Wear-resistance and corrosion-resistance polyurethane paint

A polyurethane paint and corrosion-resistant technology, applied in the field of polyurethane paint, can solve the problems of lack of hardness and wear resistance, corrosion pollution, easy scratching of polyurethane paint, etc., and achieve the effect of good protection, improved protection and high hardness

Inactive Publication Date: 2016-01-27
天津渤海望亚涂料有限公司
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the general one-component polyurethane paint is still lacking in hardness and wear resistance. As time goes by, the polyurethane paint on furniture and metal surfaces is easily scratched and polluted by corrosion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A wear-resistant and corrosion-resistant polyurethane paint, prepared from the following raw materials in parts by weight: 90 parts of polyurethane, 15 parts of silicon dioxide, 10 parts of titanium dioxide, 25 parts of asphalt, 15 parts of nano-alumina, and 20 parts of zirconia , 20 parts of silicon nitride, 30 parts of talc, 25 parts of phenolic resin, 10 parts of butyl methacrylate, 20 parts of epoxy resin, and 10 parts of dispersing aid.

[0012] The dispersion aid is composed of the following raw materials in parts by weight: 60 parts of diatomite, 20 parts of jade powder, 10 parts of silane coupling agent, 15 parts of acrylate, 8 parts of pentaerythritol triacrylate. The preparation method is to add diatomite to 10 parts % hydrochloric acid solution for 5 hours, take it out and rinse it with clean water, place it in a calciner at 550°C for 4 hours, and after natural cooling, grind it together with jade powder to form a 300-mesh powder, add silane coupling agent, ac...

Embodiment 2

[0015] A wear-resistant and corrosion-resistant polyurethane paint, prepared from the following raw materials in parts by weight: 100 parts of polyurethane, 20 parts of silicon dioxide, 15 parts of titanium dioxide, 30 parts of asphalt, 20 parts of nano-alumina, and 22 parts of zirconia , 22 parts of silicon nitride, 40 parts of talc, 30 parts of phenolic resin, 15 parts of butyl methacrylate, 25 parts of epoxy resin, and 15 parts of dispersing aid.

[0016] The dispersing aid has the following raw materials in parts by weight: 70 parts of diatomite, 25 parts of jade powder, 15 parts of silane coupling agent, 20 parts of acrylate, 10 parts of pentaerythritol triacrylate. Add 10% hydrochloric acid solution and soak for 5.5 hours, take it out, rinse it with clean water, put it in a calciner at 550°C for 4.5 hours, and after natural cooling, grind it together with jade powder to form a 300-mesh powder, add silane coupling agent, acrylic acid ester and pentaerythritol triacrylate,...

Embodiment 3

[0019] A wear-resistant and corrosion-resistant polyurethane paint, prepared from the following raw materials in parts by weight: 110 parts of polyurethane, 25 parts of silicon dioxide, 20 parts of titanium dioxide, 35 parts of asphalt, 25 parts of nano-alumina, and 24 parts of zirconia , 24 parts of silicon nitride, 50 parts of talcum powder, 35 parts of phenolic resin, 20 parts of butyl methacrylate, 30 parts of epoxy resin, and 20 parts of dispersing aid.

[0020] The dispersing aid consists of the following raw materials in parts by weight: 80 parts of diatomite, 30 parts of jade powder, 20 parts of silane coupling agent, 25 parts of acrylate, 12 parts of pentaerythritol triacrylate. The preparation method is to add diatomaceous earth to 10 parts % hydrochloric acid solution for 6 hours, take it out, rinse it with clean water, place it in a calciner at 550°C for 5 hours, and after natural cooling, grind it together with jade powder to form a 300-mesh powder, add silane coup...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a wear-resistance and corrosion-resistance polyurethane paint, which is prepared from the raw materials such as polyurethane, silicon dioxide, titanium dioxide, asphalt, nanometer aluminum oxide, zirconium oxide, silicon nitride, talc powder, a phenolic resin, butyl methacrylate, an epoxy resin and a dispersing auxiliary agent, wherein the dispersing auxiliary agent is prepared from diatomaceous earth, jade powder, a silane coupling agent, acrylate and pentaerythritol triacrylate. According to the present invention, the paint has characteristics of extremely strong corrosion resistance, saline resistance, alkali resistance, good metal protection effect, high hardness, wear resistance, compression resistance, substantially-improved paint protection effect, strong paint stability, easy use, and easy operation.

Description

technical field [0001] The invention relates to the technical field of paint production, in particular to a wear-resistant and corrosion-resistant polyurethane paint. Background technique [0002] As an important coating, polyurethane paint has good corrosion resistance and has been widely used in home decoration and furniture coating. Polyurethane paint has properties such as high hardness, plump paint film, and good wear resistance, and is widely used in cabinet furniture, metal protection, etc. However, general one-component polyurethane paints are still lacking in hardness and wear resistance. As time goes by, polyurethane paints on furniture and metal surfaces are easily scratched and polluted by corrosion. Contents of the invention [0003] The object of the present invention is to provide a kind of wear-resistant and corrosion-resistant polyurethane paint that has good protective effect on metal and furniture surface, to solve the problems raised in the above-menti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/00C09D5/08C08F291/00
Inventor 吴津生
Owner 天津渤海望亚涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap