TiCrN/MoS2 multi-element anti-wear lubricating coating tool and preparation process thereof

A technology of lubricating coating and preparation process, which is applied in the field of TiCrN/MoS2 multi-element anti-friction lubricating coating tool and its preparation process, can solve the problem that the service life of the tool cannot meet the needs of actual use, and the service life of the tool coating flank coating Not long, the service life of the tool needs to be further improved, etc., to achieve the effect of increasing the use range, high hardness, and reducing the friction coefficient

Active Publication Date: 2016-08-17
安徽锦鹏纺织有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the cutting process without cutting fluid cooling and lubrication, the tool can form a lubricating lubricating film on the surface of the tool, thereby realizing the lubricating function of the tool itself, but the hardness of this lubricating coating is low, which leads to the tool coating especially Is the service life of the flank coating is not long
Literature (Acta Materials.2011,59(1):68-74) reported the action mechanism and performance of TiN hard coating tools during cutting, but this hard coating has limited its performance due to its relatively high coefficient of friction. widely used
Chinese Patent TiN+MoS 2 /Zr combined coating tool (Pa

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TiCrN/MoS2 multi-element anti-wear lubricating coating tool and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example one

[0021] A TiCrN / MoS 2 Multi-element anti-friction lubricating coating tool, the tool is an ordinary milling insert, and its matrix material is: hard alloy YT15. The deposition method is a composite coating prepared by a composite coating method of arc plating and intermediate frequency magnetron sputtering, including 1 Ti target arc target, 1 Cr target arc target, and 2 MoS 2 Magnetron sputtering target: Ti transition layer, Ti / Cr transition layer, TiCrN (arc ion plating) and MoS deposited by arc ion plating 2 Composite coating (magnetron sputtering), the preparation process is:

[0022] (1) Pre-treatment: Polish the surface of the tool base to remove impurities such as surface oil and rust, then put it in alcohol and acetone, ultrasonically clean each for 30 minutes, remove the oil and other attachments on the surface of the tool, and quickly dry after it is fully dried Put it into the coating machine and vacuum to 7.0~8.0×10 -3 Pa, heat to 300℃, keep for 30~35...

Example Embodiment

[0028] Example two

[0029] A TiCrN / MoS 2 Multi-element anti-friction lubricating coating tool. The tool is an ordinary twist drill. The tool base material is high-speed steel W18Cr4V. The deposition method is a composite coating prepared by a composite coating method of arc plating and intermediate frequency magnetron sputtering, including 1 Ti target arc target, 1 Cr target arc target, and 2 MoS 2 Magnetron sputtering target: Ti transition layer, Ti / Cr transition layer, TiCrN (arc ion plating) and MoS deposited by arc ion plating 2 Composite coating (magnetron sputtering), the preparation process is:

[0030] (1) Pre-treatment: Polish the surface of the tool base to remove impurities such as surface oil and rust, then put it in alcohol and acetone, ultrasonically clean each for 30 minutes, remove the oil and other attachments on the surface of the tool, and quickly dry after it is fully dried Put it into the coating machine and vacuum to 7.0~8.0×10 -3 Pa, heat to 300℃, keep for 3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of mechanically manufactured metal cutting tools, and particularly relates to a TiCrN/MoS2 multi-element anti-wear lubricating coating tool and a preparation process thereof. A tool base body comprises high-speed steel, hard alloy, ceramics, diamond or cubic boron nitride, a coating is of a multi-layer structure, and a Ti transition layer, a Ti/Cr transition layer and a TiCrN and MoS2 compounded coating are sequentially arranged between the base body and the surface of the coating. According to the coating tool, the advantages of a TiCrN multi-element hard coating and a MoS2 lubricating coating are synthesized, high hardness is achieved, a lubricating function is achieved, the good lubricating performance of the coating can be kept in the whole life period, and the cutting performance of the coating tool can be remarkably improved.

Description

technical field [0001] The invention belongs to the field of mechanical manufacturing metal cutting tools, in particular to a TiCrN / MoS 2 Multi-element anti-friction lubricating coating tool and its preparation process. Background technique [0002] According to the nature of the coating material, coated tools can be divided into two categories, namely: "hard" coated tools and "lubricated" coated tools. The main advantages of "high hardness" coating tools are high hardness and good wear resistance. Typical "high hardness" coating materials include TiN, TiCN, TiAlN and diamond-like carbon. The goal pursued by "lubricating" coating tools is low friction coefficient. Typical "lubricating" coating materials are solid lubricating materials with low friction coefficients (such as: MoS 2 、WS 2 、TaS 2 and other sulfides). The current development trend of tool coatings is: coating components tend to be diversified and compounded. Composite coatings can combine the advantages of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C14/32C23C14/16C23C14/18C23C14/35C23C14/06C23C14/02
CPCC23C14/021C23C14/022C23C14/0623C23C14/0641C23C14/16C23C14/18C23C14/325C23C14/35
Inventor 宋文龙邓建新郭宗新王首军
Owner 安徽锦鹏纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap