High-hardness two-component waterborne polyurethane floor paint and preparing method thereof

A water-based polyurethane and floor coating technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve problems such as short service life, insufficient hardness, wear resistance, low temperature resistance, and poor surface scratch resistance

Active Publication Date: 2016-08-03
厦门富思特新材料科技有限公司
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its disadvantages are: because epoxy resin is a rigid material, its wear resistance, low temperature resistance, and surface scratch resistance are poor; its weather resistance is poor, it is easy to age, and its service life is short
Compared with epoxy floor coatings, polyurethane floor coatings have better wear resistance and weather resistance, but the hardness is not enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-hardness two-component waterborne polyurethane floor paint and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A high-hardness two-component water-based polyurethane floor coating, consisting of two components, A and B, wherein, component A is a water-based aliphatic isocyanate with a solid content of 100%; component B is composed of the following components, and the mass of each component The parts are: deionized water 11.1%; modified polymer dispersant 1%, which is a product produced by Kyoeisha Chemical Co., Ltd., and its brand name is FLOWLENG-700AMP, which is a 2- Amino-2-methyl-1-propanol salt, its solid content is 40-50% by mass; multifunctional amine additives 0.5%, is a product produced by Dow Company in the United States, and its brand is AMP-95; nonionic Type wetting agent 0.3%, is a product produced by Clariant, its brand name is LCN070, it is a kind of alkyl polyoxyethylene ether, its effective substance content is 100%, HLB value is 13; titanium dioxide 10%, is The product produced by DuPont Company of the United States, its brand name is R902, it is a kind of ruti...

Embodiment 2

[0034]A high-hardness two-component water-based polyurethane floor coating, consisting of two components, A and B, wherein, component A is a water-based aliphatic isocyanate with a solid content of 100%; component B is composed of the following components, and the mass of each component The parts are: deionized water 11.1%; modified polymer dispersant 1%, which is a product produced by Kyoeisha Chemical Co., Ltd., and its brand name is FLOWLENG-700AMP, which is a 2- Amino-2-methyl-1-propanol salt, its solid content is 40-50% by mass; multifunctional amine additives 0.5%, is a product produced by Dow Company in the United States, and its brand is AMP-95; nonionic Type wetting agent 0.3%, is a product produced by Clariant, its brand name is LCN070, it is a kind of alkyl polyoxyethylene ether, its effective substance content is 100%, HLB value is 13; titanium dioxide 10%, is The product produced by DuPont Company of the United States, its brand name is R902, it is a kind of rutil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-hardness two-component waterborne polyurethane floor paint and a preparing method thereof. The floor paint is formed by evenly mixing a first component and a second component by the mass ratio of 10:1. The second component is prepared from, by mass, 7%-15% of deionized water, 0.5%-1.5% of modified polymer dispersant, 0.4%-0.9% of multifunctional auxiliary, 0.1%-0.3% of non-ionic wetting agent, 1%-25% of pigment, 5%-30% of filler, 40%-55% of hydroxyl acrylic dispersion, 3%-7% of inorganic additive, 2%-8% of high-strength ceramic microspheres, 0.3%-0.5% of polyether defoaming agent, 0.2%-0.3% of BIT preservative and 0.5%-2.5% of polyurethane thickening agent. The high-hardness two-component waterborne polyurethane floor paint prepared through the method is high in paint film hardness and excellent in abrasion resistance and other physical and chemical properties.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a high-hardness two-component waterborne polyurethane floor coating and a preparation method thereof. Background technique [0002] With the rapid development of the economy and the construction industry, floor coatings have entered a period of prosperity and development. At the same time, people's requirements for floor coatings are getting higher and higher. In the prior art, epoxy resin, as the earliest resin material used in floors, is the most mature technology and the largest proportion. [0003] The main advantages of resin floor coatings are high hardness and good acid and alkali resistance. However, its disadvantages are: because epoxy resin is a rigid material, its wear resistance, low temperature resistance, and surface scratch resistance are poor; its weather resistance is poor, it is easy to age, and its service life is short. Compared with epoxy floor c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/12
CPCC08K3/22C08K3/30C08K3/34C08K13/02C08K2003/2241C08K2003/3045C09D7/61C09D7/65C09D7/70C09D175/04
Inventor 姜年超武文斌姜向阳
Owner 厦门富思特新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com