P-type silicon solar cell and preparing method thereof

A solar cell, p-type silicon technology, applied in the field of solar cells, can solve problems such as low conversion efficiency, and achieve the effects of increasing lifespan, increasing open circuit voltage, and reducing manufacturing costs

Inactive Publication Date: 2016-04-13
HEBEI UNIVERSITY
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] One of the purposes of the present invention is to provide a p-type silicon solar cell to solve the problem of low conversion efficiency of existing p-type silicon solar cells

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • P-type silicon solar cell and preparing method thereof
  • P-type silicon solar cell and preparing method thereof
  • P-type silicon solar cell and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1, a p-type silicon solar cell.

[0030] Such as figure 1As shown, the p-type silicon solar cell provided in this embodiment includes a p-type silicon substrate 4, and the p-type silicon substrate 4 may be a single crystal p-type silicon substrate or a polycrystalline p-type silicon substrate. On the front side of the p-type silicon substrate 4, n + doped layer 3, the n + An anti-reflection layer 2 is formed on the doped layer 3, and a front electrode 1 is formed on the anti-reflection layer 2 through screen printing and sintering processes. After sintering, the front electrode 1 will pass through the anti-reflection layer 2 and n + The doped layers 3 are in contact.

[0031] The back side passivation layer 5 is formed on the back side of the p-type silicon substrate 4, and the main material of the back side passivation layer 5 is a ferroelectric thin film material, and the ferroelectric thin film material can be, for example, lead zirconate titanate (PZT)...

Embodiment 2

[0032] Embodiment 2, a preparation method of a p-type silicon solar cell.

[0033] The preparation method of the p-type silicon solar cell provided in this embodiment includes the following steps:

[0034] ①. Select a p-type silicon substrate, and clean the selected p-type silicon substrate. After cleaning, texture the front and back of the p-type silicon substrate respectively. The p-type silicon substrate can be a single crystal p-type silicon substrate, or a polycrystalline p-type silicon substrate. When it is a single crystal p-type silicon substrate, alkali is generally used to texture it, and finally a regular pyramidal light trapping structure is formed. When it is a polycrystalline p-type silicon substrate, acid is generally used to texture it, and finally a regular uneven pit-shaped surface light-trapping structure is formed. In this embodiment, the p-type silicon substrate is a single crystal p-type silicon substrate, and the average height of the pyramids formed a...

Embodiment 3

[0055] Compared with embodiment 2, this embodiment adds a step after step ① and before step ②: planarizing the back side of the p-type silicon substrate. In this embodiment, the step of "planarizing the back of the p-type silicon substrate" is added, the purpose of which is to process the pyramid-shaped back into a slightly smooth back, that is, to smooth the top tip of the pyramid, so that the pyramid The apex-like structure of the structure and the sharp-edged horn-like structure at the bottom of the valley become smooth, and at the same time, the surface of the pyramid changes from rough to relatively smooth. After planarizing the back of the p-type silicon substrate, it should be ensured that a natural local contact can still be formed after the subsequent formation of the back passivation layer, which facilitates the subsequent preparation of the back electrode through printing and sintering processes.

[0056] In this embodiment, the backside of the p-type silicon substr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a p-type silicon solar cell and a preparing method thereof. The p-type silicon solar cell comprises a p-type silicon substrate. The front surface of the p-type silicon solar cell is provided with an n<+> doped layer and a reflection reducing layer. Front anodes which penetrate the reflection reducing layer are manufactured. The front anodes are connected with the n<+> doped layer. The back surface of the p-type silicon substrate is provided with a back passivation layer. The back passivation layer comprises a film layer which is made of a ferroelectric film material or a doped ferroelectric film material. A back electrode is manufactured on the back passivation layer through a printing process and a sintering process. According to the p-type silicon solar cell, the ferroelectric film material is used as the main material of the back passivation layer of the cell, thereby greatly improving the open circuit voltage and shortcircuit current of the cell and improving conversion efficiency of the cell.

Description

technical field [0001] The invention relates to the technical field of solar cells, in particular to a p-type silicon solar cell and a preparation method thereof. Background technique [0002] The surface defects of crystalline silicon solar cells have a great influence on the performance of the cells. The open circuit voltage (V oc ), short circuit current (J sc ), fill factor (FF) and other main parameters largely depend on the level of surface defect density. The recombination loss of photogenerated carriers is one of the main ways of solar cell efficiency loss, and the surface recombination is the most important recombination loss. Reducing the surface defect density and reducing surface recombination are important means to improve the energy conversion efficiency of silicon solar cells. Passivation can effectively reduce the recombination of carriers, thereby improving the conversion efficiency of solar cells. Passivation usually has two methods: chemical passivatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01L31/18H01L31/0216H01L31/068
CPCH01L31/02167H01L31/02168H01L31/068H01L31/1804H01L31/1868Y02E10/547Y02P70/50
Inventor 麦耀华陈兵兵陈剑辉许颖代秀红刘保亭
Owner HEBEI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com