Alkaline platinum plating P salt electroplating bath and electroplating method thereof

An alkaline platinum plating and electroplating solution technology, applied in the field of platinum electroplating, can solve the problems of low plating solution current efficiency, poor plating quality, poor plating solution performance, etc., and achieve good plating quality, excellent plating solution performance, and cathode current. Efficient effect

Inactive Publication Date: 2016-03-09
WUXI QINGYANG MACHINERY MFG
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the process is relatively simple, the current efficiency of the plating solution is low, the performance of the plating solution is poor, and the quality of the coating is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alkaline platinum plating P salt electroplating bath and electroplating method thereof
  • Alkaline platinum plating P salt electroplating bath and electroplating method thereof
  • Alkaline platinum plating P salt electroplating bath and electroplating method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The formulation of the electroplating solution is as follows:

[0027]

[0028] Plating process conditions: the pulse width of single pulse square wave current is 0.5ms, the duty cycle is 30%, and the average current density is 0.5A / dm 2 ; The pH is 11, the temperature is 70°C, and the electroplating time is 40min.

Embodiment 2

[0030] The formulation of the electroplating solution is as follows:

[0031]

[0032] Plating process conditions: the pulse width of single pulse square wave current is 0.6ms, the duty cycle is 25%, and the average current density is 0.8A / dm 2 ; The pH is 13, the temperature is 80° C., and the electroplating time is 35 minutes.

Embodiment 3

[0034] The formulation of the electroplating solution is as follows:

[0035]

[0036]

[0037] Plating process conditions: the pulse width of single pulse square wave current is 0.8ms, the duty cycle is 20%, and the average current density is 3A / dm 2 ; The pH is 12, the temperature is 70°C, and the electroplating time is 20min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses alkaline platinum plating P salt electroplating bath and an electroplating method of the electroplating bath. The electroplating bath comprises, by platinum, 20-30 g / L of P salt, 90-110 g / L of ammonium nitrate, 8-12 g / L of potassium nitrite or sodium nitrite and 2-6 mg / L of calcium chloride by calcium. The ammonium nitrate and the potassium nitrite or sodium are taken as auxiliary salt, and strontium chloride serves as a brightening agent, so that the obtained electroplating bath has the good dispersion force and deep plating capacity, the current efficiency of a negative pole is high, and the performance of the plating bath is excellent. A coating obtained through electroplating of the electroplating bath under the alkaline condition is low in porosity, high in brightness and good in quality.

Description

technical field [0001] The invention relates to the technical field of electroplating platinum, in particular to a P-salt electroplating solution for alkaline platinum plating and an electroplating method thereof. Background technique [0002] Platinum has superior properties and is widely used. In the jewelry industry, it is mainly used as decorations and handicrafts. In the chemical industry, it is used to manufacture advanced chemical vessels, platinum crucibles, electrodes and catalysts to accelerate chemical reactions. Platinum-iridium alloy is the material from which fountain pen nibs are made. Especially in the automobile industry, platinum plays an irreplaceable role in exhaust gas treatment, and its consumption accounts for almost half of the platinum industry's consumption. because. However, platinum resources are scarce and expensive, which restricts the application of platinum electrodes. Therefore, platinum-plated materials are used to replace pure platinum ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D3/52C25D5/18
Inventor 唐靖岚
Owner WUXI QINGYANG MACHINERY MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com