Environment-friendly polyurethane composite plastic runway material and preparation method thereof

A plastic track, polyurethane technology, applied in the field of polymer materials, can solve problems such as human health hazards, and achieve the effect of good wear resistance and good tensile strength

Inactive Publication Date: 2016-03-23
SUZHOU FAST INFORMATION TECH CO LTD
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now many primary and secondary schools are also laying polyurethane plastic tracks on sports grounds, but these polyurethane tracks will still cause harm to human health
However, nowadays there are frequent reports about the "poisonous runway"; in addition, with the development of national fitness, the demand for the application of plastic runways is also increasing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The environmentally friendly polyurethane composite plastic runway material in this embodiment includes the following components in parts by weight: 42 parts of polyether polyol, 18 parts of isocyanate, 10 parts of modified polypropylene, 7 parts of 9,10-phenanthrenequinone, 1,4 cyclohexyl 5 parts of dimethanol, 3 parts of polyvinyl alcohol, 1 part of polymethylol fiber, 4 parts of silicone powder, 2 parts of stainless steel fiber, 3 parts of ethylene bis stearic acid amide, 0.5 part of catalyst, 8 parts of filler, anti-aging agent 0.2 parts, 0.4 parts of flame retardant, 0.5 parts of pigment;

[0028] Wherein, the functionality of the polyether polyol is 2, and the hydroxyl value is 150-500 mgKOH / g;

[0029] Described isocyanate is diphenylmethane diisocyanate;

[0030] The preparation method of the modified polypropylene is as follows: add calcium silicate powder and serine into a stirring tank, heat to 95°C, mix and stir, then add a silane coupling agent, and contin...

Embodiment 2

[0041] The environmentally friendly polyurethane composite plastic runway material in this embodiment includes the following components in parts by weight: 65 parts of polyether polyol, 32 parts of isocyanate, 116 parts of modified polypropylene, 16 parts of 9,10-phenanthrenequinone, and 1,4 cyclohexyl 12 parts of dimethanol, 8 parts of polyvinyl alcohol, 6 parts of polymethylol fiber, 8 parts of silicone powder, 5 parts of stainless steel fiber, 9 parts of ethylene bis stearic acid amide, 3 parts of catalyst, 15 parts of filler, anti-aging agent 1.4 parts, 1 part of flame retardant, 2 parts of pigment;

[0042] Wherein, the functionality of the polyether polyol is 4, and the hydroxyl value is 250~600mgKOH / g;

[0043] Described isocyanate is toluene isocyanate;

[0044] The preparation method of the modified polypropylene is as follows: add calcium silicate powder and serine into a stirring tank, heat to 95°C, mix and stir, then add a silane coupling agent, and continue stirr...

Embodiment 3

[0055] The environmentally friendly polyurethane composite plastic runway material in this embodiment includes the following components in parts by weight: 53 parts of polyether polyol, 25 parts of isocyanate, 14 parts of modified polypropylene, 11 parts of 9,10-phenanthrenequinone, and 1,4 cyclohexyl 8 parts of dimethanol, 6 parts of polyvinyl alcohol, 3 parts of polymethylol fiber, 6 parts of silicone powder, 3 parts of stainless steel fiber, 6 parts of ethylene bis stearic acid amide, 1.6 parts of catalyst, 11 parts of filler, anti-aging agent 0.8 parts, 0.7 parts of flame retardant, 1.2 parts of pigments;

[0056] Wherein, the functionality of the polyether polyol is 3;

[0057] Described isocyanate is diphenylmethane diisocyanate;

[0058] The preparation method of the modified polypropylene is as follows: add calcium silicate powder and serine into a stirring tank, heat to 95°C, mix and stir, then add a silane coupling agent, and continue stirring for 45 minutes; wait f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly polyurethane composite plastic runway material. The plastic runway material is prepared from the following components in parts by weight: 42 parts of polyether polyol, 18 parts of isocyanate, 10 parts of modified polypropylene, 7 parts of 9, 10-phenanthrenequinone, 5 parts of 1,4-cyclohexynol, 3 parts of polyvinyl alcohol, 1 part of polycarboxymethyl fiber, 4 parts of silicone powder, 2 parts of stainless steel fiber, 3 parts of ethylene bis stearamide, 0.5 part of catalyzer, 8 parts of filler, 0.2 part of antiager, 0.4 part of flame-retardant and 0.5 part of pigment. The invention also discloses a preparation method of the environment-friendly polyurethane composite plastic runway material. The plastic runway material prepared by the preparation method disclosed by the invention is not only green and environment-friendly, but also has excellent tensile strength, elongation at break, rebound resilience and flame retardance. Besides, a testing result also displays that the prepared plastic runway material of each embodiment has good wear resistance and meets actual application demands.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an environment-friendly polyurethane composite plastic runway material and a preparation method thereof. Background technique [0002] The plastic track began in the 1960s with the plastic horse racing track laid by the 3M company in the United States with polyurethane materials. Compared with cinder and gravel fields, the plastic runway has the advantages of good elasticity, good shock absorption performance, wear resistance and anti-aging, does not pollute the environment, and is easy to clean and maintain. For this reason, the plastic track has been internationally recognized as the best race track. [0003] The polyurethane plastic runway used in the Bird's Nest Stadium of the 2008 Olympic Games in my country has the advantages of good elasticity, shock absorption, skid resistance, wear resistance and easy cleaning and maintenance. Now many primary and secondary s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08L23/12C08L29/04C08L1/28C08L83/04C08K13/04C08K3/34C08K5/17C08K5/053C08K7/06C08K5/20C08G18/48C08G18/76
CPCC08L75/08C08G18/4825C08G18/7671C08L2201/02C08L2205/035
Inventor 彭孝茹
Owner SUZHOU FAST INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com