Antibiosis oxidized graphene heat dissipation coating for artificial turf and preparing method thereof

A technology for heat-dissipating paint and artificial turf, which is applied to coatings and other directions, can solve the problems of poor heat-dissipation performance and high preparation cost, and achieve the effects of improving compatibility, simple and easy operation of preparation route, and high heat-dissipation efficiency.

Active Publication Date: 2016-06-08
WUXI GREEN LAWN CO LTD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Artificial turf adopts the principle of bionics, has good elasticity and sports performance, and can effectively reduce sports injuries, but there is also a serious problem: the temperature of artificial turf is much higher than that of natural turf, and its heat dissipation performance is poor
Graphene material, which has attracted much attention in recent years, has a large specific surface area and outstanding thermal conductivity, and can be used as a thermal conductivity material, but its preparation cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibiosis oxidized graphene heat dissipation coating for artificial turf and preparing method thereof
  • Antibiosis oxidized graphene heat dissipation coating for artificial turf and preparing method thereof
  • Antibiosis oxidized graphene heat dissipation coating for artificial turf and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An antibacterial graphene oxide heat-dissipating coating for artificial turf, the raw materials contained in the heat-dissipating coating and the parts by weight of each raw material are:

[0028]

[0029] The preparation method of described light-cured graphene oxide is:

[0030] Graphene oxide is dissolved in toluene, while adding consumption is the active hydroxyethyl methacrylate of graphene oxide quality 6 times, and add catalyst methanesulfonic acid (1% of hydroxyethyl methacrylate molar number), and The polymerization inhibitor p-hydroxyanisole (0.5% of the molar number of hydroxyethyl methacrylate) was reacted at 60° C. for 48 hours; after the reaction was completed, the photocured graphene oxide was obtained by centrifuging, washing and drying. The transmission electron microscope picture of the product is as follows figure 1 Shown; the Raman spectrum is shown in figure 2 shown.

[0031] Depend on figure 1 It can be seen that the color of photocured gra...

Embodiment 2

[0034] An antibacterial graphene oxide heat-dissipating coating for artificial turf, the raw materials contained in the heat-dissipating coating and the parts by weight of each raw material are:

[0035]

[0036]

[0037] The preparation method of described light-cured graphene oxide is:

[0038] Graphene oxide is dissolved in ethyl acetate, while adding consumption is the glycidyl methacrylate of graphene oxide quality 4 times, and add catalyst tetrabutyl ammonium bromide (0.5% of glycidyl methacrylate molar number) ) and a polymerization inhibitor hydroquinone (0.1% of the molar number of glycidyl methacrylate), reacted for 24 hours at 100° C.; after the reaction was completed, centrifuged, washed, and dried to obtain the photocured graphene oxide.

[0039] 1 part of photocurable graphene oxide, 80 parts of castor oil-based acrylate oligomer, 10 parts of N-allylpyridine triacrylate, 2 parts of 1-hydroxy-cyclohexyl phenone, and 3 parts of mesoporous zirconium phosphate ...

Embodiment 3

[0041] An antibacterial graphene oxide heat-dissipating coating for artificial turf, the raw materials contained in the heat-dissipating coating and the parts by weight of each raw material are:

[0042]

[0043] The preparation method of described light-cured graphene oxide is:

[0044] Graphene oxide is dissolved in dioxane, while adding the amount of pentaerythritol triacrylate that is 2 times the quality of graphene oxide, and adding catalyst triphenylphosphine (2% of the pentaerythritol triacrylate double bond molar number) and barrier Polymerizing agent hydroquinone (0.5% of pentaerythritol triacrylate double bond mole number), react at 130° C. for 12 hours; after the reaction is completed, centrifuge, wash and dry to obtain the photocured graphene oxide.

[0045] In the Blending at a temperature of 35° C., stirring for 3 hours at a rotational speed of 1000 rpm, and ultrasonically dispersing for 30 minutes to obtain the antibacterial graphene oxide heat-dissipating coa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antibiosis oxidized graphene heat dissipation coating for artificial turf and a preparing method thereof. The coating comprises, by weight, 1-10 parts of light-cured oxidized graphene, 50-80 parts of plant-based light-cured resin, 10-30 parts of antibacterial activated monomer, 1-4 parts of photoinitiator and 1-3 parts of antibiosis assistant. The coating can effectively solve the problem that the heat dissipation of artificial turf is hard, and has the advantages that heat dissipation property and antibacterial property are excellent, cost is low, environment friendliness is realized, and the preparing process is simple.

Description

technical field [0001] The invention relates to the technical field of ultraviolet curing heat dissipation coatings, in particular to an antibacterial heat dissipation coating made of graphene oxide basic raw materials and its application on artificial turf. Background technique [0002] In recent years, with the improvement of people's living standards, the use of artificial turf has become more and more extensive. Artificial turf can be used in sports projects, such as football fields, tennis courts, golf courses, etc., and can also be used in environmental and landscaping, such as airports, apartment greening, public buildings, commercial areas, and entertainment venues. Artificial turf adopts the principle of bionics, has good elasticity and sports performance, and can effectively reduce sports injuries, but there is also a serious problem: the temperature of artificial turf is much higher than that of natural turf, and its heat dissipation performance is poor. This is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D7/12
CPCC09D4/00C09D7/62C08F220/18C08F220/40C08F222/26
Inventor 袁成程亚权
Owner WUXI GREEN LAWN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com