Paper wood-plastic composite material, preparation process and application thereof

A wood-plastic material and plastic technology, which is used in buildings, building structures, floors, etc., can solve problems such as unfavorable use and low thermal deformation temperature, and achieve extended service life, low requirements for paper scraps, and reuse of resources. Effect

Inactive Publication Date: 2016-06-08
中山市易高达环保科技有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the existing technology, in order to save cost and energy, the PE plastic used is recycled PE plastic, but the heat distortion temperature is low, which is not conducive to the use at higher temperatures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The present invention also provides a preparation process for the aforementioned paper-wood-plastic material, including:

[0037] A. Mix wood flour, waste paper scraps, recycled PP plastics, recycled PE plastics, fillers, and coupling agents, stir and heat to 90°C, add antioxidants and lubricants, stir and heat to 100°C;

[0038] B. Cold mixing for 5-10 minutes to remove moisture;

[0039] C. After cooling, the paper-wood-plastic material can be obtained.

[0040] The present invention also provides the application of the above-mentioned paper-wood-plastic material, which is used to prepare the paper-wood-plastic floor: the above-mentioned paper-wood-plastic material is transferred to a granulator for granulation, and then passed through an extruder equipped with a floor mould. Out of the machine, it is extruded into paper wood-plastic floor profiles.

[0041] As preferably, 40% of wood powder; 15% of waste paper; 15% of recycled PP plastic; 20% of recycled PE plastic...

Embodiment 1

[0044] 40kg of wood powder; 15kg of waste paper; 15kg of recycled PP plastic; 20kg of recycled PE plastic; 1.3kg of white carbon black; 3.9kg of calcium carbonate; 1.3kg of talcum powder; kg; add it to the hot mixing pot of the high-speed mixer, stir at high speed to make the material heat up to 90°C through self-friction, then add 0.167kg of antioxidant (1010), 0.333kg of antioxidant (168); 1.35kg of polyethylene wax, Stearic acid 0.45kg; then continue to stir at high speed and heat to 100°C; put the mixture into a cold mixing pot, and cold mix for 5 minutes to remove moisture; cool to room temperature to obtain the paper wood plastic material.

[0045] The paper wood plastic material is transferred to a granulator for granulation to make granules with a particle size of 5-8 mm, and then extruded into paper wood plastic floor profiles through an extruder equipped with a floor mold. The specifications of the floor profile can be made into various specifications according to th...

Embodiment 2

[0047] Wood powder 37kg; waste paper scraps 20kg; recycled PP plastic 17kg; recycled PE plastic 15kg; white carbon black 1.5kg; calcium carbonate 4.5kg; talcum powder 1.5kg; Add 0.4kg of silane coupling agent and 0.6kg of silane coupling agent; add it into the hot mixing pot of high-speed mixer, stir at high speed to make the material heat up to 90°C through self-friction, then add 0.133kg of antioxidant (1010), antioxidant (168) 0.267kg; polyethylene wax 0.6kg, maleic anhydride grafted polyethylene wax 0.675kg; stearic acid 0.225kg, calcium stearate 0.2kg; then continue high-speed stirring and heating to 100°C; put the mixture into a cold mixing pot, Cold mixing for 8 minutes to remove water vapor; cooling to room temperature to obtain paper wood plastic material.

[0048] The paper wood plastic material is transferred to a granulator for granulation to make granules with a particle size of 5-8 mm, and then extruded into paper wood plastic floor profiles through an extruder e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The present invention provides a paper wood-plastic composite material, a preparation process and application thereof. The material includes wood flour, paper scrap, recycled PP plastics, recycled PE plastics, an antioxidant, a filler, a lubricant and a coupling agent. The preparation process of the present invention includes the steps of: mixing wood flour, paper scrap, recycled PP plastics, recycled PE plastics, the filler and the coupling agent; stirring and heating to 90 DEG C; adding the antioxidant and lubricant, stirring and heating to 100 DGE C; conducting cold mixing for 5-10 min; and cooling to obtain the paper wood-plastic composite material. The added paper scrap is from wastepaper with low quality requirements, so as to eliminate the sorting process of the waste paper products and save energy.

Description

technical field [0001] The invention relates to the field of material preparation, in particular to a paper-wood-plastic material, its preparation process and its application. Background technique [0002] Wood-plastic material is a composite material filled with thermoplastics with wood powder, wood fiber or other plant fibers. [0003] Most of the wood-plastic materials currently used outdoors are made of PE plastic and wood powder as raw materials. [0004] In the prior art, in order to save cost and energy, the PE plastic used is recycled PE plastic, but the heat distortion temperature is low, which is not conducive to the use at a higher temperature. Contents of the invention [0005] In view of this, the present invention provides a paper-wood-plastic material, its preparation process and its application. By adjusting the formula, PP plastic and paper scraps are added, and the heat distortion temperature increases through the addition of paper scraps. At the same ti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L1/02C08L23/12C08L23/06E04F15/10
CPCC08L97/02C08L2201/08C08L2205/035E04F15/102C08L1/02C08L23/12C08L23/06
Inventor 赖志华陈再顺刘志鹏
Owner 中山市易高达环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap