Ultraviolet-light-ageing-resistant high-intensity polyethylene IBC inner container material and preparation method

A technology of high-density polyethylene and anti-ultraviolet light, which is applied in the field of blow molding materials, can solve the problems of poor anti-aging performance of products and difficulty in meeting market demand, and achieve outstanding environmental stress cracking resistance, light stability, and environmental stress cracking resistance Excellent performance and light stability, good product quality

Active Publication Date: 2016-01-20
CHINA PETROLEUM & CHEM CORP
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, domestic enterprises have not formed a scale in the special material for IBC barrels, and the prepared products have poor anti-aging performance and various other quality reasons, which cannot meet the production needs of manufacturers.
Therefore, the special materials used in the manufacture of IBC barrels in China are mainly imported materials, which is difficult to meet market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet-light-ageing-resistant high-intensity polyethylene IBC inner container material and preparation method
  • Ultraviolet-light-ageing-resistant high-intensity polyethylene IBC inner container material and preparation method
  • Ultraviolet-light-ageing-resistant high-intensity polyethylene IBC inner container material and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The preparation method of ethylene-hexene copolymerized polyethylene resin:

[0040] The diluent isobutane is always in a circulating state, inject ethylene and hexene into the loop reactor respectively, strictly control the feed ratio of ethylene and hexene, and add a pre-activated catalyst to control the reaction temperature in the reactor to 92.0±2.0 ℃, ethylene feed rate 37.5t / h, hexene-1 / ethylene ratio 17.6kg / t, catalyst 963T feed rate 193kg / h, so that the melt flow rate is 5.95g / 10min and the density is 0.9448kg / m 3 , a weight average molecular weight of 280,000, a molecular weight distribution of 16.4, and an ethylene-hexene copolymerized polyethylene resin with a hexene monomer content of 0.34%.

[0041] Raw materials (parts by weight) of IBC liner material:

[0042] Ethylene Hexene Copolymerized Polyethylene Resin 100

[0043] Antioxidant 0.09

[0044] Auxiliary antioxidant 0.07

[0045] Light stabilizer 0.18

[0046] Among them, the antioxidant is tetraki...

Embodiment 2

[0050] The preparation method of ethylene-hexene copolymerized polyethylene resin:

[0051] The diluent isobutane is always in a circulating state, inject ethylene and hexene into the loop reactor respectively, strictly control the feed ratio of ethylene and hexene, and add a pre-activated catalyst to control the reaction temperature in the reactor to 92.0±2.0 ℃, ethylene feed rate 36.3t / h, hexene-1 / ethylene ratio 18.4kg / t, catalyst 963T feed rate 185kg / h, so that the melt flow rate is 5.84g / 10min and the density is 0.9452kg / m 3 , a weight average molecular weight of 286,000, a molecular weight distribution of 17.7, and an ethylene-hexene copolymerized polyethylene resin with a hexene monomer content of 0.41%.

[0052] Raw materials (parts by weight) of IBC liner material:

[0053] Ethylene Hexene Copolymerized Polyethylene Resin 100

[0054] Antioxidant 0.09

[0055] Auxiliary antioxidant 0.07

[0056] Light stabilizer 0.18

[0057] Among them, the antioxidant is tetraki...

Embodiment 3

[0061] The preparation method of ethylene-hexene copolymerized polyethylene resin:

[0062] The diluent isobutane is always in a circulating state, inject ethylene and hexene into the loop reactor respectively, strictly control the feed ratio of ethylene and hexene, and add a pre-activated catalyst to control the reaction temperature in the reactor to 92.0±2.0 ℃, the ethylene feed rate is 38.1t / h, the hexene-1 / ethylene ratio is 18.8kg / t, and the catalyst 963T feed rate is 204kg / h, so that the melt flow rate is 6.10g / 10min and the density is 0.9455kg / m 3 , a weight average molecular weight of 272,000, a molecular weight distribution of 15.3, and an ethylene-hexene copolymerized polyethylene resin with a hexene monomer content of 0.42%.

[0063] Raw materials (parts by weight) of IBC liner material:

[0064] Ethylene Hexene Copolymerized Polyethylene Resin 100

[0065] Antioxidant 0.09

[0066] Auxiliary antioxidant 0.07

[0067] Light stabilizer 0.18

[0068] Among them, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultraviolet-light-ageing-resistant high-intensity polyethylene IBC inner container material and a preparation method. The ultraviolet-light-ageing-resistant high-intensity polyethylene IBC inner container material is mainly prepared from, by mass, 100 parts of ethylene hexylene copolymer polyethylene resin, 0.05-0.1 part of antioxidant, 0.05-0.1 part of antioxidant aid and 0.15-0.20 part of composite light stabilizer. The invention further discloses a preparation method of the material. An IBC bucket inner container manufactured through the material is good in formability, excellent in environmental stress cracking resistance and light stability, and all mechanical properties are stable.

Description

technical field [0001] The invention relates to a blow molding material, in particular to an anti-ultraviolet light aging high-density polyethylene IBC liner material. Meanwhile, the invention also relates to a preparation method of the material. Background technique [0002] IBC (Intermediate Bulk Container) refers to a composite bulk container with a rigid plastic inner container for shipping liquids. It is mainly composed of high-density polyethylene plastic liner, plastic corner accessories, high-precision ball valve, steel tray base and guardrail steel Composed of racks and other parts, it is a new type of packaging container that can fill Class II and III dangerous goods liquids. The global IBC container has formed a series of products ranging from 1000 to 2000L and has become an indispensable product in the packaging field. As the scope of IBC applications becomes wider and wider, the demand is growing rapidly at an annual growth rate of more than 10%. After my cou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08K5/134C08K5/526C08K5/357C08F210/16C08F210/14
CPCC08F210/16C08F2800/20C08K5/1345C08K5/357C08K5/526C08L2201/08C08L2207/062C08F210/14C08F2500/04C08F2500/07C08L23/0815
Inventor 张玮钟向宏林国易志勤骆新平李伟陈仕兵
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com