A kind of low compression bit thickness low alloy steel plate and its manufacturing method

A shrinkage and low-alloy technology, which is applied in the field of ultra-thick low-alloy steel plate and its low compression ratio controlled rolling, can solve the problems of high production cost, poor practicability, low compression ratio, etc., and achieve the reduction of production cost , Excellent overall performance, and the effect of improving weldability

Active Publication Date: 2017-09-29
JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The patent (CN 102009332A) discloses a method for producing extra-thick plates with a stacked rolling welding process, which has a high compression ratio and good internal quality, but it needs to be welded by two or more continuous casting blanks, which is complicated in process, high in cost, and practical Not strong, low yield
[0007] To sum up, when the existing ultra-thick low-alloy steel plates with a thickness of 150-180 mm are produced by die casting, electroslag remelting, and composite slabs, there are problems such as high production costs, long cycle times, and poor practicability; the use of continuous casting slabs During production, there are problems such as low compression ratio and insufficient strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low compression bit thickness low alloy steel plate and its manufacturing method
  • A kind of low compression bit thickness low alloy steel plate and its manufacturing method
  • A kind of low compression bit thickness low alloy steel plate and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] Below in conjunction with embodiment the present invention is described in further detail.

[0035] Embodiments 1-3 are low-pressure, bit-thick, low-alloy steel plates, respectively, and the main production process is smelting in a 150-ton oxygen converter→refining in a ladle furnace→vacuum degassing treatment→continuous casting of 370mm thick slab→cooling the slab→heating the slab →Controlled rolling→Controlled cooling→Stacking slow cooling→Flaw detection→Performance inspection.

[0036] The smelting chemical composition of embodiment 1-3 and comparative example is shown in Table 1:

[0037] Table 1 Melting chemical composition (wt%)

[0038]

[0039] Table 1. Examples 1-3 all meet the chemical composition requirements of the present invention. Slabs with a thickness of 370mm are produced in strict accordance with the process of the present invention. The steel ingots with a large head diameter of 850mm are produced in comparative examples according to the electric...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an extremely-thick low-alloy steel plate with a low compression ratio. The steel plate is 150-180 mm thick, and consists of the following components in percentage by mass: 0.10-0.17% of C, 0.15-0.45% of Si, 1.18-1.40% of Mn, less than or equal to 0.010% of P, less than or equal to 0.003% of S, 0.10-0.20% of Ni, 0.010-0.040% of Nb and the balance Fe and inevitable impurities; and meanwhile, the content of the corresponding elements meets the following relation: Ceq less than or equal to 0.39%, [C]+[Mn] greater than or equal to 1.35% but less than or equal to 1.50%. A melting process comprises the following steps: oxygen converter smelting, ladle furnace refining, vacuum degassing treatment, continuous casting for slab with thickness being 370 mm or greater, casting blank cover-cooling, casting blank heating, rolling control, cooling control, stacking and slow-cooling, flaw detection and performance examination. The steel plate has the characteristics of being high in strength, excellent in low-temperature toughness, excellent in weldability and the like, and is wider in scope of application.

Description

technical field [0001] The invention belongs to the technical field of low-alloy steel plate smelting, and in particular relates to an extra-thick low-alloy steel plate and its manufacturing method by adopting low compression ratio controlled rolling. Background technique [0002] Extra-thick plates generally refer to steel plates with a thickness ≥ 60mm. Low-alloy extra-thick steel plates are mainly used for large-scale facilities and components that require high steel performance, such as boilers, offshore platforms, bridges, and high-rise buildings. With the rapid development of my country's energy development and infrastructure construction, more and more markets are in urgent need of extra-thick plates, especially some high-performance extra-thick steel plates with a thickness ≥ 150mm. In order to fully ensure the inherent metallurgical quality and core performance of the steel plate , requires the compression ratio of the billet and the steel plate to be ≥ 3, and domest...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/08C22C38/12C22C33/04C21D8/02
CPCC21D8/0226C21D2211/002C21D2211/005C21D2211/009C22C33/04C22C38/02C22C38/04C22C38/08C22C38/12
Inventor 丁庆丰高助忠胡建国李经涛杨宏伟葛亮李科袁伽利黄军高俊
Owner JIANGYIN XINGCHENG SPECIAL STEEL WORKS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products