A kind of preparation technology of epoxy resin polymer grouting liquid

A technology of epoxy resin and preparation process, which is applied in fiber treatment, textiles and papermaking, fiber types, etc. It can solve the problems of high volatility and non-environmental protection, and achieve the effects of improved adhesion, fast strength development, and good pourability

Active Publication Date: 2019-02-05
中水华通工程有限公司 +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The other is to use polyurethane epoxy and add a large amount of furfural and acetone diluent. These two methods can form a grouting material with certain elasticity, but there are disadvantages such as high volatility and not environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of preparation technology of epoxy resin polymer grouting fluid, comprises the following steps:

[0023] (1), take epoxy resin (epoxy equivalent of 220-240g / mol) into the reaction kettle, stir and heat up to 85°C, then dropwise add a mixture of acrylic acid, triethylbenzyl ammonium chloride and hydroquinone solution (the mass ratio of acrylic acid, triethylbenzyl ammonium chloride and hydroquinone in the mixed solution is 75:2:1), stirred and reacted for 4 hours (the mass ratio of epoxy resin to the mixed solution was 8:5 ), to obtain preform A; take polypropylene oxide diol and add it to the reactor, heat it to 130°C while stirring and vacuuming it and keep it warm for 1h; then cool to 80°C, add toluene diisocyanate dropwise to the reactor while stirring Insulation, after the dropwise addition, the temperature was gradually raised to 90°C and kept for 2 hours, cooled and discharged to obtain preform B; preform A and preform B were added to the reactor at a ratio...

Embodiment 2

[0031] A kind of preparation technology of epoxy resin polymer grouting fluid, comprises the following steps:

[0032] (1), take epoxy resin (epoxy equivalent of 220-240g / mol) into the reaction kettle, stir and heat up to 85°C, then dropwise add a mixture of acrylic acid, triethylbenzyl ammonium chloride and hydroquinone solution (the mass ratio of acrylic acid, triethylbenzyl ammonium chloride and hydroquinone in the mixed solution is 75:2:1), stirred and reacted for 5 hours (the mass ratio of epoxy resin to the mixed solution was 8:5 ), to obtain preform A; take polypropylene oxide diol and add it to the reactor, heat it to 130°C while stirring and vacuuming it and keep it warm for 1h; then cool to 80°C, add toluene diisocyanate dropwise to the reactor while stirring Insulation, after the dropwise addition, the temperature was gradually raised to 90°C and kept for 2 hours, cooled and discharged to obtain preform B; preform A and preform B were added to the reactor at a ratio...

Embodiment 3

[0040] A kind of preparation technology of epoxy resin polymer grouting fluid, comprises the following steps:

[0041] (1), take epoxy resin (epoxy equivalent of 220-240g / mol) into the reaction kettle, stir and heat up to 85°C, then dropwise add a mixture of acrylic acid, triethylbenzyl ammonium chloride and hydroquinone solution (the mass ratio of acrylic acid, triethylbenzyl ammonium chloride and hydroquinone in the mixed solution is 75:2:1), stirred and reacted for 4 hours (the mass ratio of epoxy resin to the mixed solution was 8:5 ), to obtain preform A; take polypropylene oxide diol and add it to the reactor, heat it to 130°C while stirring and vacuuming it and keep it warm for 1h; then cool to 80°C, add toluene diisocyanate dropwise to the reactor while stirring Insulation, after the dropwise addition, the temperature was gradually raised to 90°C and kept for 2 hours, cooled and discharged to obtain preform B; preform A and preform B were added to the reactor at a ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a technology for preparing epoxy-resin-polymer grouting liquid. The technology includes the following steps that 1, modified epoxy resin is prepared; 2, modified aramid fibers are prepared; 3, a reactive diluent is prepared; 4, a curing agent is prepared; 5, 40% of modified epoxy resin, 30% of bisphenol F-type epoxy resin, 5% of modified aramid fibers, 20% of reactive diluent and 5% of silane coupling agent are taken and mixed to obtain a component A; 6, 70%-80% of curing agent and 20%-30% of silane coupling agent are taken and mixed to obtain a component B; 7, during construction, the component A and the component B are taken in the weight proportion of (3-5):1, mixed, stirred to obtain the epoxy-resin-polymer grouting liquid. According to the technology, as all the components of the prepared epoxy-resin-polymer grouting liquid have the synergistic effect, coupling and solidifying of the epoxy resin can be promoted to form a space network of a stable structure, and therefore the epoxy-resin-polymer grouting liquid has the advantages of being high in strength, rapid in strength development, good in tenacity, high in binding power, good in durability and the like.

Description

technical field [0001] The invention relates to the technical field of polymer grouting fluid, in particular to a preparation process of epoxy resin polymer grouting fluid. Background technique [0002] Epoxy resin has the characteristics of strong adhesion, curing at room temperature, small curing shrinkage, high mechanical properties and excellent corrosion resistance. It can be used as adhesives, coatings, grouting materials, etc. field. At present, most of the commonly used epoxy grouting materials in China are high-strength grouting materials. The epoxy grouting materials of this system are mainly used for crack and bedrock reinforcement. They have been widely used in my country and solved many engineering problems. For the treatment of small (less than 0.5mm) deformation joints or movable joints, grouting materials with certain elasticity are required. Although polyurethane grouting materials are elastic materials, they have high viscosity and limited groutability. In...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L63/00C08L77/10C08G59/17C08G59/50C08G18/32C08G18/48C08G18/66C08G18/65C08G18/58C08G18/40C08G18/10D06M13/395D06M101/36
CPCC08G18/10C08G18/3206C08G18/4045C08G18/4825C08G18/581C08G18/6677C08G59/1466C08G59/1494C08G59/502C08G59/5073C08L63/00C08L2205/025C08L2205/035C08L2205/04C08L2205/16D06M13/395D06M2101/36C08L77/10C08G18/6517
Inventor 主义刘娉婷王坤鹏张贺强王晓辉范建存阎宪平王红恩赵绍飞师月朋李宽孟欣马艳民刘彦芳张海涛李会宾高宁波杨垒魏鹏郝宗才傅豪函
Owner 中水华通工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com