Preparation method of water-borne inorganic paint and method for preparation of inorganic coating from water-borne inorganic paint

A water-based inorganic coating and silicone technology, which is applied in the direction of antifouling/underwater coatings, coatings, paints containing biocide, etc., to achieve the effect of improving strength and toughness, and good hydrophobicity

Active Publication Date: 2016-08-31
福建釉时代环保涂料有限公司
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Relatively speaking, there is no such transparent inorganic coating in the market, because compared with transparent organic coatings, transparent inorganic coatings have significantly improved durability, weather resistance, water resistance and other properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] It is a kind of preparation method of water-based inorganic coating, and preparation step is as follows:

[0025] In the first step, the metal silicate is dispersed in the silica sol to obtain a silicate silica sol solution, wherein the mass ratio between the metal silicate and the silica sol is 1:0.1;

[0026] In the second step, add the trimethoxysilane mixture into the water, stir evenly, then add the inorganic acidic catalyst, continue to stir evenly to obtain the organosilicon prepolymer solution, wherein the mixture between the trimethylsilane mixture and water, and the inorganic acid The mass ratio is: 1:0.002:0.001;

[0027] The third step is to mix the silicate silica sol solution in the first step with the silicone prepolymer solution in the second step, then add film-forming aids, leveling agents and defoamers, and use sand milling Stir evenly with a machine to prepare the required water-based inorganic coating, wherein the mass ratio between the silicate si...

Embodiment 2

[0031] It is a kind of preparation method of water-based inorganic coating, and preparation step is as follows:

[0032] The first step is to disperse the metal silicate in the silica sol to obtain a silicate silica sol solution, wherein the mass ratio between the metal silicate and the silica sol is 1: 0.5;

[0033] In the second step, add the trimethoxysilane mixture into the water, stir evenly, then add the inorganic acidic catalyst, continue to stir evenly to obtain the organosilicon prepolymer solution, wherein the mixture between the trimethylsilane mixture and water, and the inorganic acid The mass ratio is: 1:0.4:0.2;

[0034] The third step is to mix the silicate silica sol solution in the first step above with the silicone prepolymer solution in the second step, and then add film-forming aids, leveling agents and defoamers. The mill is stirred evenly to prepare the required water-based inorganic coating, wherein the mass ratio between the silicate silica sol solutio...

Embodiment 3

[0038] It is a preparation method of water-based inorganic paint, and the preparation steps are as follows:

[0039] The first step is to disperse the metal silicate in the silica sol to obtain a silicate silica sol solution, wherein the mass ratio between the metal silicate and the silica sol is 1:0.15;

[0040] In the second step, add the trimethoxysilane mixture into the water, stir evenly, then add the inorganic acidic catalyst, continue to stir evenly to obtain the organosilicon prepolymer solution, wherein the mixture between the trimethylsilane mixture and water, and the inorganic acid The mass ratio is: 1:0.2:0.005;

[0041] The third step is to mix the silicate silica sol solution in the first step with the silicone prepolymer solution in the second step, then add film-forming aids, leveling agents and defoamers, and use sand milling Stir evenly with a machine to prepare a water-based inorganic coating, wherein the mass ratio between the silicate silica sol solution,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a water-borne inorganic paint and a method for preparation of an inorganic coating from the water-borne inorganic paint. The method is characterized by including the preparation steps of: firstly dispersing metal silicate in silica sol to obtain a silicate silica sol solution; then adding a trimethoxy silane mixture into water, stirring the substances evenly, then adding an inorganic acidic catalyst, further stirring the substances evenly to obtain an organosilicon prepolymer solution; finally mixing the silicate silica sol solution with the organosilicon prepolymer solution, then adding a film-forming assistant, a leveling agent and a defoaming agent, and stirring the substances evenly to obtain the water-borne inorganic paint; and adding a proper amount of water into the inorganic paint to obtain an inorganic paint's diluent solution with a solid content of 10%-30%, brushing or spraying the diluent solution to a matrix surface, and performing natural drying, thus obtaining an inorganic transparent coating. The strength and toughness of the coating are improved, and the water-borne inorganic paint has the advantages of good hydrophobic, waterproof and anti-mildew effects, etc.

Description

technical field [0001] The present invention relates to a kind of preparation method of water-based inorganic paint and preparation method of water-based inorganic paint [0002] Coating method. Background technique [0003] Compared with the currently widely used organic-based architectural coatings (emulsion paint, etc.), it has the following advantages: 1. Petrification: Inorganic coatings can react with mineral substrates to form a waterproof and acid-resistant silicon 2. Non-combustibility: Inorganic coatings have the characteristics of inorganic substances, and their temperature resistance is particularly good. Not only will they not burn at a high temperature of 1200 ° C, but they are also flame-retardant; 3. Breathability : Inorganic coatings are waterproof and highly breathable, so that the water inside the stone building can evaporate freely; at the same time, it has the filtering effect of alkali substances, which can prevent the coating from bubbles, thermal bur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D5/14C09D7/12C09J183/04C09J11/04
CPCC08K3/34C08K3/36C08K2201/011C09D5/14C09D7/61C09D7/67C09D183/04C09J11/04C09J183/04
Inventor 刘锋邹海良
Owner 福建釉时代环保涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap