High-pressure braided-hose inner-layer rubber

A braided hose and rubber technology, which is applied in the field of high-pressure braided hose inner layer rubber, can solve problems such as pipe catching and constricting, and achieve the effects of cost control, energy consumption reduction, and excellent solvent resistance

Inactive Publication Date: 2016-05-25
LUOHE BONWELL RUBBER
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the present invention, the above-mentioned three kinds of polymer materials are compounded and used together to refine the inner layer rubber of the high-pressure braided hose. By using the NBR / PVC rubber-plastic alloy that has been compounded and modified for mixing, it can solve the problem of high-pressure steel wire braiding. During the production process of rubber hose, there are quality problems such as rushing and tightening the hose, solving the melting problem of PVC and nitrile rubber, improving the solvent resistance of hydraulic hoses, and effectively controlling the cost of raw materials for hoses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The formula of the high-pressure braided hose inner layer glue described in this embodiment includes the raw materials in parts by mass:

[0032] Nitrile rubber 2870100

[0033] NBR / PVC rubber-plastic alloy 509080

[0034] SBR 150250

[0035] Active Zinc Oxide 9

[0036] Stearic acid 2

[0037] Light magnesium oxide 12

[0038] Antiaging agent 4010NA3

[0039] Solid Coumarone 18

[0040] Carbon black N550230

[0041] Silica 23

[0042] Light calcium carbonate 46

[0043] Dioctyl 27

[0044] Adhesive RC12

[0045] Accelerator CZ2

[0046] Sulfur powder5.

[0047] The refining method of the high-pressure braided hose inner layer rubber described in this embodiment is as follows:

[0048] A. Weighing Weigh each compounding substance according to the formula;

[0049] B. During the internal mixing production process, use a kneader for internal mixing. Add the weighed nitrile rubber, rubber-plastic alloy, and styrene-butadiene rubber directly into the internal ...

Embodiment 2

[0053] The formula of the high-pressure braided hose inner layer glue described in this embodiment includes the raw materials in parts by mass:

[0054] Nitrile rubber 2870100

[0055] NBR / PVC rubber-plastic alloy 5090100

[0056] SBR 150250

[0057] Other material consumption is identical with the consumption in embodiment 1.

[0058] The refining method of the inner layer rubber of the high-pressure braided hose described in the following examples is the same as that in Example 1.

Embodiment 3

[0060] The formula of the high-pressure braided hose inner layer glue described in this embodiment includes the raw materials in parts by mass:

[0061] Nitrile rubber 28706.5Kg100

[0062] NBR / PVC rubber-plastic alloy 5090120

[0063] SBR 150250

[0064] Other material consumption is identical with the consumption in embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strength at breakaaaaaaaaaa
Permanent deformationaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to high-pressure braided-hose inner-layer rubber. As compositely-modified NBR / PVC rubber and plastic alloy is mixed, the quality problems of hose shifting, hose pinching and the like in the production process of a high-pressure steel-wire braided rubber hose can be well solved, the fusing problem of PVC and nitrile butadiene rubber is solved, the solvent resistance of a hydraulic rubber hose is improved, and the cost of a raw material of the rubber hose can be effectively controlled. The made high-pressure braided-hose inner-layer rubber has excellent oil resistance and excellent solvent resistance; meanwhile, processing difficulty can be greatly lowered, the stability of the quality of a product can be improved, and the cost of the raw material of the rubber is further optimized.

Description

technical field [0001] The invention relates to a rubber formula, in particular to an inner layer rubber of a high-pressure braided hose. technical background [0002] Nitrile rubber is a kind of oil-resistant rubber with strong polarity. Polyvinyl chloride has excellent solvent resistance and aging resistance. At the same time, it can effectively improve the Green hardness of the mixed rubber. Filling performance can reduce processing difficulty and production cost, and improve the bonding strength between inner rubber and steel wire. Contents of the invention [0003] In the present invention, the above-mentioned three kinds of polymer materials are compounded and used together to refine the inner layer rubber of the high-pressure braided hose. By using the NBR / PVC rubber-plastic alloy that has been compounded and modified for mixing, it can solve the problem of high-pressure steel wire braiding. In the production process of rubber hose, there are quality problems such ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L27/06C08L9/06C08L45/02C08K13/02C08K3/22C08K5/09C08K3/36C08K3/04
CPCC08L9/02C08L27/06C08L2203/18C08L2205/02C08L2205/035C08L9/06C08L45/02C08K13/02C08K2003/2296C08K5/09C08K3/36C08K3/04
Inventor 田海涛肖鹏涛林春喜
Owner LUOHE BONWELL RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products