Hydrophobic modified expanded perlite thermal insulation board and production method thereof

A technology of expanded perlite and its production method, which is applied in the field of building materials, can solve problems such as application limitations of expanded perlite insulation boards, and achieve the effects of superior fire resistance, reasonable folding ratio, and good thermal insulation performance

Active Publication Date: 2016-09-21
XINYANG CITY OF CRYSTAL ENG MATERIALS CO LTD
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to various reasons, the application of expanded p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophobic modified expanded perlite thermal insulation board and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1

[0038] The hydrophobic modified expanded perlite insulation board of this embodiment includes the following components in parts by weight: 25 parts by weight of cement, 5 parts by fly ash, 5 parts by triethoxysilane, 10 parts by polyacrylate emulsion, and modified 50 parts of sexually expanded perlite, 2 parts of sodium dodecylbenzene sulfonate, 8 parts of additives, 1 part of quicklime, 0.3 parts of PP fiber, 0.5 parts of carbon fiber, 5 parts of diatomaceous earth, 4 parts of sodium silicate and 20 parts of water .

[0039] The additive includes the following components in parts by weight: 30 parts of calcium sulfate, 5 parts of alumina, 3 parts of sodium carboxymethyl cellulose, 10 parts of zinc phosphate and 15 parts of iron oxide.

[0040] The specific preparation method of the modified expanded perlite is as follows: heat the perlite to 1000°C for puffing treatment to expand the volume of the perlite by 7 times to obtain expanded perlite, and then lower the ...

Example Embodiment

[0046] Example 2

[0047] The hydrophobic modified expanded perlite insulation board of this embodiment includes the following components in parts by weight: 40 parts by weight of cement, 8 parts by fly ash, 2 parts by triethoxysilane, 5 parts by polyacrylate emulsion, and modified 60 parts of sexually expanded perlite, 0.7 parts of sodium dodecylbenzene sulfonate, 5 parts of additives, 2 parts of quicklime, 0.1 parts of PP fiber, 2 parts of carbon fiber, 10 parts of diatomaceous earth, 10 parts of sodium silicate and 15 parts of water .

[0048] The additive includes the following components in parts by weight: 25 parts of calcium sulfate, 3 parts of alumina, 0.2 parts of sodium carboxymethyl cellulose, 5 parts of zinc phosphate and 20 parts of iron oxide.

[0049] The specific preparation method of the modified expanded perlite is as follows: heat the perlite to 1300°C for puffing treatment, expand the volume of the perlite by 10 times to obtain expanded perlite, and then lower th...

Example Embodiment

[0055] Example 3

[0056] The hydrophobic modified expanded perlite insulation board of this embodiment includes the following components in parts by weight: 30 parts of cement, 7 parts of fly ash, 3 parts of triethoxysilane, 7 parts of polyacrylate emulsion, modified 70 parts of sexually expanded perlite, 2.9 parts of sodium dodecylbenzene sulfonate, 10 parts of additives, 3 parts of quicklime, 0.5 parts of PP fiber, 1 part of carbon fiber, 7 parts of diatomaceous earth, 8 parts of sodium silicate and 10 parts of water .

[0057] The additive includes the following components in parts by weight: 35 parts of calcium sulfate, 2 parts of alumina, 5 parts of sodium carboxymethyl cellulose, 8 parts of zinc phosphate and 16 parts of iron oxide.

[0058] The specific preparation method of the modified expanded perlite is as follows: heat the perlite to 1200°C for puffing treatment, expand the volume of the perlite by 7 times to obtain expanded perlite, and then lower the temperature. When...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyacrylate enhanced modified expanded perlite thermal insulation board and a production method thereof. The modified expanded perlite thermal insulation board comprises the following components, by weight: 25-40 parts of cement, 5-8 parts of fly ash, 2-5 parts of triethoxysilane, 5-10 parts of polyacrylate emulsion, 50-70 parts of modified expanded perlite, 0.7-2.9 parts of sodium dodecylbenzenesulfonate, 5-10 parts of additives, 1-3 parts of quicklime, 0.1-0.5 parts of PP fiber, 0.5-2 parts of carbon fiber, 5-10 parts of diatomite, 4-10 parts of sodium silicate and 10-20 parts of water. According to the modified expanded perlite thermal insulation board, cement, fly ash, diatomite, PP fiber and other organics and inorganics are adopted as raw materials, such that industrial and mining waste materials are effectively utilized, and no toxic or harmful substance is added. Therefore, the modified expanded perlite thermal insulation board is green and environment-friendly. The modified expanded perlite thermal insulation board has the advantages of wide raw material source and low cost. The production process is simple and is easy to operate. With the thermal insulation board, requirements by different building materials can be satisfied, and good social and economic benefits are provided.

Description

technical field [0001] The invention relates to a hydrophobic modified expanded perlite insulation board and a production method thereof, belonging to the technical field of building materials. Background technique [0002] Building energy conservation is an industry supported by the national industrial policy. At present, building energy-saving materials are mainly divided into inorganic thermal insulation lightweight aggregates and organic thermal insulation lightweight aggregates. However, due to the characteristics of the chemical properties of materials, no matter whether it is an inorganic system or an organic system, it is impossible to meet the requirements of thermal insulation and energy saving performance and fire safety at the same time: from In terms of thermal insulation performance, organic materials are superior to inorganic materials; in terms of fire safety performance, Class A flame-retardant thermal insulation materials are the best choice. In recent yea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B14/18C04B20/06C04B20/10C04B24/42C04B16/06C04B14/38C04B18/08B28B3/00B28B1/50B28B1/52B28B11/24C04B111/28C04B111/40
CPCB28B1/50B28B1/52B28B1/525B28B3/00B28B11/243C04B20/06C04B20/10C04B20/1051C04B28/04C04B2111/28C04B2111/40C04B2201/20C04B2201/32C04B2201/50C04B18/08C04B24/42C04B24/2641C04B14/185C04B24/20C04B22/143C04B14/303C04B24/383C04B22/16C04B14/308C04B22/064C04B16/0633C04B14/386C04B14/08C04B22/08Y02W30/91
Inventor 安武梅春河厉励蔡燚
Owner XINYANG CITY OF CRYSTAL ENG MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap