Solvent-free polyurethane adhesive with high initial viscosity and preparation method thereof
A solvent-free polyurethane and adhesive technology, used in polymer adhesive additives, adhesive additives and other directions, can solve the problems of small viscosity, low viscosity, quality accidents, etc., to improve the curing speed, popularize the scope of use, expand The effect of using the range
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0026] Example 1:
[0027] Synthesis of A-0
[0028] Put 50 parts of polyoxypropylene glycol with a molecular weight of 1000 and 100 parts of castor oil into the reaction vessel, the reaction temperature is raised to 110 degrees, and the pressure Dehydrate for 2h at <1.3KPa, control the water content below 0.1%, then lower the temperature to below 70 degrees, add 252 parts of diphenylmethane diisocyanate (MDI), react at 85 degrees for 2.5h, filter and discharge the material to obtain A Components.
Example Embodiment
[0029] Example 2:
[0030] Synthesis of A-1
[0031] Put 50 parts of polyoxypropylene glycol with a molecular weight of 1000 and 100 parts of castor oil into the reaction vessel. The temperature is raised to 60 degrees, and 0.2 parts of azobisisobutyronitrile, 15 parts of butyl acrylate, 5 parts are added dropwise. The mixed solution of methyl methacrylate was added dropwise within 2h, kept for 1.5h, and the reaction temperature was raised to 110 degrees. Dehydrate for 2h at <1.3KPa, control the water content below 0.1%, then lower the temperature to below 70 degrees, add 252 parts of diphenylmethane diisocyanate (MDI), react at 85 degrees for 2.5h, filter and discharge the material to obtain A Components.
Example Embodiment
[0032] Example 3:
[0033] Synthesis of A-2
[0034] Put 50 parts of polyoxypropylene glycol with a molecular weight of 1000 and 100 parts of castor oil into a reaction vessel. The temperature is raised to 900 degrees Celsius, and 0.2 parts of benzoyl peroxide, 10 parts of butyl acrylate, and 5 parts of methyl alcohol are added dropwise. The mixed solution of methyl acrylate and 5 parts of hydroxyethyl acrylate, dripped in 2h, keep for 1.5h, raise the reaction temperature to 110 degrees, under pressure Dehydrate for 2h at <1.3KPa, control the water content below 0.1%, then lower the temperature to below 70 degrees, add 252 parts of diphenylmethane diisocyanate (MDI), react at 85 degrees for 2.5h, filter and discharge the material to obtain A Components.
PUM
Property | Measurement | Unit |
---|---|---|
Initial peel strength | aaaaa | aaaaa |
Peel strength | aaaaa | aaaaa |
Peel strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap