Environmental protection luminous paint and production method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of luminous paint and production method, applied in the field of paint, can solve the problems of gun body collision, difficulty in coating, reducing wear-resisting effect, etc., and achieve the effects of high strength, good sealing and good bonding
Inactive Publication Date: 2016-06-01
裴振
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The coating protects the base material, but due to the technical reasons of the conventional thermal spraying technology, it is difficult to form a completely dense coating. The existence of coating pores not only reduces the wear resistance effect, but also is a fatal defect for corrosion protection.
But the current paint cannot emit light, in the case of bad light, there is no light source, causing us to collide with the gun body
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0008] An environment-friendly luminescent paint and its production method, which are configured by the following weights, including 18kg of varnish, 13kg of luminescent pigment, 8kg of epoxy ester, 13kg of talcum powder, 8kg of dioctyl phthalate, 8kg of polyacrylic acid, and 8kg of hydroxycellulose solution , white mud 8kg, cement 18kg, water 900kg.
[0009] The preparation method of the present invention is specifically as follows: First, weigh the raw materials according to the raw materials of each component, then pour water into the reaction kettle, and when heated to 30-40°C, add varnish, luminescent pigment, epoxy ester, talcum powder, orthophthalene Stir dioctyl formate, polyacrylic acid, hydroxycellulose solution, white clay, and cement, then raise the temperature to 90°C, and keep it warm for 30 minutes to obtain the finished product.
Embodiment 2
[0011] Embodiment two is basically the same as implementation one, except that the following weight configurations are 15kg of varnish, 10kg of luminescent pigment, 5kg of epoxy ester, 10kg of talcum powder, 5kg of dioctyl phthalate, 5kg of polyacrylic acid, and hydroxycellulose Solution 5kg, lime mud 5kg, cement 15kg, water 800kg.
Embodiment 3
[0013] Embodiment three is basically the same as implementation one, except that the following weight configurations are 20kg of varnish, 15kg of luminous pigment, 10kg of epoxy ester, 15kg of talcum powder, 10kg of dioctyl phthalate, 10kg of polyacrylic acid, and hydroxycellulose Solution 10kg, lime mud 10kg, cement 20kg, water 1000kg.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to an environmental protectionluminous paint and a production method thereof. The environmental protectionluminous paint comprises the following components by weight: 15-20 kg of a varnish, 10-15 kg of a luminous pigment, 5-10 kg of epoxy ester, 10-15 kg of powdered steatile, 5-10 kg of dioctyl phthalate, 5-10 kg of polyacrylic acid, 5-10 kg of a hydroxy cellulose solution, 5-10 kg of white mud, 15-20 kg of cement, and 800-1000 kg of water. The production method comprises the following steps: weighing the raw materials according to proportion, then dumping water in a reaction vessel, heating the raw materials to the temperature of 30-40 DEG C, adding the varnish, the luminous pigment, epoxy ester, powdered steatile, dioctyl phthalate, polyacrylic acid, the hydroxy cellulose solution, the white mud and the cement, stirring the above materials, heating the raw materials to the temperature of 90 DEG C, and insulating the raw materials for 30 minutes to obtain the product. The environmental protectionluminous paint has the advantages of no toxicity, tastelessness and no corrosion, no pollution on environment, good sealing performance, high intensity, and no cracking.
Description
technical field [0001] The invention relates to the field of coatings, in particular to a high-temperature-resistant coating suitable for buildings and a preparation method thereof. Background technique [0002] The coating protects the base material, but due to the technical reasons of the conventional thermal spraying technology, it is difficult to form a completely dense coating. The existence of coating pores not only reduces the wear resistance effect, but also is a fatal defect for corrosion protection. . But the current paint cannot emit light. In the case of bad light, there is no light source, which causes us to collide with the gun body. Contents of the invention [0003] The object of the present invention is to provide an environmentally friendly luminous coating and a production method that has a closed-cell microporous structure made of a non-toxic and tasteless thermal insulation material with good thermal insulation performance, low thermal conductivity, s...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More