A kind of method for preparing graphene-reinforced copper-based composite material

A copper-based composite material and graphene technology, which is applied in the field of preparing graphene-reinforced copper-based composite materials, can solve the problems of complex process, poor graphene dispersion and high cost, achieve uniform dispersion, control the time of ball milling, and tensile strength. improved effect

Inactive Publication Date: 2018-01-26
HARBIN UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the technical problems of poor graphene dispersion, high cost and complicated process in the existing preparation of graphene-reinforced copper-based composite materials, and provide a preparation method of graphene-reinforced copper-based composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing graphene-reinforced copper-based composite material
  • A kind of method for preparing graphene-reinforced copper-based composite material
  • A kind of method for preparing graphene-reinforced copper-based composite material

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0016] Specific embodiment one: this embodiment is a kind of method for preparing graphene-reinforced copper-based composite material, specifically carries out according to the following steps:

[0017] 1. Preparation of graphene oxide: add 1g of graphite powder and 1g of sodium nitrate to the Erlenmeyer flask containing 46mL of concentrated sulfuric acid under the condition of ice-water bath, mix and stir for 20min under the condition of ice-water bath; Add 6g of potassium permanganate and stir for 40 minutes to obtain a green-purple mixed solution. Keep the green-purple mixed solution at a temperature of 30°C to 40°C for 1 hour, and then add it at a temperature of 30°C to 40°C. Incubate 40mL of distilled water at a temperature of 85°C to 95°C for 30 minutes to obtain a brown mixed solution. Add 100mL of distilled water and 6mL of hydrogen peroxide to the brown mixed solution at room temperature to obtain a bright yellow mixed solution. Then repeatedly wash the bright yellow ...

specific Embodiment approach 2

[0020] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is: the graphene oxide obtained in step 1 is weighed in step 2 to be 0.5 g. Others are the same as the first embodiment.

specific Embodiment approach 3

[0021] Embodiment 3: The difference between this embodiment and Embodiments 1 to 2 is that in step 2, the ultrasonic frequency is 10 kHz and lasts for 1 hour. Others are the same as the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing a graphene-reinforced copper-based composite material. The purpose of the present invention is to solve the problems of poor dispersion of graphene, high cost and complicated process existing in the existing method for preparing graphene-reinforced copper-based composite materials. The invention uses graphene oxide as a reinforcing body precursor, ultrasonically mixes prepared graphene oxide and copper powder in an ethanol solution, and uses low-cost ball milling technology to uniformly disperse graphene oxide and copper powder. Finally, graphene-reinforced copper matrix composites were prepared by vacuum hot-pressing sintering. The composite material prepared by the invention has the advantages of good graphene dispersion, simple and efficient preparation method and easy realization of large-scale production.

Description

technical field [0001] The invention relates to a method for preparing a graphene-reinforced copper-based composite material. Background technique [0002] Copper and its alloy materials have the advantages of good electrical and thermal conductivity and easy forming, and have been widely used in aerospace, transportation, machinery industry, energy, chemical industry, power electronics and other fields. With the development of modern science and technology, traditional copper and copper alloys have low strength and poor high-temperature performance and can no longer meet the performance requirements of practical applications. By adding high-strength second-phase particles to the copper matrix, it has more excellent properties. The comprehensive properties can effectively expand the application fields of copper and copper alloys. The added second phase mainly includes oxides, nitrides and new carbon materials. [0003] Graphene is a carbon atom with sp 2 The hexagonal hon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/05C22C9/00B22F3/14B22F9/04
CPCB22F3/14B22F9/04B22F2009/043B22F2998/10C22C1/05C22C9/00
Inventor 岳红彦姚龙辉高鑫林轩宇王宝郭二军
Owner HARBIN UNIV OF SCI & TECH