A kind of thermochromatic intelligent film and preparation method thereof

A smart film and thermochromic technology, applied in the field of thermochromic smart film and its preparation, to achieve good weather resistance

Active Publication Date: 2018-12-07
GUANGZHOU INST OF ENERGY CONVERSION - CHINESE ACAD OF SCI
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In short, the reflective layer provided by the present invention can solve or improve the time efficiency problem of radiative heating annealing of the vanadium oxide film layer, and the setting of the composite barrier layer can realize that the thermochromic smart film containing the vanadium oxide film layer can withstand relatively high pressure in vacuum and atmospheric environments. After a long time annealing treatment, the vanadium oxide film layer will not be oxidized or reduced to deteriorate, and a thermochromic smart film product with better weather resistance can be obtained

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of thermochromatic intelligent film and preparation method thereof
  • A kind of thermochromatic intelligent film and preparation method thereof
  • A kind of thermochromatic intelligent film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The preparation method of thermochromatic intelligent film, the step comprises:

[0034] a. providing a substrate 1;

[0035] b. Depositing a first dielectric layer 2, an infrared reflection layer 4, a vanadium oxide film layer 7, a first barrier layer 8, a second barrier layer 9 and a second dielectric layer 10 on the substrate 1 by vacuum magnetron sputtering, Wherein the first barrier layer 8 and the second barrier layer 9 are sputtered with different targets, the first barrier layer 8 is a metal oxide, nitride or oxynitride, and the second barrier layer 9 is a metal film;

[0036] c. Anneal the coated glass.

[0037] In the preparation method of the thermochromic intelligent film layer described in the present invention, the annealing treatment can adopt any one of infrared radiation lamp annealing, flash lamp annealing, laser annealing and tempering annealing. In the present invention, the annealing treatment is preferably carried out by means of infrared radiati...

Embodiment 1

[0039] figure 1 It is the cross-sectional view of the thermochromic smart film of specific embodiment 1, and the thermochromic smart film comprises a substrate 1 (including transparent glass or colored glass with a thickness of 1 to 10 mm, preferably with a thickness of 4 mm to 6 mm) and the substrate is followed by a first medium Layer 2 (in contact with the glass substrate), infrared reflection layer 4, vanadium oxide film layer 7, first barrier layer 8 (close to the vanadium oxide film layer 7), second barrier layer 9 (connected to the first barrier layer 8) And the second dielectric layer 10 (located on the second barrier layer 9, which is also the topmost layer of the composite film layer). The non-limiting material film layers 1 to 10 as shown in the figure form a thermochromic smart film film layer with adjustable heat gain as the ambient temperature changes. This film layer can be deposited on plastic substrates, glass substrates, and metal substrates. , ceramic subst...

Embodiment 2

[0050] figure 2 It is the cross-sectional view of the thermochromic smart film of specific embodiment 2, the thermochromic smart film comprises a substrate 1 (including transparent glass or colored glass with a thickness of 1 to 10 mm, preferably with a thickness of 4 mm to 6 mm) and the substrate is followed by a first medium Layer 2 (in contact with glass substrate), infrared reflection layer 4, first barrier layer 6, vanadium oxide film layer 7, first barrier layer 8 (close to vanadium oxide film layer 7), second barrier layer 9 (with first The barrier layer 8 is connected) and the second dielectric layer 10 (located on the second barrier layer 9, which is also the topmost layer of the composite film layer). The non-limiting material film layers 1-10 as shown in the figure form a thermochromic intelligent film film layer with adjustable heat gain as the ambient temperature changes, and this film layer can be deposited on plastic substrates, glass substrates, and metal subs...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a thermochromic intelligent film and a preparation method therefor. The thermochromic intelligent film consists of a substrate and a complex film layer, wherein the complex film layer comprises a thermochromic functional layer with ambient temperature adjusted heat, a film layer with an infrared reflection function is arranged at the lower part of the thermochromic functional layer and can be used for increasing the efficiency of annealing, a barrier layer which is used for preventing the thermochromic functional layer from oxidation or reduction metamorphism in a heat-treatment annealing and crystallizing modification process is arranged on the thermochromic functional layer, and a dielectric film layer is arranged on the barrier layer and is used for adjusting the appearance color and other protective actions of the complex film layer. The thermochromic intelligent film has the characteristics that the arrangement of the infrared reflection layer is beneficial to the increase of annealing efficiency, the arrangement of the barrier layer is beneficial to the improvement of crystallization quality of the thermochromic functional layer, and meanwhile, the heating annealing treatment on the complex film layer in an atmospheric environment and a vacuum environment can be achieved. According to the thermochromic intelligent film disclosed by the invention, after related film layers are subjected to vacuum plating, the crystallizing modification of the film can be carried out by adopting infrared vacuum-atmosphere environment, infrared atmospheric environment or tempering furnace heat treatment.

Description

Technical field: [0001] The invention relates to a thermochromic smart film and a preparation method thereof, in particular to the problem of promoting high-efficiency heating crystallization modification in the heat treatment process of the smart film and preventing the annealing crystallization oxidation or reduction deterioration of the thermochromic functional layer. Background technique: [0002] For the mass production of thermochromic smart films, there are two traditional preparation process routes, namely chemical spraying thermal decomposition and sputtering coating. The thermal decomposition of chemical spraying has certain limitations due to the control of its appearance color, film thickness, etc., and its industrial production is seldom used. Compared with chemical spray thermal decomposition, sputtering coating has more advantages, such as easy control of film composition, easy control of film thickness and good repeatability. Since the formation of the therm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/36
Inventor 徐刚詹勇军史继富肖秀娣
Owner GUANGZHOU INST OF ENERGY CONVERSION - CHINESE ACAD OF SCI