Ceramic product crack adhesive

A technology for ceramic products and adhesives, applied in the field of ceramic manufacturing, can solve the problems of generating harmful substances and affecting the safety of use, and achieve the effect of improving the safety of use, moderate viscosity and excellent high temperature resistance

Inactive Publication Date: 2016-07-20
ANHUI QINGHUAFANG FINE BONE PORCELAIN
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If glue is used for bonding, although the cracks can barely be repaired, there will be a smell of glue after being exposed to hot water or heating, and harmful substances may be generated, which will affect the safety of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] (1) Add 8 parts of guar gum and 5 parts of rice bran wax to 40 parts of water, heat to a boiling state and keep it warm for 15 minutes, then add 6 parts of butadiene rubber and 5 parts of alkyd resin, mix well, and then use microwave frequency 2450MHz, power 800W Under microwave treatment for 10min, the material I was obtained;

[0015] (2) Add 8 parts of hydroxyethyl cellulose, 3 parts of polyoxyethylene lauryl ether and 2 parts of sodium polyacrylate into 40 parts of water, mix well, soak for 30 minutes, and then stand at 0-5°C for 2 hours to obtain Material II;

[0016] (3) Add material II, 13 parts of flue ash, 10 parts of activated clay, 8 parts of nano-ceramic powder and 4-6 parts of vermiculite powder to material I, then heat to reflux state and keep warm for 10 minutes, then add 3 parts of asbestos wool, 2 parts of barium sulfate and 1 part of nano-alumina are mixed evenly, then added to a ball mill, and ball milled to a fineness of less than 50 μm.

Embodiment 2

[0018] (1) Add 10 parts of guar gum and 6 parts of rice bran wax to 50 parts of water, heat to a boiling state and keep it warm for 15 minutes, then add 8 parts of butadiene rubber and 3 parts of alkyd resin, mix well, and then use microwave frequency 2450MHz, power 800W Under microwave treatment for 10min, the material I was obtained;

[0019] (2) Add 10 parts of hydroxyethyl cellulose, 5 parts of lauryl polyoxyethylene ether and 3 parts of sodium polyacrylate into 50 parts of water, mix well, soak for 30 minutes, and then stand at 0-5°C for 2 hours to obtain Material II;

[0020] (3) Add material II, 15 parts of flue ash, 12 parts of activated clay, 6 parts of nano-ceramic powder and 5 parts of vermiculite powder to material I, then heat to reflux state for 10 minutes, then add 2 parts of asbestos wool, 1 part of Barium sulfate and 2 parts of nano-alumina are mixed evenly and added to a ball mill, and ball milled to a fineness of less than 50 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ceramic product crack adhesive, and relates to the technical field of ceramic manufacturing. The ceramic product crack adhesive is prepared from the following raw materials in parts by weight: 13-16 parts of flue ash, 10-15 parts of activated clay, 8-12 parts of hydroxyethyl cellulose, 6-10 parts of guar gum, 6-10 parts of nano ceramic powder, 5-8 parts of butadiene rubber, 5-8 parts of rice bran wax, 4-6 parts of vermiculite powder, 3-5 parts of alkyd resin, 3-5 parts of laurinol polyoxyethylene ether, 2-4 parts of sodium polyacrylate, 2-3 parts of asbestos wool, 1-2 parts of barium sulfate, 1-2 parts of nanometer aluminum oxide and 80-100 parts of water. The ceramic product crack adhesive is moderate in adhesion property, clear and transparent, moreover is excellent in high temperature resistance, weather resistance and wearing resistance and safe and non-toxic; no harmful substances can be released, so that the use security can be improved; and ceramic product cracks can be effectively bonded, a bonded ceramic product is smooth in hand feeling, cracks can be vanished, and original attractiveness of appearance can be recovered.

Description

Technical field: [0001] The invention relates to the technical field of ceramic manufacturing, in particular to a crack adhesive for ceramic products. Background technique: [0002] Ceramic products have the disadvantage of being brittle and fragile, so cracks often appear during use. Cracks directly affect the normal use of ceramic products, especially ceramic products that hold liquids. It would be a pity to throw away ceramic products with cracks directly. If glue is used for bonding, although the cracks can barely be repaired, there will be a smell of glue after hot water or heating, and harmful substances may be generated, which will affect the safety of use. Invention content: [0003] The technical problem to be solved by the present invention is to provide a crack adhesive for ceramic products that is safe, environmentally friendly, high temperature resistant and has good adhesion. [0004] Technical problem to be solved by the present invention adopts following...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J105/00C09J101/28C09J191/06C09J109/00C09J167/08C09J11/04C09J11/06C09J11/08
CPCC09J105/00C08K2201/011C08K2201/014C08L2201/08C09J11/04C09J11/06C09J11/08C09J101/284
Inventor 许纯荣
Owner ANHUI QINGHUAFANG FINE BONE PORCELAIN