A wooden furniture, white technology, applied in the field of white primer, can solve the problem of high price, achieve the effect of low cost, high hardness and saving painting cost

Inactive Publication Date: 2016-05-18
彭绍宾
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the actual production process, the water-based wood white primer should have good construction performance, high hardness, easy grinding, and good filling performance. However, the white primer that meets these conditions usually uses titanium dioxide as a filler, and its price is relatively high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] White primer for wooden furniture, by weight percentage, including the following components: water-based acrylic emulsion 38-41%, filler 53-56%, auxiliary agent 1.7%, film-forming auxiliary agent 4%, thickener 0.3 %, the filler is composed of titanium dioxide, heavy calcium, and talcum powder, and the three percentages by weight of the white primer raw materials are respectively: titanium dioxide 4.5-5.5%, heavy calcium 38.5-40%, and talcum powder 9-10.5%. The white primer formulation for wooden furniture provided by the invention uses titanium dioxide, talcum powder and heavy calcium as fillers in an appropriate ratio, and properly reduces the cost of the white primer without affecting the performance of the primer.

[0020] In this embodiment, the auxiliary agent is one or a combination of defoamers, dispersants, wetting agents, anti-mold and bactericides; the water-based acrylic emulsion has a core-shell structure and a predetermined glass transition temperature. The...

Embodiment 2

[0022] The difference between this embodiment and embodiment 1 is:

[0023] White primer for wooden furniture, by weight percentage, includes the following components: water-based acrylic emulsion 39%, titanium dioxide 5%, heavy calcium 40%, talcum powder 10%, film-forming aid 4%, thickener 0.3% agent, 0.2% defoamer, 1.2% dispersant, 0.2% wetting agent, 0.1% anti-mold fungicide.

[0024] Its preparation method is to add water-based acrylic emulsion, titanium dioxide, heavy calcium, talc powder, film-forming aids, defoamers, dispersants, and wetting agents into the beaker in sequence according to the formula quantity, and the speed is 2000r / min Stir for 30 minutes under the same conditions, then add anti-mold and fungicide, thickener, and stir evenly.

Embodiment 3

[0026] The difference between this embodiment and embodiment 2 is: the white primer for wooden furniture, by weight percentage, comprises the following components: water-based acrylic emulsion 40%, titanium dioxide 5%, heavy calcium 39%, talcum powder 10% %, film-forming aid 4%, thickener 0.3%, defoamer 0.2%, dispersant 1%, wetting agent 0.2%, anti-mold fungicide 0.3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a white priming paint used for wood furniture. The white priming paint comprises the following components by weight percentage: 38-41% of an aqueous acrylic acid emulsion, 53-56% of a filling material, 1.7% of an auxiliary agent, 4% of a film forming auxiliary agent, and 0.3% of a thickening agent. The filling material is composed of 4.5-5.5% of titanium dioxide, 38.5-40% of heavy calcium and 9-10.5% of powdered steatile with weight percentage in the white priming paint raw material. The white priming paint has excellent polishing property and filling property; has advantages of high hardness and good sealing performance, can effectively seal tannic acid in timber, can solve the problems of wood swelling and fiberboard swelling, can simplify the construction operation, saves coating cost; and employs an acrylic acid emulsion with low cost, wherein titanium dioxide, powdered steatile and heavy calcium can be the filling materials with a proper ratio, and cost of the white priming paint is reduced under prerequisite that the priming paint performance is not influenced, and cost of the white priming paint is lower than that of the other priming paints.

Description

technical field [0001] The invention relates to the technical field of paint for furniture, in particular to a white primer for wooden furniture. Background technique [0002] With people's increasing requirements for environmental protection and health, as well as the continuous improvement and strengthening of domestic and foreign environmental protection laws and regulations, water-based wood coatings have attracted more and more attention. Water-based wood coatings are a type of coating with water as the dispersion medium. They have the advantages of non-combustibility, non-toxicity, no pollution to the environment, and energy saving. The market prospect is broad. [0003] In the actual production process, the water-based wood white primer should have good construction performance, high hardness, easy grinding, and good filling performance. However, the white primer that meets these conditions usually uses titanium dioxide as a filler, and its price is relatively high. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D7/12
Inventor 彭绍宾
Owner 彭绍宾
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com