Normal temperature desulfurization and arsenic removal agent and preparation method thereof

A technology of desulfurization and dearsenic, by weight, applied in separation methods, chemical instruments and methods, refining hydrocarbon oil, etc. The effect of increasing the chance of interface contact

Active Publication Date: 2019-01-25
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is the problem of high bulk density and low sulfur capacity and arsenic capacity of the desulfurization and arsenic removal agent in the prior art, and a new desulfurization and arsenic removal agent and its preparation method are provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Normal temperature desulfurization and arsenic removal agent and preparation method thereof
  • Normal temperature desulfurization and arsenic removal agent and preparation method thereof
  • Normal temperature desulfurization and arsenic removal agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 30 kilograms of copper nitrate, 40 kilograms of zinc nitrate, 10 kilograms of aluminum nitrate, 1.0 kilogram of cerium nitrate and 500 kilograms of water are mixed and stirred to obtain a metal salt solution, and 30 kilograms of sodium carbonate and 550 kilograms of water are mixed to obtain a sodium carbonate solution. Mix the sodium solution and metal salt solution evenly, react at 70°C for 1 hour, wash and dry the precipitate, then add 6 kg of alumina and 1 kg of graphite, mix and roll, then add 30% by weight of water, granulate, and roast at 270°C After 2 hours, it was pressed into tablets and formed, and the composition of the obtained sample is shown in Table 1.

Embodiment 2

[0036] 30 kilograms of copper nitrate, 40 kilograms of zinc nitrate, 10 kilograms of aluminum nitrate, 0.02 kilogram of cerium nitrate and 500 kilograms of water are mixed and stirred to obtain a metal salt solution, and 30 kilograms of sodium carbonate and 550 kilograms of water are mixed to obtain a sodium carbonate solution. Mix the sodium solution and metal salt solution evenly, react at 70°C for 1 hour, wash and dry the precipitate, then add 6 kg of alumina and 1 kg of graphite, mix and roll, then add 30% by weight of water, granulate, and roast at 270°C After 2 hours, it was pressed into tablets and formed, and the composition of the obtained sample is shown in Table 1.

Embodiment 3

[0038] 30 kilograms of copper nitrate, 40 kilograms of zinc nitrate, 10 kilograms of aluminum nitrate, 0.1 kilogram of cerium nitrate and 500 kilograms of water are mixed and stirred to obtain a metal salt solution, and 30 kilograms of sodium carbonate and 550 kilograms of water are mixed to obtain a sodium carbonate solution. Mix the sodium solution and metal salt solution evenly, react at 70°C for 1 hour, wash and dry the precipitate, then add 6 kg of alumina and 1 kg of graphite, mix and roll, then add 30% by weight of water, granulate, and roast at 270°C After 2 hours, it was pressed into tablets and formed, and the composition of the obtained sample is shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a normal-temperature desulfurization dearsenic agent and a preparation method thereof. The invention mainly aims at solving problems of high bulk density, low sulfur capacity and low arsenic capacity of desulfurization dearsenic agents in prior arts. The desulfurization dearsenic agent provided by the invention comprises the following components, by weight: (a) 1-10 parts of aurichalcite, (10) 10-50 parts of copper oxide, (c) 10-60 parts of zinc oxide, and (d) 0.01-3 parts of rare earth metal R. With the above technical scheme, the problem is well solved. The method can be applied in the purification of natural gas, synthetic gas, light gas-liquid hydrocarbons, and the like.

Description

technical field [0001] The invention relates to a normal temperature desulfurization and arsenic removal agent and a preparation method thereof. Background technique [0002] Impurities such as sulfur and arsenic are widely present in raw materials such as natural gas, synthesis gas, coal gas, light gas and liquid hydrocarbons. The existence of these impurities will lead to poisoning and deactivation of many catalysts, greatly shorten the life of catalysts, and even cause the catalytic reaction to fail to proceed normally. ; In addition, the sulfur and arsenic impurities that have not been removed will enter the downstream synthetic products as the production progresses, which will bring a series of environmental and health problems. Therefore, efficient and high-precision removal of impurities such as sulfur and arsenic is of great significance for protecting the main catalyst of downstream devices and improving the quality of downstream products at the same time. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/06B01J20/30B01D53/02C10G25/00
Inventor 贾银娟王灿杨贺勤刘志成高焕新
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com