Method for preparing electric insulation anticorrosion powder coating
A powder coating and electrical insulation technology, which is applied in powder coatings, anti-corrosion coatings, epoxy resin coatings, etc., can solve the problems of powder coating usage restrictions, anti-corrosion and electrical insulation can not meet the needs at the same time, to achieve good electrical insulation , market application prospects, good corrosion resistance effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] A kind of preparation method of electrical insulation anticorrosion powder coating provided by the invention comprises the following steps:
[0025] (1) Preparation of raw materials: Weigh the raw materials according to the following proportions by weight: 600 parts of epoxy resin, 82 parts of curing agent, 10 parts of leveling agent, 8 parts of brightener, 5 parts of benzoin, 2 parts of catalyst, defoaming dispersion 10 parts of agent, 20 parts of pigment, 150 parts of mica powder, 63 parts of silicon micropowder, 50 parts of flame retardant, epoxy resin is a mixture of bisphenol F epoxy resin and novolac epoxy resin, and bisphenol F type The weight portion ratio of epoxy resin and novolac epoxy resin is 2: 1, and the weight portion of bisphenol F type epoxy resin is 400 parts, and the weight portion of novolac epoxy resin is 200 parts;
[0026] (2), pre-mixing: mix the above-mentioned raw materials evenly in the mixer;
[0027] (3) Melt extrusion mixing: Put the abov...
Embodiment 2
[0048] The difference between this example and Example 1 is that 2 parts by weight of modified chitin fibers are added between the second and third melting zones, and the modified chitin fibers are based on chitin fibers with a diameter of 1.5-2 μm. The wire is composed of nano-zirconium carbide fibers wrapped outside, and the diameter of the wrapped modified chitin fibers is 3-4 μm.
[0049] The cured coating of the electrical insulation anticorrosion powder coating obtained in the present embodiment is detected, and the following data are obtained:
[0050] Test items
[0051] From the above test results, it can be seen that the powder coating prepared in this embodiment has improved impact strength and salt spray test, and has a certain antibacterial effect.
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com