Manufacturing method of light-permeable ceramic colored glaze
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production method and ceramic color technology, applied in the field of ceramic technology, can solve the problems of not conforming to the production concept of low carbon and environmental protection, time-consuming and labor-consuming color glaze process, unstable quality of colored glaze, etc., to achieve uniform and stable glaze slurry, The effect of reducing energy consumption and reducing firing time
Inactive Publication Date: 2016-05-11
FUJIAN WANQI SANDT CERAMICS CO LTD
View PDF5 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Traditional ceramic products have poor light transmission, which affects their further popularization in architectural decoration and other fields; at the same time, in the colored glaze technology of traditional light-transmitting ceramics, the process is complicated and the quality of colored glaze is unstable; Time-consuming and labor-intensive, does not conform to the production concept of low-carbon and environmental protection
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0039] Below in conjunction with the examples, the present invention is further described, the following examples are illustrative, not limiting, and the protection scope of the present invention cannot be limited by the following examples.
[0040] A method for manufacturing light-transmitting ceramic color glaze, characterized in that: comprising:
[0041] Step A: preparation of the ceramic body;
[0042] Step B: applying colored glaze on the surface of the ceramic body prepared in step A;
[0043] Described step A comprises the following steps:
[0044] Step A01: batching; mixing the raw materials in proportion, adding special additives including reinforcing agents and water reducers to the raw materials as required;
[0045] Step A02: ball milling; the mixed raw materials are ground by wet ball milling;
[0046] Step A03: sieving to remove iron; the raw material after grinding is sieved to remove iron and spray-dried to obtain powder;
[0047] Step A04: squeezing mud; ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a manufacturing method of light-permeable ceramic colored glaze. The method comprises the steps that A, a ceramic body is prepared; B, the surface of the ceramic body prepared in the step A is colored and glazed. The step A comprises the following substeps of ingredient preparation, ball milling, sieving for iron removal, clay pressing, clay preparation, aging, refining and wet blank forming, drying, washing and renovation, biscuit firing at the temperature of 750-850 DEG C, fine trimming, dry blank forming, and the ceramic body is obtained. The step B comprises the following substeps that 1, raw materials are treated, wherein 65-75% by weight of volcano slime and 25-35% by weight of albite are used as base materials, the base materials and water are poured into a ball mill to be subjected to ball milling for 2+ / -0.1 h, sieving is carried out, and glaze slip is obtained; 2, the ceramic body is evenly coated with the glaze slip in a glaze soaking or glaze spraying or coating mode, and then the ceramic body is dried; 3, the ceramic body coated with the glaze slip is placed into a kiln to be heated to 1280-1350 DEG C, the temperature is kept, and firing is carried out for 0.5-1 h, so that the reddish brown light-permeable ceramic colored glaze is obtained.
Description
technical field [0001] The invention relates to the field of ceramic technology, in particular to a manufacturing process of light-transmitting ceramic color glaze. Background technique [0002] my country has a very long history of ceramics, and now it has been used in many fields, especially in daily necessities, ceramic products can be seen everywhere, and its preparation technology has been widely used all over the world. It has become an indispensable part of people's daily life. All kinds of tableware, tea sets, and various sanitary ware can be seen everywhere. Most of these ceramics are beautiful and generous, with various shapes. Ceramics are deeply loved by consumers; [0003] Traditional ceramic products have poor light transmission, which affects their further popularization in architectural decoration and other fields; at the same time, in the colored glaze technology of traditional light-transmitting ceramics, the process is complicated and the quality of colored...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.