polyurethane coating, which is prone to blisters during coating, which will affect the quality of clothing materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-wrinkle anti-fouling microfiber leather and its manufacturing method
  • Anti-wrinkle anti-fouling microfiber leather and its manufacturing method
  • Anti-wrinkle anti-fouling microfiber leather and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Wrinkle-resistant and stain-resistant microfiber leather, such as Figure 1 to Figure 3 As shown, it includes a dyed layer 1, a composite membrane 2 coated on the upper surface of the dyed layer 1, a base layer 3 arranged on the lower surface of the dyed layer 1, and an anti-wrinkle mesh layer 4 arranged on the lower surface of the base layer 3. The composite membrane 2 is made of polyester Made of tetrafluoroethylene (PTFE) film coated with a layer of polyurethane (PU) film. The lower surface of the dyed layer 1 is coated with a layer of water-repellent layer 10 . The dyed layer 1 is made of superfiber material, the upper surface of the dyed layer 1 is uneven, the upper surface of the dyed layer 1 is provided with a groove 5, and the cross-sectional area of ​​the lower part of the groove 5 is larger than the cross-sectional area of ​​the upper part of the groove 5. The base layer 3 is made of spandex yarn, and the spandex yarn forms several coils 6 on the lower surfac...

Embodiment 2

[0040] The manufacture method of anti-wrinkle anti-pollution microfiber leather comprises the following steps:

[0041] a. Dyeing the dyed layer 1;

[0042] The dyeing process adopts the Italian Bazzoni environmental protection O-type low-tension dyeing machine. The dyeing machine enters the water and divides the cloth into the cloth at room temperature, and adds CD-1000N, stirs it in the auxiliary cylinder of the dyeing machine and opens an automatic feeding system, which will automatically Pump into the dyeing machine, the pH value in the dyeing machine is controlled between 3-6; then enter the process parameters in the computer system: tension 20N, speed 150m / min, nozzle pressure 0.21MP / cm 2, the rotation speed of the main pump is 1005r / min, the bath ratio is 1:5, the pretreatment temperature is 98°C, the heating rate is 2°C / min, and the holding time is 20min; CD-1000N; heat up to the post-treatment temperature of 50°C at a rate of 2°C / min, and hold for 20 minutes. Input ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of apparel fabric, and discloses crease-resistant oil-resistant superfine fiber leather. The crease-resistant oil-resistant superfine fiber leather comprises a dyed layer, a composite film covering on the upper surface of the dyed layer, a basement layer arranged on the lower surface of the dyed layer and a crease-resistant net layer arranged on the lower surface of the basement layer; the dyed layer is made of superfine fiber materials, the crease-resistant net layer is a net-shaped body woven by PTT fibers, and the mesh size of the crease-resistant net layer ranges from 2 mm to 6 mm. The invention further discloses a manufacturing method of the superfine fiber leather. The crease-resistant oil-resistant superfine fiber leather has the properties of wind resistance, moisture permeability, water resistance, oil resistance, warmth retention and good chemical resistance and low temperature resistance, and the peeling strength, the moisture penetrability and the elastic recovery rate of the superfine fiber leather are all high; the crease-resistant net layer can effectively enable the superfine fiber leather to restore from corrugations; the dyed layer is arranged, therefore, when dyeing is conducted, only the dyed layer needs to be dyed, the dyeing cost is reduced, resources are saved, and the dyed layer made of the superfine fiber materials is not prone to color losing.

Description

technical field [0001] The invention relates to the field of clothing materials, in particular to an anti-wrinkle and anti-fouling superfine fiber leather and a manufacturing method thereof. Background technique [0002] At present, the existing clothing materials for making clothes mainly attract the attention of consumers with durability and appearance, and most of the clothing materials are single-layer, for example, single-layer clothing made of pure cotton material, polyester fiber material Single layer material. These clothing materials all have certain performance advantage, also have certain performance defect simultaneously. For example, although pure cotton clothing has a strong moisture absorption and perspiration function, its wrinkle resistance is poor. With the improvement of people's living standards, people have higher and higher requirements for clothing materials, not only requiring beautiful appearance, but also good moisture absorption and ventilation e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06N3/08B32B27/08B32B27/30B32B27/40B32B27/02B32B27/36B32B37/02B32B37/12
Inventor 周文贽蔡裕泰
Owner TIANSHOU FUJIAN SUPERFIBER TECH