Granular cryolite and preparation method capable of regulating and controlling molecular ratio thereof

A cryolite and granular technology, which is applied in the field of granular cryolite and its preparation, can solve the problems of brittle ice and increased cost, and achieve the effects of stable quality, easy control and high hardness.

Inactive Publication Date: 2016-06-08
HUNAN NONFERROUS FLUORIDE CHEM
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The cryolite produced by the disclosed technical schemes such as CN1259242C, CN1043033C, CN1225897A, CN1300879A, CN1260130C are all powdery cryolite, to produce granular cryolite must carry out post-pressing, not only cost rises, and the granular ice that dry product is pressed out is easy Another technical defect in the production of cryolite by the above scheme is that the molecular ratio cannot be adjusted in the production process, some can only produce cryolite with high molecular ratio, and some can only produce cryolite with ordinary molecular ratio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

reference example 1

[0034] The preparation method of the seed solution obtained by the preliminary ammoniation of sodium fluorosilicate: mix 600kg of sodium fluorosilicate with 14m 3 Cryolite mother liquor (the main component concentration is: F: 8.4g / L, Na: 4.1g / L, NH 4 + : 22.4g / L, specific gravity 1.05), stir the ingredients in the reaction tank, add ammonia water until the pH value is 7, and aging for 40min, serve.

[0035] Preparation method of sodium aluminate solution: prepare 4.4m 3 Sodium hydroxide solution with a mass concentration of 33.2wt%, steam heated to 110°C, add 3000kg aluminum hydroxide, stir and react until the solution is clear, to obtain sodium aluminate solution (wherein, the concentration of Al is 198.72g / L, the concentration of Na It is 218.96g / L, and the causticity ratio is 1.29).

reference example 2

[0037] Preparation method of sodium aluminate solution: prepare 4.4m 3 Sodium hydroxide solution with a mass concentration of 33.1wt%, steam heated to 115°C, add 3000kg aluminum hydroxide, stir and react until the solution is clear, to obtain sodium aluminate solution (wherein, the concentration of Al is 197.37g / L, the concentration of Na It is 212.98g / L, and the causticity ratio is 1.2).

reference example 3

[0039] Preparation method of sodium aluminate solution: prepare 4.4m 3 32.4wt% sodium hydroxide solution, steam heated to 120℃, add 3000kg aluminum hydroxide, stir and react until the solution is clear, to obtain sodium aluminate solution (wherein, the concentration of Al is 185.44g / L, and the concentration of Na is 196.88g / L, caustic ratio is 1.25).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses granular cryolite and a preparation method capable of regulating and controlling a molecular ratio thereof. The cryolite is mainly composed of, by mass, 52-55% of F, 12-15% of Al and 28-33% of Na according to a molecular ratio of 2.0-3.0, the cryolite is naturally granulated, and weight of the cryolite less than 1mm in grain diameter is less than or equal to 15%. The preparation method includes following steps: (1), adding sodium fluosilicate into cryolite mother liquid, adding ammonia water to enable pH value to be 8.0-9.5, and performing press filtering to obtain a sodium fluoride and ammonium fluoride mixed solution; (2), adding the sodium fluoride and ammonium fluoride mixed solution and a sodium aluminate solution into a synthesis tank to obtain cryolite slurry; (3), adding an aluminum-based compound into the cryolite slurry, and performing stirring reaction, solid-liquid separation and drying to obtain the granular cryolite. The granular cryolite is adjustable in the molecular ratio within a range of 2.0-3.0. The preparation method is simple, convenient and easy to operate, and the cryolite mother liquid is recyclable, low in energy consumption and low in pollution.

Description

Technical field [0001] The invention relates to a granular cryolite and a preparation method thereof, in particular to a granular cryolite and a preparation method capable of regulating its molecular ratio. Background technique [0002] The chemical name of cryolite is sodium fluoroaluminate, and the molecular formula is Na 3 AlF 6 . Cryolite is divided into natural and artificial. It is mainly used as a flux for electrolytic aluminum smelting, abrasion-resistant filler for rubber and grinding wheels, a brightener for enamel, and a flux for metals. The traditional process of sodium cryolite production is the fluoroaluminate soda method, and the emerging technologies include the clay brine method and the sodium fluorosilicate method. [0003] However, the sodium fluorosilicate method as an emerging process has certain drawbacks: in the process of producing cryolite with sodium fluorosilicate, the causticity ratio of sodium aluminate used cannot reach 1.0. If the cryolite mother liq...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01F7/54
CPCC01F7/54C01P2004/51
Inventor 王晓玲刘龙平陈华何志仁周伟梁星李文英
Owner HUNAN NONFERROUS FLUORIDE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products