A kind of floor heating pipe repairing agent and preparation method thereof

A repairing agent and heating pipe technology, applied in the directions of adhesives, adhesive types, adhesive additives, etc., can solve problems such as troublesome handling, and achieve the effects of reducing repairing costs, increasing mechanical properties, and excellent compressive capacity.

Inactive Publication Date: 2017-06-06
唐兴彦
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But no matter what kind of floor heating pipe, it is more troublesome to deal with when it leaks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of floor heating pipe repairing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A repairing agent for floor heating pipes, comprising A component and B component, A component comprising the following components in parts by mass:

[0040] 90 parts of epoxy resin,

[0041] 15 parts of unsaturated polyester resin,

[0042] 2 parts cellulose ether,

[0043] 0.8 parts of polyvinyl alcohol,

[0044] Attapulgite 1.5 parts,

[0045] 0.6 part of alkylphenol polyoxyethylene ether,

[0046] 12 parts of stuffing;

[0047] B component is curing agent;

[0048] The mass mixing ratio of A component and B component is 100:4.

[0049] Wherein, the epoxy resin is bisphenol A type epoxy resin, and its epoxy value is 0.42-0.45mol / 100g.

[0050] The filler is white carbon black and aluminum powder, the mass ratio of the two is 1:1.

[0051] The curing agent is a mixture of low-molecular polyamide curing agent and polyetheramine curing agent, and the mass ratio of the two is 2:1.

[0052] The preparation method of described floor heating pipe restoration agent,...

Embodiment 2

[0059] A repairing agent for floor heating pipes, comprising A component and B component, A component comprising the following components in parts by mass:

[0060] 80 parts of epoxy resin,

[0061] 10 parts of unsaturated polyester resin,

[0062] 1 part cellulose ether,

[0063] 1 part polyvinyl alcohol,

[0064] Attapulgite 1 part,

[0065] 0.5 part of alkylphenol polyoxyethylene ether,

[0066] 10 parts of stuffing;

[0067] B component is curing agent;

[0068] The mass mixing ratio of A component and B component is 100:3.

[0069] Wherein, the epoxy resin is bisphenol A type epoxy resin, and its epoxy value is 0.42-0.45mol / 100g.

[0070] The filler is preferably white carbon black and aluminum powder, and the mass ratio of the two is 1:2.

[0071] The curing agent is a mixture of low-molecular polyamide curing agent and polyetheramine curing agent, and the mass ratio of the two is 3:1.

[0072] The preparation method of described floor heating pipe restoration a...

Embodiment 3

[0079] A repairing agent for floor heating pipes, comprising A component and B component, A component comprising the following components in parts by mass:

[0080] 100 parts of epoxy resin,

[0081] 20 parts of unsaturated polyester resin,

[0082] 3 parts cellulose ether,

[0083] 0.5 parts of polyvinyl alcohol,

[0084] Attapulgite 2 parts,

[0085] 1 part of alkylphenol polyoxyethylene ether,

[0086] 18 parts of stuffing;

[0087] B component is curing agent;

[0088] The mass mixing ratio of A component and B component is 100:5.

[0089] Wherein, the epoxy resin is bisphenol A type epoxy resin, and its epoxy value is 0.42-0.45mol / 100g.

[0090] The filler is preferably white carbon black and aluminum powder, and the mass ratio of the two is 3:2.

[0091] The curing agent is a mixture of low-molecular polyamide curing agent and polyetheramine curing agent, and the mass ratio of the two is 2:1.

[0092] The preparation method of described floor heating pipe restorat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy valueaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of pipe repair, and particularly discloses geothermal pipe repairing agent and a preparation method thereof. The repairing agent is prepared from a component A and a component B, wherein the component A is prepared from the following components in parts by weight: 80-100 parts of epoxy resin, 10-20 parts of unsaturated polyester resin, 1-3 parts of cellulose ether, 0.5-1 part of polyving akohol, 1-2 parts of attapulgite, 0.5-1 part of alkylphenol polyoxyethylene and 10-18 parts of filler, and the component B is curing agent. The invention also discloses a preparation method of the geothermal pipe repairing agent. The geothermal pipe repairing agent has excellent construction performance, and a repairing layer has good anti-pressure ability, bonding strength and corrosion resistance. The geothermal pipe repairing agent can be used for repairing the geothermal pipe, can carry out on-line repair, is convenient and quick, and does not affect the normal life of users, and meanwhile, the repair cost can be greatly lowered.

Description

technical field [0001] The invention belongs to the technical field of pipeline repair, and in particular relates to a floor heating pipe repair agent and a preparation method thereof. Background technique [0002] With the development of society and the continuous improvement of people's living standards, traditional heating equipment has been difficult to meet people's needs. Floor heating design has gradually become the trend of people's needs. It is a heating method that bury the floor heating pipes under the floor, add heat-conducting liquid to the floor heating pipes, use hot water or heating cables, and radiate heat evenly to the room through the ground. Compared with traditional heating methods, geothermal radiant heating has the advantages of comfort, energy saving and environmental protection. [0003] At present, the heat transfer liquid used in the floor heating pipe is flowing, that is, it enters from the entrance of the floor heating pipe and then flows out f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J163/00C09J167/06C09J11/08C09J11/04
CPCC08K2201/011C08L2203/18C08L2205/035C09J11/04C09J11/08C09J163/00C08L67/06C08L1/26C08L29/04C08L71/00C08K3/346C08K3/36C08K2003/0812