One-component beautifying agent with high solid content and preparation method thereof

A technology with high solid content and beautifying agent, applied in the field of caulking agent, it can solve the problems of affecting market competitiveness, low solid content of beautifying agent, gloss of covering pigment, etc., and achieve outstanding anti-contamination and salting-out resistance , enrich the color, improve the effect of solid content

Active Publication Date: 2017-09-29
广东龙湖科技股份有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the solid content of the beautifying agents currently on the market is relatively low, and the gaps between tiles are generally 5-10mm deep. When using beautifying agents for caulking, there are often cases where the paint film shrinks severely after drying and requires secondary caulking. Disadvantages: The essential reason for the low solid content lies in the high price of pigments. Adding a large amount of pigments can certainly increase the solid content of the product, but it also leads to high product costs and affects market competitiveness. However, the solid content of the emulsion itself is low, generally only at 45 % to 50%, and by adding other fillers to increase the solid content of the system, there is a problem that the filler will cover the pigment luster and seriously affect the appearance. Various reasons make the solid content of the existing beautifying agent low, and the product has obvious shrinkage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1. Formula (parts by weight)

[0027] Silicone acrylic emulsion 20 parts

[0028] 5 parts of pearlescent pigment with particle size of 400-600 mesh

[0029] 70 parts of nano fumed silica

[0030] Carbendazim 0.2 parts

[0031] Cason 0.2 parts

[0032] Mingling A203E defoamer 0.2 parts

[0033] Coapur 6050 thickener 0.2 part

[0034] Dodecyl alcohol ester 1 part

[0035] Propylene glycol 1 part

[0036] 97.8 parts by weight

[0037] 2. Preparation:

[0038] According to the above formula, mix the carbendazim, cassone, Mingling A203E defoamer, dodecyl alcohol ester, propylene glycol, and 1 / 2 amount of silicone-acrylic emulsion, and then add them to the disperser at 400 revolutions per minute. Next, add pearlescent pigment and nano fumed silica. After the addition is complete, increase the speed to 1000 rpm, disperse for 15-20 minutes, then reduce the speed to 450 rpm, slowly add the remaining silicone acrylic emulsion, and disperse 2~ After 3 minutes, add Coapur 6050 thickener dropwise ...

Embodiment 2

[0040] 1. Formula

[0041] Silicone acrylic emulsion 25 parts

[0042] 8 parts of pearlescent pigment with particle size of 600-800 mesh

[0043] 70 parts of nano fumed silica

[0044] Carbendazim 0.2 parts

[0045] Cason 0.2 parts

[0046] Mingling A203E defoamer 0.2 parts

[0047] Coapur 6050 thickener 0.2 part

[0048] Dodecyl alcohol ester 1 part

[0049] Ethylene glycol 1 part

[0050] Total parts by weight 105.8 parts

[0051] 2. Preparation:

[0052] According to the above formula, mix carbendazim, cassone, Mingling A203E defoamer, dodecyl alcohol ester, ethylene glycol, 2 / 5 amount of silicone-acrylic emulsion, and then add it to the disperser at 400 rpm Add pearlescent pigment and nano fumed silica at a minute speed. After the addition is complete, increase the speed to 1000 rpm, disperse for 15-20 minutes, then reduce the speed to 450 rpm, slowly add the remaining silicone acrylic emulsion, and disperse After 2 to 3 minutes, add Coapur 6050 thickener dropwise at a speed of 1000 revo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a one-component beauty joint agent with high solid content, which comprises 20-30 parts by weight of silicone acrylic emulsion, 5-8 parts of pearlescent pigment, and 55-70 parts of transparent filler , 0.2-0.5 parts of preservatives, 0.2-0.5 parts of fungicides, 0.2-0.5 parts of defoamers, 0.2-0.5 parts of thickeners and 1-1.5 parts of film-forming aids, of which silicone acrylic emulsion It is a copolymer emulsion of organosiloxane and acrylate, the pearlescent pigment is pearlescent pigment powder with a particle size of 400 mesh to 800 mesh, and the transparent filler is nano fumed silica. The beautifying joint agent of the present invention has high solid content and can effectively solve the problem of severe shrinkage after construction and cannot be molded at one time. It has soft pearl luster and rich colors, as well as high waterproof performance and good weather resistance, which is especially suitable for Use as a grout for high-grade tiles, mosaics or stone. The present invention also provides a preparation method of the above-mentioned one-component beauty joint agent with high solid content.

Description

Technical field [0001] The invention relates to a sealant, in particular to a beautifying agent whose decoration and practicability are obviously better than that of a colored sealant, and more specifically to a one-component beautifying agent with high solid content. The invention also relates to a preparation method of the above-mentioned beautifying seam agent. Background technique [0002] With the development of society, tiles, mosaics or stone have become one of the most commonly used materials in the field of architectural decoration. In order to facilitate transportation and storage, the size of the finished ceramic tiles, mosaics or stones should not be too large. Therefore, to form the entire wall or floor, it needs to be tiled piece by piece. Considering the factors of thermal expansion and contraction, In the process of laying ceramic tiles, mosaics or stone, certain gaps need to be reserved between the blocks, and these gaps need to be filled with a caulking agent. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/08C09D5/16C09D7/12
Inventor 林森安洪永顺刘双华刘亚芹陈晓丹
Owner 广东龙湖科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products