Preparation method of resin dispersed titanium carbide silicon carbide-carbon fiber friction material

A titanium carbide silicon carbide and friction material technology, which is applied in the field of friction material preparation, can solve problems such as reduced friction performance and potential safety hazards, and achieve the effects of improving wear resistance and high manufacturing cost.

Inactive Publication Date: 2016-03-30
SHANDONG UNIV OF TECH
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the friction performance of C / C composite materials will be reduced in a humid environment, which will bring serious safety hazards to the use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] (1) Set the density to 1.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixed gas of propane gas and nitrogen at a temperature of 900°C. The molar ratio of propane gas: nitrogen is 1:4, the flow rate is controlled at 50ml / min, and the carburizing treatment is performed for 24 hours to obtain a carburized carbon fiber blanket. ;

[0020] (2) Immerse the above-mentioned carburized carbon fiber blanket into a titanium carbide resin slurry with a particle size of less than 0.3 μm and a content of 5%, place it in an ultrasonic cleaner and fill it with titanium carbide for 50 minutes, take it out and dry it to prepare a titanium carbide filled carbon fiber blanket, The resin slurry is a 5% ethanol solution containing phenolic resin;

[0021] (3) Pass the above-mentioned filled titanium carbide carbon fiber blanket into a mixed gas of trichloromethylsilane gas, hydrogen gas and argon gas at a temperature of 900 °C, and the molar ratio of trichloromethylsilane gas:...

Embodiment 2

[0025] (1) Set the density to 0.8g / cm 3 The graphitized carbon fiber blanket is fed with a mixture of propane gas and nitrogen at a temperature of 1000°C. The molar ratio of propane gas: nitrogen is 1:5, the flow rate is controlled at 350ml / min, and the carburizing treatment is performed for 18 hours to obtain a carburized carbon fiber blanket. ;

[0026] (2) Immerse the above-mentioned carburized carbon fiber blanket into a titanium carbide resin slurry with a particle size of less than 0.3 μm and a content of 12%, place it in an ultrasonic cleaner and fill it with titanium carbide for 40 minutes, take it out and dry it to obtain a carbon fiber blanket filled with titanium carbide, The resin slurry is a 12% ethanol solution containing phenolic resin;

[0027] (3) Pass the above-mentioned filled titanium carbide carbon fiber blanket into a mixed gas of trichloromethylsilane gas, hydrogen gas and argon gas at a temperature of 1000 °C, and the molar ratio of trichloromethylsila...

Embodiment 3

[0031] (1) Set the density to 0.1g / cm 3 The graphitized carbon fiber blanket is fed with a mixed gas of propane gas and nitrogen at a temperature of 1100°C. The molar ratio of propane gas: nitrogen is 1:6, the flow rate is controlled at 600ml / min, and the carburizing treatment is performed for 10 hours to obtain a carburized carbon fiber blanket. ;

[0032] (2) Immerse the above-mentioned carburized carbon fiber blanket into a titanium carbide resin slurry with a particle size of less than 0.3 μm and a content of 20%, place it in an ultrasonic cleaner and fill it with titanium carbide for 30 minutes, take it out and dry it to obtain a carbon fiber blanket filled with titanium carbide, The resin slurry is a 20% ethanol solution containing phenolic resin;

[0033] (3) Pass the above-mentioned filled titanium carbide carbon fiber blanket into a mixed gas of trichloromethylsilane gas, hydrogen gas and argon gas at a temperature of 1100 °C, and the molar ratio of trichloromethylsi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

A preparation method of a resin dispersed titanium carbide silicon carbide-carbon fiber friction material is characterized in that a graphited carbon fiber blanket with the density of 0.1-1.8g / cm<3> is subjected to carburizing treatment, and then is subjected to resin dispersed titanium carbide filling treatment, silicon carbide deposition treatment is performed, embedment siliconizing treatment is performed, and nitriding treatment is performed in a nitrogen atmosphere to obtain the resin dispersed titanium carbide silicon carbide-carbon fiber friction material. The preparation of the friction material is realized by adopting the graphited carbon fiber blanket through the steps such as carburizing, titanium carbide filling, silicon carbide deposition, embedment siliconizing and nitriding, and the prepared friction material has high strength, high tenacity and high friction performance, and adapts to various weather conditions.

Description

technical field [0001] The invention relates to a preparation method of a friction material composited by carbon fiber and ceramic material, and belongs to the technical field of composite material preparation. Background technique [0002] At present, carbon fiber and carbon (C / C) composite materials are mainly used as friction materials. Since the wear resistance of C / C composite materials is relatively low, people are looking for a method for preparing friction materials with higher wear resistance. In addition, the friction performance of C / C composite materials will be reduced in a humid environment, which will bring serious safety hazards to the use. Contents of the invention [0003] The object of the present invention is to provide a method for preparing a friction material that can overcome the above-mentioned defects, achieve higher strength, higher friction performance and adapt to various climatic conditions. Its technical solution is: [0004] The preparatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/80C04B35/56C04B35/565C04B35/584C04B35/634C04B35/65C04B35/622
CPCC04B35/5611C04B35/565C04B35/584C04B35/622C04B35/63476C04B35/65C04B35/806C04B2235/428C04B2235/46
Inventor 唐竹兴
Owner SHANDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com