A technology of ultra-fine fiber and manufacturing method, which is applied in the direction of fiber type, fiber treatment, skin care preparation, etc., and can solve the problems of low strength and rough cloth surface

Active Publication Date: 2018-08-17
NOX BELLCOW COSMETICS CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The cloths for facial masks of skin care products on the market are basically made of one or several short fibers that have been made, which are opened, carded, and netted, and then mechanically, chemically or thermally bonded and reinforced to form short fiber mask cloths. ; The short-fiber facial mask cloth made from this has simple production process, soft hand feeling and water absorption, but low strength and rough cloth surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of manufacture method of microfiber mask cloth, it comprises the following steps:

[0016] (1) Melt the PA-6 polymer slices and PET polymer slices according to the ratio of 50% by weight: 50%, that is, hot air drying, heating, melting, extrusion, and filtration of the obtained melt, and inject it into the orange segment In the spinning hole of the shape, in the air shower state, the original silk of the orange segment shape is obtained;

[0017] (2) Carry out slit airflow drafting and spinning of raw silk, and then vibrate and swing the pierced-shaped fiber group made above to form a continuous fiber web;

[0018] Then, the continuous fiber web is sprayed with a high-pressure water needle with a pressure of 150KG to form a three-dimensional filament microfiber cloth;

[0019] After drying this filament superfine fiber cloth, promptly make 140 grams / square meter of long filament superfine fiber cloth semi-finished product,

[0020] Then fully immerse the semi-fi...

Embodiment 2

[0022] (1) Melt PA-6 polymer slices and PET polymer slices according to the ratio of 50%, pressurize and inject them into the segmented pie-shaped spinning holes, and obtain segmented-orange-shaped raw silk in the air-drenched state,

[0023] (2) Carry out slit airflow drafting and spinning of raw silk, and then vibrate and swing the pierced-shaped fiber group made above to form a continuous fiber web; use a high-pressure water needle with a pressure of 100KG for this continuous fiber web Spray to form a three-dimensional long-filament microfiber cloth with a three-dimensional structure; then dry this long-filament superfine fiber cloth to make 80 grams / square meter of long-filament superfine fiber cloth semi-finished products, and then 80 grams \ Square meters of filament microfiber cloth semi-finished products are fully immersed in a sodium hydroxide solution with a temperature of 95 degrees and a concentration of 15 grams\liter for 50 minutes to partially hydrolyze the PET m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A manufacturing method for an ultrafine fiber mask fabric is characterized by comprising the steps of: (1) obtaining orange slice-type raw silk by slicing a PA6 polymer and a PET polymer; (2) carrying out slit type airflow drafting spinning on the raw silk, and vibrating, swinging and laying on prepared orange slice-type fiber groups to form a continuous fiber net; spraying the continuous fiber net by using a high-pressure water needle, wherein PA-6 and PET combined fiber silk in the orange slice-type fiber groups is split under the action of the high-pressure water needle so that ultrafine continuous independent PA-6 superfine fiber silk and PET ultrafine fiber silk are formed; and when the combined fiber silk is split by the high-pressure water needle, embedding the independent PA-6 ultrafine fiber silk and PET ultrafine fiber silk in a double-layered stereoscopic receiving net curtain in a flushing manner by the high-pressure water needle to form the filament ultrafine fiber fabric with a three-dimensional structure. The ultrafine fiber mask fabric is characterized by being ultra-soft, fine, smooth and well attached to skin.

Description

technical field [0001] The invention relates to the technical field of polymer melt-spinning cloth forming technology and skin care product mask cloth production technology, in particular to a manufacturing method of superfine fiber mask cloth Background technique [0002] Polymer melt spinning fabric technology is a commonly used spinning manufacturing technology, that is, the polymer in the molten state is drawn out of the fiber filaments by using high-pressure airflow, and the polymer can be one or several kinds; after The drawn fiber filaments are mechanically, chemically or thermally bonded and reinforced to form a continuous filament cloth; the continuous filament cloth made from this has high strength and low cost, but the cloth surface is rough, feels stiff, and does not absorb water. [0003] The cloths for facial masks of skin care products on the market are basically made of one or several short fibers that have been made, which are opened, carded, and netted, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/4382D04H1/492D04H1/732A61K8/02A61K8/85A61K8/88A61Q19/00D06M11/38D06M101/32
CPCA61K8/0212A61K8/85A61K8/88A61Q19/00D04H1/4382D04H1/492D04H1/732D06M11/38D06M2101/32
Inventor 郝景标
Owner NOX BELLCOW COSMETICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap