A kind of imitation wood floor

A technology of imitation wood floor and base layer, which is applied in the field of imitation wood floor, can solve the problems such as formaldehyde release, and achieve the effect of good woody feeling, not cold feeling, and good woody feeling

Active Publication Date: 2018-10-16
广东惠众新材料科技股份有限公司 +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The transfer-printed composite wooden floor provided by the prior art saves wood, but uses high-density fiberboard as the matrix, which will cause the release of formaldehyde

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of imitation wood floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0093] Dissolve 20 g of sodium hydroxide in 100 g of sodium water glass, add 5 g of water and mix and cool to room temperature to obtain the first liquid raw material;

[0094] The fly ash of 100g, the slag of 10g and the silica sand of 50g are mixed, obtain the first solid raw material;

[0095]Mix 7.55g of styrene-acrylic emulsion, 4.53g of alkali-resistant glass fiber and 1.51g of polycarboxylate water reducer to obtain the first additive;

[0096] Mixing the first solid raw material, the first liquid raw material and the first additive according to a mass ratio of 100:25:5 to obtain a base compound;

[0097] Distributing the base layer mixture into a mold of 120mm × 60mm × 15mm to make it smooth and even to form a base layer with a thickness of 10mm;

[0098] The potassium hydroxide of 15g is dissolved in the potassium water glass of 100g, is cooled to room temperature after adding the water of 5g mixing, obtains the second liquid raw material;

[0099] 100g of calcined ...

Embodiment 2

[0109] Dissolving 5 g of potassium hydroxide in 100 g of potassium water glass, adding 1 g of water and mixing, cooling to room temperature to obtain the first liquid raw material;

[0110] 100g of fly ash, 1g of slag and 30g of silica sand are mixed to obtain the first solid raw material;

[0111] Mix 1.31g of silicone-acrylic emulsion, 1.31g of alkali-resistant glass fiber and 0.655g of melamine-based water reducer to obtain the first additive;

[0112] Mixing the first solid raw material, the first liquid raw material and the first additive according to a mass ratio of 100:1:1 to obtain a base compound;

[0113] Distributing the base layer mixture into a mold of 120mm × 60mm × 15mm to make it smooth and even to form a base layer with a thickness of 5mm;

[0114] Dissolving 5g of lithium hydroxide in 100g of lithium water glass, adding 1g of water and mixing, cooling to room temperature to obtain a second liquid raw material;

[0115] 100g of calcined kaolin, 1g of slag an...

Embodiment 3

[0125] Dissolving 40g of lithium hydroxide in 100g of lithium water glass, adding 10g of water and mixing, cooling to room temperature to obtain the first liquid raw material;

[0126] The fly ash of 100g, the slag of 20g and the silica sand of 70g are mixed, obtain the first solid raw material;

[0127] Mix 19g of pure acrylic emulsion, 9.5g of alkali-resistant glass fiber and 5.7g of naphthalene-based water reducer to obtain the first additive;

[0128] Mixing the first solid raw material, the first liquid raw material and the first additive according to a mass ratio of 100:50:10 to obtain a base compound;

[0129] Distributing the base layer mixture into a mold of 120mm × 60mm × 15mm to make it smooth and even to form a base layer with a thickness of 15mm;

[0130] Dissolve 4g of sodium hydroxide in 100g of sodium water glass, add 10g of water and mix and cool to room temperature to obtain a second liquid raw material;

[0131] 100g of calcined kaolin, 20g of slag and 70g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a simulated wood floor, which comprises a base layer, a coloring layer arranged at the surface of the base layer, a color layer arranged at the surface of the coloring layer and a texture layer arranged at the surface of the color layer, wherein the base layer and the coloring layer are prepared independently by solid materials, liquid materials and additives; the solid materials comprise mineral powder and sand; the liquid materials comprise an alkali metal hydroxide, water glass and water; the texture layer is prepared by a high polymer material, an inorganic powder material and a coupling agent, and the high polymer material is formed by solidification of polyurethane and a solidification agent. The simulated wood floor provided by the invention has a unique structure design, and various materials in each layer are interacted, so that the simulated wood floor is enabled to have good abrasive resistance and excellent wood texture. In addition, the simulated wood floor is good in fire retardancy and free of formaldehyde release.

Description

technical field [0001] The invention relates to the field of floor technology, in particular to a wood-like floor. Background technique [0002] Imitation wood flooring is a type of flooring that looks similar to wooden floor patterns and patterns, mainly including ceramic imitation wood grain flooring, plastic imitation wood flooring, and composite wood flooring. The ceramic imitation wood grain floor is glazed and printed on the surface of the wood grain color by inkjet printing or transfer printing. The material of this imitation wood floor is still ceramics, the surface is hard, and it lacks the soft texture of wood. [0003] The plastic imitation wood floor is based on plastic, and the floor with wood grain effect on the surface of the board is realized by embossing on the surface of the substrate. Some fillers and other additives are added to the plastic imitation wood floor to ensure the performance. The Chinese patent that application number is 200710039105.8 disclo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F15/02C04B28/26
Inventor 贾屹海王川行何伟发陈思颖
Owner 广东惠众新材料科技股份有限公司