Method for preparing block graphene aerogel

A technology of graphene airgel and graphene dispersion liquid, which is applied in the field of graphene airgel preparation, can solve the problems of increasing the production cost of graphene airgel, harsh process conditions, complex preparation process, etc., and achieve improved mechanical strength and compression properties, high mechanical strength, and simple steps

Active Publication Date: 2016-08-03
SOUTHEAST UNIV
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The additives or crosslinking agents used in these published patents are relatively expensive, and the preparation process is more complicated than pure graphene aerogels and even requires harsh process conditions, which undoubtedly increases the production cost of graphene aerogels. limit its application in many fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing block graphene aerogel
  • Method for preparing block graphene aerogel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Take 0.3g of the prepared graphite oxide and add it to a beaker containing 100ml of distilled water, take it out after ultrasonication for 1.5h, cool to room temperature, and obtain a graphene oxide dispersion, add propylene oxide PO60mL at one time, and control its pH with NaOH solution after stirring The value is in the range of 2.0-6.8, then put the graphene oxide dispersion liquid with propylene oxide into the reaction kettle, put it into the oven for reaction, first set the temperature to 60°C, and after 30 minutes of reaction, raise the temperature to 80°C ℃, after reacting for 1 hour, raise the temperature to 250℃ and react for 60 hours to obtain a wet gel, and freeze-dry the wet gel at -50℃ for 9 hours to obtain a product with high mechanical strength, good elasticity and a density as low as 0.19g / cm 3 ultralight graphene airgel.

Embodiment 2

[0024] Take 0.5g of the prepared graphite oxide into a beaker containing 100ml of distilled water, take it out after ultrasonication for 1.5h, cool to room temperature, and obtain a graphene oxide dispersion, add 10ml of propylene oxide PO at one time, and control its pH with NaOH solution after stirring The value is in the range of 2.0-6.8, then put the graphene oxide dispersion liquid with propylene oxide into the reaction kettle, put it into the oven for reaction, first set the temperature to 60°C, and after 30 minutes of reaction, raise the temperature to 80°C °C, after reacting for 1 h, the temperature was raised to 250 °C for 6.5 h to obtain a wet gel, and the wet gel was freeze-dried at -50 °C for 9 h to obtain a graphene airgel.

Embodiment 3

[0026] Take 0.5g of the prepared graphite oxide into a beaker containing 100ml of distilled water, take it out after ultrasonication for 1.5h, cool to room temperature, and obtain a graphene oxide dispersion, add 100ml of propylene oxide PO at one time, and control its pH with NaOH solution after stirring The value is in the range of 2.0-6.8, then put the graphene oxide dispersion liquid with propylene oxide into the reaction kettle, put it into the oven for reaction, first set the temperature to 60°C, and after 30 minutes of reaction, raise the temperature to 80°C °C, after reacting for 1 hour, the temperature was increased to 120 °C for 18 hours to obtain a wet gel, and the wet gel was dried under normal pressure for 10 hours to obtain a graphene airgel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing block graphene aerogel. The method includes the specific steps that cheap small molecule epoxy propane serves as a cross-linking agent and is mixed with oxidized graphene or graphene dispersion liquid, a hydrothermal method is utilized to obtain graphene wet gel, drying is further conducted, and the graphene aerogel is obtained. The method is simple in operation step, good in repeatability, mild in reaction condition and suitable for industrialized production, the price of the cross-linking agent is low, and the finally obtained graphene aerogel is complete in block degree, low in density, good in elasticity and high in mechanical strength.

Description

technical field [0001] The invention relates to the field of graphene airgel preparation, in particular to a simple and fast method for preparing graphene airgel with large block size, high strength and good compressibility. Background technique [0002] Because aerogels have many unique advantages such as low density, small thermal conductivity, and well-developed pores, they are used in heat-insulating refractory materials, sound-absorbing and shock-absorbing materials, catalysts, dust traps, and purifiers for gas and water. Broad application prospects. Graphene aerogels (Graphene aerogels) not only have a series of characteristics of traditional aerogels, but also endow aerogels with unique three-dimensional structure due to their excellent physical and chemical properties, such as super adsorption. At the same time, based on its The unique monolithic structure, high specific surface area, and excellent electrical conductivity endow it with broad application prospects in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/04
CPCC01P2006/10
Inventor 任丽丽高丙莹贺赫卢绍祥
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com