Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method for high-dispersion deposition white carbon black

A technology of precipitated silica and high dispersion, which is applied in the treatment of fibrous fillers and dyed organosilicon compounds. It can solve the problems of unfavorable industrialization and rising production costs, so as to reduce surface energy, improve processing performance, and reduce time and cost. Effect

Active Publication Date: 2016-01-27
SHENYANG RES INST OF CHEM IND
View PDF9 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adding water-soluble polymers to the reaction can only produce silica with high purity by supercritical drying process, which leads to an increase in production costs and is not conducive to industrialization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for high-dispersion deposition white carbon black

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] 1) Preparation of umbrella-shaped siloxane dispersant

[0025] The trisiloxane surfactant of 271 grams is joined in the n-butyl acrylate of 172 grams, then adding concentration is 1.2 grams of chloroplatinic acid of 5wt%, the reaction temperature is raised to 85 ℃, and the reaction time is 1 hour, obtained Umbrella silicone coupling agent.

[0026] 2) Preparation of highly dispersed precipitated silica

[0027] Add 100 grams of precipitated white carbon black into 900 grams of absolute ethanol and stir to obtain a uniformly dispersed suspension of white carbon black. Add 10 grams of the umbrella-shaped silicone dispersant prepared in the above step 1) and 10 grams of mercaptotrimethoxysilane coupling agent to the suspension, and then add 4 grams of p-toluenesulfonic acid to adjust the pH of the solution to 4. Then the prepared solution was placed in a water bath and heated to 50°C. React for 4 hours and cool to room temperature. The ethanol solvent is removed by rot...

Embodiment 2

[0029] The difference from Example 1 is:

[0030] Add 100 grams of precipitated white carbon black into 900 grams of absolute ethanol and stir to obtain a uniformly dispersed suspension of white carbon black. 15 grams of the umbrella-shaped silicone dispersant prepared in the above step 1) and 5 grams of vinyltrimethoxysilane coupling agent were added to the suspension, and then 4 grams of sulfuric acid was added to adjust the pH value of the solution to 5. The prepared solution was then placed in a water bath and heated to 79°C. React for 1 hour, cool to room temperature, and then remove the ethanol solvent by rotary evaporation, then dry, pulverize, and finally obtain the final high-dispersion precipitated white carbon black.

Embodiment 3

[0032] 1) Preparation of umbrella-shaped siloxane dispersant

[0033] The trisiloxane surfactant of 271 grams is joined to the α olefin of 286 grams C14-C18, then adding concentration is 1.2 grams of chloroplatinic acid of 5wt%, the temperature of reaction is raised to 75 ℃, and the reaction time is 2 hours, preparation Obtain umbrella-shaped siloxane coupling agent.

[0034] 2) Preparation of highly dispersed precipitated silica

[0035] Add 100 grams of precipitated white carbon black into 900 grams of absolute ethanol and stir to obtain a uniformly dispersed suspension of white carbon black. Add 5 grams of the umbrella-shaped silicone dispersant prepared in the above step 1) and 15 grams of mercaptotrimethoxysilane coupling agent to the suspension, and then add 4 grams of p-toluenesulfonic acid to adjust the pH value of the solution to 6. Then the prepared solution was placed in a water bath and heated to 30°C. React for 6 hours, cool to room temperature, then remove the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for white carbon black, and concretely relates to a preparation method for high-dispersion deposition white carbon black. A white carbon black suspension, an umbrella-shaped siloxane dispersant and a siloxane coupling agent containing sulfydryls or carbon-carbon double bonds are mixed, the pH value is adjusted to 2-7 after mixing, the mixture is heated to 30-79 DEG C and reacted for 1-6h, and high-dispersion deposition white carbon black is obtained. The umbrella-shaped siloxane dispersant and the white carbon black suspension are mixed at a mass ratio of 1:1-1:20. The siloxane coupling agent and the white carbon black suspension are mixed at a mass ratio of 1:1-1:20. The prepared white carbon black has superstrong hydrophobicity, the processing performance in subsequent preparation of rubber compounds can be raised effectively, dynamic mechanical properties of vulcanized rubber as tyre tread rubber can be improved effectively, the rolling resistance of tread rubber is lowered effectively, and the wear resistant performance of tread rubber is raised.

Description

technical field [0001] The invention relates to a preparation method of white carbon black, in particular to a preparation method of highly dispersed precipitated white carbon black. Background technique [0002] White carbon black is the general term for white powdery silicic acid and silicate products, mainly refers to precipitated silica, fumed silica, ultrafine silica gel and aerogel, and also includes powdered synthetic aluminum silicate and calcium silicate etc. Precipitated silica is widely used as a reinforcing filler material in elastic or rubber materials. For example, they have been used as white reinforcing agents in vehicle tires. In order to make the performance of tire rubber good, silica must have a high binding effect with rubber molecules and have good dispersion in tire rubber. [0003] Compared with fumed silica, ordinary precipitated silica has the advantage of low cost. However, because precipitated silica contains a large amount of silanol and has ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/28C09C3/12
Inventor 李嵬刘冬雪王新王元霞
Owner SHENYANG RES INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com