Composite sound-insulation material and preparation method thereof
A technology of sound insulation materials and materials, applied in the field of sound insulation materials, can solve the problems of limited application scope, high cost, bulky and thick, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0038] like figure 1 Shown: the preparation method of the composite sound insulation material comprises the following steps:
[0039] (1) Metering and preparation: Weigh each component according to the mass fraction, stir the recovered steel slag powder and coupling agent in a high-speed mixer for 5-10 minutes, and control the stirring temperature at 90-110 °C to complete the surface treatment of the steel slag powder. activation treatment;
[0040] (2) Sequential feeding and high-speed dispersion: firstly add recycled polyethylene, linear low-density polyethylene and polymer compatibilizer to the mixed materials in step (1), stir at high speed for 3-5 minutes, and control the stirring temperature at 70-80 ℃; then add diluent and antioxidant, stir at high speed for 3 to 5 minutes, and control the stirring temperature at 70 to 90 °C;
[0041] (3) Banburying and plasticizing: add the materials mixed in step (2) into the Banbury mixer and knead for 15-20min, the banburying temp...
Example Embodiment
[0051] Example 1:
[0052] The ingredients are prepared according to Table 1.
[0053] Table 1 The mass fraction of each component
[0054]
[0055] The preparation steps are as follows:
[0056] (1) Stir 75% steel slag powder and 1% silane coupling agent in a high-speed mixer for 10 minutes, and control the stirring temperature at 110 °C to complete the activation treatment of the surface of the steel slag powder.
[0057] (2) Put 15% recycled polyethylene, 5% linear low density polyethylene and 2.5% maleic anhydride grafted polyethylene into the mixed materials in step (1) and stir at high speed for 5 minutes, and the stirring temperature is controlled at 80 °C; then Add 1% chlorinated paraffin 42, 0.3% antioxidant 1010 and 0.2% antioxidant 168, stir at high speed for 5 min, and control the stirring temperature at 90 °C.
[0058] (3) Add the materials mixed in step (2) into the internal mixer and knead for 20 minutes, and the temperature of each section of the internal m...
Example Embodiment
[0063] Example 2
[0064] The ingredients are prepared according to Table 3.
[0065] Table 3 The mass fraction of each component
[0066]
[0067] The preparation steps are as follows:
[0068] (1) 65% steel slag powder and 1.2% titanate coupling agent were stirred in a high-speed mixer for 8 minutes, and the stirring temperature was controlled at 100 °C to complete the activation treatment of the surface of the steel slag powder.
[0069] (2) Put 18% recycled polyethylene, 8% linear low density polyethylene and 5% maleic anhydride grafted ethylene-vinyl acetate copolymer into the mixed materials in step (1) and stir at high speed for 4 minutes, and the stirring temperature is controlled at 75°C; then add 2% chlorinated paraffin 52, 0.5% antioxidant 1010 and 0.3% antioxidant 168, stir at high speed for 4 min, and control the stirring temperature at 80°C.
[0070] (3) Add the mixed materials in step (2) into the internal mixer and knead for 18 minutes. The temperature of...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Areal density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap